Formation of zinc phosphate coating on metallic surface

Claim 2

An acidic aqueous coating solution for forming a zinc phosphate coating on a metal surface consisting essentially of about 0.4 to about 1 g/l of zinc, about 5 to about 40 g/l of phosphate, about 0.01 to about 0.2 g/l of nitrite and about 2 to about 5 g/l of chlorate.

Claim 3

The composition of claim 1 wherein the concentration of zinc is from about 0.5 to about 0.9 g/l, the concentration of phosphate is from about 10 to about 20 g/l, the concentration of nitrite is from about 0.04 to about 0.15 g/l, and the concentration of chlorate is from about 2.5 to about 4 g/l.

Claim 4

The composition of claim 1 wherein the source of zinc is a compound selected from the group consisting of zinc oxide, zinc carbonate, and zinc nitrate.

Claim 5

The composition of claim 1 wherein the source of phosphate is a compound selected from the group consisting of phosphoric acid, alkali metal phosphate, zinc phosphate and nickel phosphate.

Claim 6

The composition of claim 1 wherein the source of nitrite is a compound selected from the group consisting of alkali metal nitrite and ammonium nitrite.

Claim 7

The composition of claim 1 wherein the source of chlorate is a compound selected from the group consisting of chloric acid, alkali metal chlorate, and ammonium chlorate.

Claim 8

The composition of claim 1 including at least about 0.2 g/l of one or more ions selected from the group consisting of nickel, cobalt, calcium, and manganese.

Claim 9

The composition of claim 7 wherein the concentration of said ion is from about 0.2 to about 2 g/l.

Claim 10

The composition of claim 7 wherein the source of nickel ion is a compound selected from the group consisting of nickel carbonate, nickel nitrate, nickel chloride, and nickel phosphate.

Claim 11

The composition of claim 7 wherein the source of cobalt ion is cobalt carbonate, cobalt nitrate, cobalt chloride, and cobalt phosphate.

Claim 12

The composition of claim 7 wherein the source of calcium ion is a compound selected from the group consisting of calcium carbonate, calcium nitrate, calcium chloride, and calcium phosphate.

Claim 13

The composition of claim 7 wherein the source of manganese ion is a compound selected from the group consisting of manganese carbonate, manganese nitrate, manganese chloride and manganese phosphate.

Claim 14

The composition of claim 1 or 7 including about 0 to about 4 g/l of a complex fluoride ion.

Claim 15

The composition of claim 1 or 7 including about 0 to about 5 g/l of chloride ion.

Claim 16

The composition of claim 1 or 7 including about 0 to about 15 g/l of nitrate ion.

Claim 17

An acidic aqueous composition for forming a zinc phosphate coating on a metal surface consisting essentially of about 0.5 to about 0.9 g/l of zinc ion, about 10 to about 20 g/l of phosphate ion, about 0.04 to about 0.15 g/l of nitrite ion, about 2.5 to about 4 g/l of chlorate ion, and about 0.2 to about 2 g/l of one or more ions selected from the group consisting of nickel, cobalt, calcium and manganese.

Claim 18

An acidic aqueous composition for forming a zinc phosphate coating on a metal surface consisting essentially of about 0.5 to about 0.9 g/l of zinc ion, about 10 to about 20 g/l of phosphate ion, about 0.04 to about 0.15 g/l of nitrite ion, about 2.5 to about 4 g/l of chlorate ion, and about 0.2 to about 2 g/l of one or more ions selected from the group consisting of nickel, cobalt, calcium and manganese.

Claim 19

A process for forming a zinc phosphate coating on a metal surface comprising contacting the metal surface with an acidic aqueous coating composition comprising about 0.4 to about 1 g/l of zinc ion, about 5 to about 40 g/l of phosphate ion, about 0.01 to about 0.2 g/l of nitrite ion, and about 2 to about 5 g/l of chlorate ion.

Claim 20

A process for forming a zinc phosphate coating on a metal surface comprising contacting the metal surface with an acidic aqueous coating composition comprising about 0.4 to about 1 g/l of zinc ion, about 5 to about 40 g/l of phosphate ion, about 0.01 to about 0.2 g/l of nitrite ion, and about 2 to about 5 g/l of chlorate ion.

Claim 21

A process according to claim 17 wherein said composition is sprayed on said surface.

Claim 22

The process of claim 18 wherein the metal surface is sprayed for longer than about 40 seconds.

Claim 23

The process of claim 19 wherein the metal surface is sprayed with the coating composition for about 1 to about 3 minutes.

Claim 24

The process of claim 20 wherein the metal surface is sprayed with the coating composition for about 1.5 to about 2.5 minutes.

Claim 25

The process of claim 18 wherein the temperature of the coating composition is about 40° to about 70° C.

Claim 26

The process of claim 22 wherein the temperature of the coating composition is about 50° to about 60° C.

Claim 27

The process of claim 18 wherein the pressure of spraying is about 0.5 to about 2 kg/cm 2 .

Claim 28

A process for forming a zinc phosphate coating on a metal surface comprising subjecting the surface to at least one cycle of the following sequential steps: (A) spraying the metal surface for about 10 to about 30 seconds with an acidic aqueous coating composition comprising about 0.4 to about 1 g/l of zinc ion, about 5 to about 40 g/l of phosphate ion, about 0.01 to about 0.2 g/l of nitrite ion, and about 2 to about 5 g/l of chlorate ion; (B) suspending the spraying for about 5 to about 30 seconds; and then (C) spraying the metal surface with the coating composition so that the total time of spraying is longer than about 40 seconds.

Claim 29

A process for forming a zinc phosphate coating on a metal surface comprising subjecting the surface to at least one cycle of the following sequential steps: (A) spraying the metal surface for about 10 to about 30 seconds with an acidic aqueous coating composition comprising about 0.4 to about 1 g/l of zinc ion, about 5 to about 40 g/l of phosphate ion, about 0.01 to about 0.2 g/l of nitrite ion, and about 2 to about 5 g/l of chlorate ion; (B) suspending the spraying for about 5 to about 30 seconds; and then (C) spraying the metal surface with the coating composition so that the total time of spraying is longer than about 40 seconds.

Claim 30

The process of claim 25 wherein the first spraying is about 15 to about 25 seconds.

Claim 31

The process of claim 25 wherein the spraying is suspended for about 10 to about 20 seconds.

Claim 32

The process of claim 25 wherein the total time of spraying is about 1 minute to about 3 minutes.

Claim 33

The process of claim 25 wherein the temperature of the coating composition is about 40° to about 70° C.

Claim 34

The process of claim 29 wherein the temperature of the coating composition is about 50° to about 60° C.

Claim 35

The process of claim 25 wherein the pressure of spraying is about 0.5 to about 2 kg/cm 2 .

Claim 36

The process according to claim 17 or 25 including applying to said zinc phosphate coating a paint film by cationic electrodeposition.

Claim 37

The process according to claim 17 or 25 including applying to said zinc phosphate coating a paint film by cationic electrodeposition, wherein said zinc phosphate coating is not treated with chromium prior to applying thereto said paint film.

Claim 38

A metal surface having thereon a zinc phosphate coating formed by the process of claim 17 or 25.

Claim 39

In a process wherein a zinc phosphate coating is formed on a metal surface by spraying the metal surface with an aqueous coating solution capable of forming thereon a zinc phosphate coating, wherein the coating solution tends to unduly etch the metal surface and/or form coatings characterized by imperfections such as being non-uniform, rusty or a blue-iron phosphate coating, the improvement comprising subjecting the metal surface to at least one cycle of the sequential steps which include spraying the metal surface with the coating solution and thereafter suspending the spraying of the solution for time periods sufficient to form crystalline nuclei which function as sites for the subsequent formation of plate-like crystal structures, and thereafter spraying the metal surface with the composition for a period of time sufficient to form said plate-like crystals, wherein the coating solution which is intermittently sprayed on the metal surface as aforesaid consists essentially of the coating solution defined in claim 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12 or 16, and including applying to the zinc phosphate coating a paint film by cationic electrodeposition.

Claim 40

The process according to claim 35 wherein the metal surface is initially sprayed for about 10 to about 30 seconds, then spraying is suspended for about 5 to about 30 seconds, and thereafter the metal surface is sprayed so the total time of spraying is longer than about 40 seconds.

Claim 41

The process according to claim 35 wherein the metal surface is iron or zinc.