Method to synthesize and produce thin films by spray pyrolysis
Assignee: Radiation Monitoring Devices Inc
•
Filing: 1981-02-03
•
Granted: 1982-07-06
•
Expires: 2001-02-03
Abstract
Abstract Forming a film by spraying onto a heated substrate an atomized solution containing the appropriate salt of a constituent element of the film and a reducing agent at a concentration greater than 1 M and greater than 10 times the stoichiometric amount of reducing agent.
Inventors
- 👤 Richard L. Turcotte
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 23:44
CPC Classifications
H; H10; H10F; H10F71/00; H10F71/127; H10F71/1272; C; C03; C03C; C03C17/00; C03C17/22; C23; C23C; C23C18/00; C23C18/02; C23C18/12; C23C18/1204; C23C18/125; C23C18/1258; C23C18/16; C23C18/1601; C23C18/1633; C23C18/1646; C23C18/165; C23C18/1651; C23C18/1655; C23C18/1675; C23C18/1678; C23C18/31; H10F71/125; H10F71/1253; C03C2217/00; C03C2217/20; C03C2217/28; C03C2217/283; C03C2217/287; C03C2217/288; C03C2217/289; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/112; C23C18/48; C23C18/50; Y; Y02; Y02E; Y02E10/00; Y02E10/50; Y02E10/543; Y02E10/544
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
116 words
In the process of making a thin film comprising preparing a solution with solute elements including a salt of a first constituent element of said film and spraying said solution onto a heated substrate to form a film on said substrate, the solute and solvent elements not constituting said film forming volatile reaction products after contacting said heated substrate, said solution also including a reducing agent in sufficient amount to change the oxidation state of at least one said solute element after contacting said heated substrate, the improvement wherein the concentration of said reducing agent is greater than 1 M and greater than 10 times the stoichiometric amount necessary to react with said one solute element.
Claim 2
Dependent Claim
116 words
In the process of making a thin film comprising preparing a solution with solute elements including a salt of a first constituent element of said film and spraying said solution onto a heated substrate to form a film on said substrate, the solute and solvent elements not constituting said film forming volatile reaction products after contacting said heated substrate, said solution also including a reducing agent in sufficient amount to change the oxidation state of at least one said solute element after contacting said heated substrate, the improvement wherein the concentration of said reducing agent is greater than 1 M and greater than 10 times the stoichiometric amount necessary to react with said one solute element.
Claim 3
Dependent Claim
20 words
The improvement of claim 1 wherein the concentration of said reducing agent is greater than 900 times the stoichiometric amount.
Claim 4
Dependent Claim
17 words
The improvement of claim 1 wherein said one solute element is a constituent element of said film.
Claim 5
Dependent Claim
38 words
The improvement of claim 3 wherein said one solute element is said first constituent element and is tellurium, said solute elements further comprising a soluble inorganic compound of a second constituent element, said second constituent element being cadmium.
Claim 6
Dependent Claim
34 words
The improvement of claim 4 wherein said salt of said first constituent element is (NH 4 ) 2 TeO 4 and said soluble inorganic compound of said second constituent element is Cd(OH) 2 .
Claim 7
Dependent Claim
26 words
The improvement of claim 4 or 5 wherein another said solute element is a dopant, said dopant changing in oxidation state after contacting said heated substrate.
Claim 8
Dependent Claim
25 words
The improvement of claim 1 wherein said one solute element is an impurity that converts to a volatile form with said change in oxidation state.
References Cited (Backward Citations)
US3148084A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-05 | 1986-01-04 | 1986-07-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-05 | 1990-01-04 | 1990-07-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-05 | 1994-01-04 | 1994-07-06 | $7700.00 | Window Closed / Lapsed |