Laser treatment method for imparting increased mechanical strength to glass objects
Assignee: Rexam Beverage Can Co
•
Filing: 1980-08-21
•
Granted: 1982-07-06
•
Expires: 2000-08-21
Abstract
Abstract A method for imparting increased mechanical strength to a glass object having imperfections in a surface thereof. The glass object is heated to a temperature above the strain point of the glass. A laser beam is generated having a wavelength absorbable by the glass and impinged on all portions of the surface containing the imperfections. The power density at which the beam is impinged is sufficient to rapidly heat a surface stratum of the glass to establish a thermal gradient therein whereby the viscosity at a depth from the surface sufficient to encompass the imperfections is low enough that the stress induced by the surface tension of the glass at the sites of the imperfections is sufficient to cause flow of glass and effect a reforming of the glass surface at said sites.
Inventors
- 👤 M. Clifford Brockway
- 👤 Craig T. Walters
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 19:01
CPC Classifications
C; C03; C03B; C03B29/00; C03B29/04; B; B23; B23K; B23K26/00; B23K26/02; B23K26/06; B23K26/073; B23K26/0736; B23K26/08; B23K26/0823; B23K26/352; B23K26/3568; B23K26/3576; C03B27/00; C03B27/012; C03B29/02; Y; Y10; Y10S; Y10S65/00; Y10S65/04
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
173 words
A method for imparting increased mechanical strength to a glass object having imperfections in a surface thereof, comprising the steps of: heating the object to a temperature above the strain point of the glass; generating a laser beam having a wavelength absorbable by the glass; and impinging said beam on all portions of said surface from which it is desired to remove said imperfections, the power density of said beam being sufficient to rapidly heat a surface stratum of said glass to establish a thermal gradient therein whereby the viscosity at a depth from said surface sufficient to encompass said imperfections is low enough that the stress induced by the surface tension of the glass at the sites of said imperfections is sufficient to cause flow to glass and effect a reforming of the glass surface at said sites, the dwell time of said beam at any particular portion of said surface being limited so that flow inducing viscosities do not extend to a depth beyond a thin surface stratum of the glass.
Claim 2
Independent Claim
173 words
A method for imparting increased mechanical strength to a glass object having imperfections in a surface thereof, comprising the steps of: heating the object to a temperature above the strain point of the glass; generating a laser beam having a wavelength absorbable by the glass; and impinging said beam on all portions of said surface from which it is desired to remove said imperfections, the power density of said beam being sufficient to rapidly heat a surface stratum of said glass to establish a thermal gradient therein whereby the viscosity at a depth from said surface sufficient to encompass said imperfections is low enough that the stress induced by the surface tension of the glass at the sites of said imperfections is sufficient to cause flow to glass and effect a reforming of the glass surface at said sites, the dwell time of said beam at any particular portion of said surface being limited so that flow inducing viscosities do not extend to a depth beyond a thin surface stratum of the glass.
Claim 3
Dependent Claim
21 words
A method as set forth in claim 1 wherein said laser is continuous and the beam is scanned over said surface.
Claim 4
Dependent Claim
37 words
A method as seth forth in claim 2 wherein said laser beam is in a fixed position and said object is simultaneously rotated and translated so that an outside surface thereof is entirely scanned by said beam.
Claim 5
Dependent Claim
38 words
A method as set forth in claim 3 wherein the path on said surface upon which said beam impinges overlaps in successive rotations so that said surface is heated to a substantially uniform maximum temperature for reforming thereof.
Claim 6
Dependent Claim
30 words
A method as set forth in claim 2 wherein the power density of the laser in the beam impinged on said surface is at least about 500 W/cm 2 .
Claim 7
Dependent Claim
21 words
A method as set forth in claim 5 wherein said power density is not greater than about 50,000 W/cm 2 .
Claim 8
Dependent Claim
22 words
A method as set forth in claim 6 wherein said power density is between about 2000 and about 10,000 W/cm 2 .
Claim 9
Dependent Claim
37 words
A method as set forth in claim 5 wherein said laser beam is in a fixed position and said object is simultaneously rotated and translated so that an outside surface thereof is entirely scanned by said beam.
Claim 10
Dependent Claim
33 words
A method as set forth in claim 8 wherein the dwell time of said beam on any point of said surface during the scanning thereof is between about 0.2 and about 25 msec.
Claim 11
Dependent Claim
38 words
A method as set forth in claim 9 wherein the path on said surface upon which said beam impinges overlaps in successive rotations so that said surface is heated to a substantially uniform maximum temperature for reforming thereof.
Claim 12
Dependent Claim
18 words
A method as set forth in claim 10 wherein said overlap is between about 5 and about 70%.
Claim 13
Dependent Claim
34 words
A method as set forth in claim 9 wherein scanning is carried out at a high ratio of circumferential to translational velocity such that dwell time is substantially entirely governed by the circumferential velocity.
Claim 14
Dependent Claim
42 words
A method as set forth in claim 12 wherein the beam impinging on said surface is of elongate configuration with its short dimension in the direction of circumferential movement and its long dimension in the direction of translational movement of said object.
Claim 15
Dependent Claim
44 words
A method as set forth in claim 1 wherein said depth is at least about 10 μm but the glass remains at a temperature low enough to resist flow beyond a stratum having a thickness no greater than about 150 m inside said surface.
Claim 16
Dependent Claim
31 words
A method as set forth in claim 14 wherein said stratum is heated to a temperature gradient such that the viscosity at said depth is no greater than about 105 poises.
Claim 17
Dependent Claim
30 words
A method as set forth in claim 1 wherein said stratum is heated to a temperature at which its surface viscosity is no greater than about 10 3 .5 poises.
Claim 18
Dependent Claim
27 words
A method as set forth in claim 16 wherein the surface on which said beam impinges is heated to a temperature of at least about 1200° C.
Claim 19
Dependent Claim
23 words
A method as set forth in claim 17 wherein the temperature in said stratum is at least about 900° C. at said depth.
Claim 20
Dependent Claim
25 words
A method as set forth in claim 1 wherein said wavelength is such that the optical penetration thereof is not more than about 10 μm.
Claim 21
Dependent Claim
26 words
A method as set forth in claim 19 wherein said glass is a soda/lime glass and said wavelength is between about 5 and about 12 μm.
Claim 22
Dependent Claim
62 words
A method as set forth in claim 1 wherein impingement of said beam rapidly creates a steep temperature gradient in the surface stratum of the glass and the dwell time of said beam at any particular portion of said surface is limited so that flow inducing viscosities do not extend to a depth sufficient to result in material deformation of the object.
Claim 23
Dependent Claim
30 words
A method as set forth in claim 14 wherein said stratum is heated to a temperature at which its surface viscosity is no greater than about 10 3 .5 poises.
Claim 24
Dependent Claim
27 words
A method as set forth in claim 22 wherein the surface on which said beam impinges is heated to a temperature of at least about 1200° C.
Claim 25
Dependent Claim
23 words
A method as set forth in claim 23 wherein the temperature in said stratum is at least about 900° C. at said depth.
Claim 26
Dependent Claim
15 words
A method as set forth in claim 1 wherein said object comprises a glass container.
Claim 27
Dependent Claim
39 words
A method as set forth in claim 1 or 25 further comprising applying a coating over said object after reformation of the surface thereof to protect said surface from abrasion and preserve it from the formation of additional imperfections.
Claim 28
Dependent Claim
26 words
A method as set forth in claim 26 wherein said coating comprises an inorganic oxide selected from the group consisting of tin oxide and titanium oxide.
Claim 29
Dependent Claim
20 words
A method as set forth in claim 27 wherein said coating comprises a plastic containment coating over said oxide coating.
Claim 30
Dependent Claim
16 words
A method as set forth in claim 26 wherein said coating comprises a plastic containment coating.
References Cited (Backward Citations)
US3259480A
Cited
US3756799A
Cited
US3538298A
Cited
US3588440A
Cited
US3656922A
Cited
US3944640A
Cited
US3663793A
Cited
US3839005A
Cited
US3764776A
Cited
US4025328A
Cited
US4146380A
Cited
US4170726A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-05 | 1986-01-04 | 1986-07-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-05 | 1990-01-04 | 1990-07-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-05 | 1994-01-04 | 1994-07-06 | $7700.00 | Window Closed / Lapsed |