Gamma radiation grafting process for preparing separator membranes for electrochemical cells
Assignee: Rai Research Corp
•
Filing: 1980-08-28
•
Granted: 1982-07-13
•
Expires: 2000-08-28
Abstract
Abstract This invention relates to an irradiation grafting process for preparing separator membranes for use in electrochemical cells, comprising contacting a polymeric base film with an aqueous solution of a hypophilic monomer and a polymerization retardant; and irradiating, said contacted film to form a graft membrane having low electrical resistivity and having monomer molecules uniformly grafted thereon.
Inventors
- 👤 Vincent F. D'Agostino
- 👤 Joseph Y. Lee
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 01:34
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0093; B01D67/00931; C; C08; C08F; C08F255/00; C08F255/02; C08F259/00; C08F259/08; H; H01; H01M; H01M50/00; H01M50/40; H01M50/409; H01M50/411; H01M50/414; H01M50/417; H01M50/426; H01M50/449; H01M50/489; B01D2323/00; B01D2323/38; B01D2323/385; H01M2300/00; H01M2300/0002; H01M2300/0014; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
124 words
A process for the preparation of a separator membrane suitable for use in electrochemical cells comprising the steps of: (a) forming a graft polymerization medium consisting substantially of water, from about 0.5 to about 25 weight percent of one or more ethylenically unsaturated hydrophilic monomers and one or more polymerization retardants selected from the group consisting of water soluble cupric salts, ferrous salts or mixtures thereof, in an amount sufficient to retard the polymerization of said monomers; (b) placing said medium in contact with an inert polymeric base film; and (c) irradiating said film while in contact with said medium with sufficient radiation to graft polymerize said monomers onto said film, wherein all weight percents are based on the total weight of the medium.
Claim 2
Dependent Claim
124 words
A process for the preparation of a separator membrane suitable for use in electrochemical cells comprising the steps of: (a) forming a graft polymerization medium consisting substantially of water, from about 0.5 to about 25 weight percent of one or more ethylenically unsaturated hydrophilic monomers and one or more polymerization retardants selected from the group consisting of water soluble cupric salts, ferrous salts or mixtures thereof, in an amount sufficient to retard the polymerization of said monomers; (b) placing said medium in contact with an inert polymeric base film; and (c) irradiating said film while in contact with said medium with sufficient radiation to graft polymerize said monomers onto said film, wherein all weight percents are based on the total weight of the medium.
Claim 3
Dependent Claim
40 words
A process according to claim 1, wherein said irradiating step is with gamma radiation at a total dose sufficient to provide up to 500 weight percent graft, wherein the weight percent is based on the total weight of the membrane.
Claim 4
Dependent Claim
26 words
A process according to claim 2, wherein said irradiating step is with gamma radiation at a total dose of from about 0.075 to about 10.0 Mrad.
Claim 5
Dependent Claim
22 words
A process according to claim 1, wherein said medium comprises from about 0.1 to about 10 weight percent of said polymerization retardants.
Claim 6
Dependent Claim
37 words
A process according to claim 1, wherein said polymerization retardant is selected from the group consisting of ferrous sulfate, ammonium ferrous sulfate, ferrous chloride, ferrous nitrate, cupric sulfate, cupric chloride, cupric nitrate, cupric acetate and mixtures thereof.
Claim 7
Dependent Claim
15 words
A process according to claim 5, wherein said retardant is ferrous sulfate or cupric sulfate.
Claim 8
Dependent Claim
19 words
A process according to claim 1, wherein said irradiating dose rate is from about 3000 to about 30,000 r/hr.
Claim 9
Dependent Claim
63 words
A process according to claim 1, wherein said base film is selected from the group consisting of: (a) polymer films of ethylenically unsaturated monomers having from 2 to 3 carbon atoms; (b) polymer films of halogenated ethylenically unsaturated monomers having from 2 to 3 carbon atoms; (c) copolymer films of said unsaturated monomers and said halongenated unsaturated monomers; and (d) laminated films thereof.
Claim 10
Dependent Claim
36 words
A process according to claim 8, wherein said base film is selected from the group consisting of polypropylene film, polyethylene film, polytetrafluoroethylene film, polytrifluorochloroethylene film, tetrafluoroethylene hexafluoroethylene copolymer film, tetrafluoroethylene-ethylene copolymer film and laminated films thereof.
Claim 11
Dependent Claim
27 words
A process according to claim 1, wherein said hydrophilic monomer is selected from the group consisting of ethylenically unsaturated aromatic and aliphatic hydrocarbons containing hydrophilic functional groups.
Claim 12
Dependent Claim
16 words
A process according to claim 10, wherein said hydrophilic monomer is acrylic acid or methacrylic acid.
Claim 13
Dependent Claim
20 words
The process of claim 1 wherein said polymerization retardant is about from 0.5 to 8 weight percent of said medium.
Claim 14
Dependent Claim
33 words
The process of claim 1 wherein said retardant is ferrous sulfate or cupric sulfate, wherein said hydrophilic monomer is acrylic acid or methacrylic acid, wherein said base film is polyethylene, polypropylene or polytetrafluoroethylene.
Claim 15
Dependent Claim
19 words
The process of claims 1 or 13 wherein dissolved oxygen is removed from said medium prior to said irradiating.
Claim 16
Dependent Claim
42 words
The process of claims 1 or 13 wherein the base film is covered with an absorbant interlayer and wound into a roll, said roll is immersed in said polymerization medium, dissolved oxygen is removed from said medium and said irradiating is conducted.
Claim 17
Dependent Claim
52 words
The process of claims 1 or 13 wherein said electrochemical cell is a secondary electrochemical cell having a catholyte compartment which contains a positive electrode selected from the group consisting of silver or nickel, and an anolyte compartment which contains a negative electrode selected from the group consisting of zinc or cadmium.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-12 | 1986-01-11 | 1986-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-12 | 1990-01-11 | 1990-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-12 | 1994-01-11 | 1994-07-13 | $7700.00 | Window Closed / Lapsed |