Process for applying a corrosion resistant two-coat system to structural steel and coated steel thus obtained
Assignee: Akzo NV
•
Filing: 1980-12-08
•
Granted: 1982-06-29
•
Expires: 2000-12-08
Abstract
Abstract A process is disclosed for applying a corrosion resistant system to structural steel, in which a zinc dust paint comprising 5-15% by weight of a binder and 85-95% by weight of a metallic zinc-based pigment component is applied to the steel as a first coat, and subsequently a coat of a composition comprising an aromatic/aliphatic polyhydroxyether and/or a saturated aromatic polyester resin having a number average molecular weight of at least 4000 and a pigment having a Mohs hardness of at least 2, the volume ratio of the binder to the pigment being in the range of 50:50 to 95:5. The thickness of the first coat is about 15-150 μm and that of the second coat is about 15-150 μm. The invention also relates to structural steel thus coated.
Inventors
- 👤 Boudewijn van den Bergh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 17:18
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/14; B05D7/16; C; C09; C09D; C09D5/00; C09D5/08; C09D5/10; C09D5/106; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12049; Y10T428/12056; Y10T428/12063; Y10T428/12104; Y10T428/12111; Y10T428/12125
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
152 words
A process for applying a corrosion resistant system to structural steel, characterized in that to the steel there is successively applied a coat consisting of a zinc dust paint based on a binder and a pigment, the weight ratio of binder to pigment being in the range of 5:95 to 15:85 and the pigment consisting essentially of 55 to 100 percent by weight of metallic zinc and a coat to a composition based on a binder in the form of an aromatic/aliphatic polyhydroxyether and/or a saturated aromatic polyester resin having a number average molecular weight of at least 4000, and a pigment having a Mohs hardness of at least 2, and the volume ratio of the binder to the pigment is in the range of 50:50 to 95:5, the thickness of the first coat being about 15 to 150 μm and that of the second coat about 15 to about 150 μm.
Claim 2
Dependent Claim
152 words
A process for applying a corrosion resistant system to structural steel, characterized in that to the steel there is successively applied a coat consisting of a zinc dust paint based on a binder and a pigment, the weight ratio of binder to pigment being in the range of 5:95 to 15:85 and the pigment consisting essentially of 55 to 100 percent by weight of metallic zinc and a coat to a composition based on a binder in the form of an aromatic/aliphatic polyhydroxyether and/or a saturated aromatic polyester resin having a number average molecular weight of at least 4000, and a pigment having a Mohs hardness of at least 2, and the volume ratio of the binder to the pigment is in the range of 50:50 to 95:5, the thickness of the first coat being about 15 to 150 μm and that of the second coat about 15 to about 150 μm.
Claim 3
Dependent Claim
19 words
The process of claim 1, wherein in addition to zinc the zinc dust paint contains another electrically conductive pigment.
Claim 4
Dependent Claim
38 words
The process of claim 1, wherein the zinc dust paint contains a corrosion resistant pigment or a corrosion inhibitor in an amount which is not more than 10 percent by weight, based on the total amount of pigment.
Claim 5
Dependent Claim
17 words
The process of claim 1, wherein the binder contained in the zinc dust paint is ethyl silicate.
Claim 6
Dependent Claim
18 words
The process of claim 1, wherein the binder contained in the zinc dust paint is an epoxy resin.
Claim 7
Dependent Claim
15 words
The process of claim 5, wherein the epoxy resin is a bisglycidyl ether of Bisphenol-A.
Claim 8
Dependent Claim
25 words
The process of claim 1, wherein in the second coat the volume ratio of binder to pigment is in the range of 65:35 to 75:25.
Claim 9
Dependent Claim
17 words
The process of claim 1, wherein the pigment contained in the second coat is micaceous iron oxide.
Claim 10
Dependent Claim
19 words
The process of claim 8, wherein the pigment comprises at least 50 percent by weight of micaceous iron oxide.
Claim 11
Dependent Claim
19 words
The process of claim 9, wherein the pigment comprises at least 55 percent by weight of micaceous iron oxide.
Claim 12
Dependent Claim
21 words
Structural steel provided with a corrosion resistant system obtained by the process of any one of the claims 1 to 10.
Claim 13
Dependent Claim
149 words
A process for improving the corrosion resistance of a corrodible structural steel surface which comprises coating said surface with a paint consisting of from 85 to 95 percent by weight of a pigment and from 5 to 15 percent by weight of a binder, the pigment consisting essentially of 55 to 100 percent by weight of particulate zinc and then coating the resulting painted surface with a coating composition consisting of from 5 to 50% by volume of a pigment having a MOHS hardness of at least 2 and a binder comprising a polyhydroxy ether and a saturated aromatic polyester resin having a number average molecular weight of at least 4000 or consisting of said saturated aromatic polyester resin, and thickness of the paint coating being from about 15 to 150 μm and that of the coating applied to the painted surface being about 15 to about 150 μm.
Claim 14
Dependent Claim
149 words
A process for improving the corrosion resistance of a corrodible structural steel surface which comprises coating said surface with a paint consisting of from 85 to 95 percent by weight of a pigment and from 5 to 15 percent by weight of a binder, the pigment consisting essentially of 55 to 100 percent by weight of particulate zinc and then coating the resulting painted surface with a coating composition consisting of from 5 to 50% by volume of a pigment having a MOHS hardness of at least 2 and a binder comprising a polyhydroxy ether and a saturated aromatic polyester resin having a number average molecular weight of at least 4000 or consisting of said saturated aromatic polyester resin, and thickness of the paint coating being from about 15 to 150 μm and that of the coating applied to the painted surface being about 15 to about 150 μm.
References Cited (Backward Citations)
FR1307766A
Cited
US3849141A
Cited
JPS5263942A
Cited
DE2612154B1
Cited
US4229495A
Cited
US4157924A
Cited
US4186036A
Cited
JPS5573372A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-28 | 1985-12-28 | 1986-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-28 | 1989-12-28 | 1990-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-28 | 1993-12-28 | 1994-06-29 | $7700.00 | Window Closed / Lapsed |