Abstract
Abstract An inexpensive, disposable, three-dimensionally contoured container, suitable for many purposes including holding food during exposure to high temperatures for long times in either a microwave or a conventional oven without any detrimental effect to the container or the food. The container consists of an essentially impervious liner of polyethylene terephthalate directly bonded by its own substance to a pre-formed contoured base obtained by molding to final shape nonbrowning substantially 100% bleached kraft wood pulp from an aqueous slurry thereof against an open-face suction mold, and drying the same under pressure imposed by a mating pair of heated dies. The liner is formed by bonding to the pulp base a 0.5-2.0 mil thick film of thermoformable, substantially amorphous, substantially unoriented polyethylene terephthalate having a molecular weight which is understood to be in excess of 15,000. The film is bonded to the base by pre-heating the base, rapidly pre-heating the film and then quickly pressing the film into contact with the base at a temperature in the range of 300°-375° F., the pressing being done by vacuum in the range of about 20 inches of mercury applied through the base for no longer than about 1 second, and finally cooling so that the liner thereafter will not shrink-separate away from the contoured base as a result of subsequently exposing the container to a temperature of up to 400° F.
Inventors
- 👤 Peter D. Foster
- 👤 Clifford Stowers
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:54
CPC Classifications
D; D21; D21J; D21J7/00; B; B29; B29C; B29C51/00; B29C51/16; B29C51/162; B32; B32B; B32B27/00; B32B27/06; B32B27/10; B65; B65D; B65D1/00; B65D1/22; B65D1/26; B65D1/28; B65D1/34; B65D1/36; B29C2795/00; B29C2795/002; Y; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1002; Y10T156/1028; Y10T428/00; Y10T428/13; Y10T428/1348; Y10T428/1352; Y10T428/1362; Y10T428/24; Y10T428/24628; Y10T428/31504; Y10T428/31786; Y10T428/3179
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
233 words
A process for directly bonding a substantially impervious polyester liner to a contoured molded pulp base which comprises the steps of (1) pre-heating a pre-formed base which has been obtained by molding fibrous pulp from an aqueous slurry thereof against an open-face suction mold to substantially finished contoured shape which includes horizontal and sloping but no substantially vertical wall portions, (2) pre-heating a film of polyester and (3) then pressing the pre-heated film into contact with at least one contoured portion of at least one surface of the pre-heated base so that the film is stretched into direct contact with the contoured base and becomes directly bonded to the base to form a contiguous and integral liner thereon, the improvement being that the polyester film is (a) substantially amorphous, substantially unoriented polyethylene terephthalate and it (b) is pre-heated to a thermoforming temperature within the range in which it will substantially crystallize in time but then (c) is rapidly pressed into contact with and bonded to the base while it is still substantially amorphous and before enough time has passed in that temperature range to crystallize it to the stage at which it will not directly bond to the base, whereby (d) after the lined product is cooled to room temperature the liner will not shrink-separate away from the contoured base as a result of subsequent exposure to a temperature of about 400° F.
Claim 2
Dependent Claim
233 words
A process for directly bonding a substantially impervious polyester liner to a contoured molded pulp base which comprises the steps of (1) pre-heating a pre-formed base which has been obtained by molding fibrous pulp from an aqueous slurry thereof against an open-face suction mold to substantially finished contoured shape which includes horizontal and sloping but no substantially vertical wall portions, (2) pre-heating a film of polyester and (3) then pressing the pre-heated film into contact with at least one contoured portion of at least one surface of the pre-heated base so that the film is stretched into direct contact with the contoured base and becomes directly bonded to the base to form a contiguous and integral liner thereon, the improvement being that the polyester film is (a) substantially amorphous, substantially unoriented polyethylene terephthalate and it (b) is pre-heated to a thermoforming temperature within the range in which it will substantially crystallize in time but then (c) is rapidly pressed into contact with and bonded to the base while it is still substantially amorphous and before enough time has passed in that temperature range to crystallize it to the stage at which it will not directly bond to the base, whereby (d) after the lined product is cooled to room temperature the liner will not shrink-separate away from the contoured base as a result of subsequent exposure to a temperature of about 400° F.
Claim 3
Dependent Claim
66 words
A process as in claim 1 wherein the film has a thickness of less than about 2.0 mil, and it is pre-heated to a thermoforming temperature within the range of from about 250° F. to about 400° F. but then is rapidly pressed into contact with and bonded to the base before the film has been at that thermoforming temperature for longer than about 2 seconds.
Claim 4
Dependent Claim
46 words
A process as in claim 2 wherein the base has been obtained by molding fibrous substantially 100% bleached kraft wood pulp from an aqueous slurry thereof against an open-face suction mold, and then drying the same under pressure imposed by a mating pair of heated dies.
Claim 5
Dependent Claim
42 words
A process as in claim 1 wherein the starting film of polyethylene terephthalate is substantially amorphous having less than about 5% crystallinity, and the crystallinity of the liner bonded to the molded pulp base has been increased to at least about 8%.
Claim 6
Dependent Claim
26 words
A process as in claim 1 wherein the polyethylene terephthalate liner is no longer readily bondable to molded pulp at any temperature below about 400° F.
Claim 7
Dependent Claim
19 words
A process as in claim 1 wherein the polyethylene terephthalate has a molecular weight in excess of about 15,000.
Claim 8
Dependent Claim
63 words
A process as in claim 1 wherein the starting film of polyethylene terephthalate becomes thermoformable at and above a temperature of about 170° F., it crystallizes when held for more than a few seconds at a temperature in the range between about 250° F. and about 400° F., and it melts at temperatures in excess of about 480° F. to about 490° F.
Claim 9
Dependent Claim
12 words
A polyester-lined molded pulp product produced by the process of claim 1.
Claim 10
Dependent Claim
12 words
A polyester-lined molded pulp product produced by the process of claim 1.
Claim 11
Dependent Claim
122 words
A plastic-lined molded pulp product which is three-dimensionally contoured with horizontal and sloping but no substantially vertical wall portions to permit like products to be nested one within another in a stack of such products, the product comprising a pre-formed base obtained by molding fibrous pulp from an aqueous slurry thereof against an open-face suction mold to substantially finished contoured shape, and a substantially impervious liner directly bonded to at least one contoured portion of at least one surface of the molded pulp base, the liner consisting essentially of polyethylene terephthalate obtained from a substantially amorphous and substantially unoriented film thereof which will not shrink-separate away from the contoured base as a result of exposure to a temperature of about 400° F.
Claim 12
Dependent Claim
122 words
A plastic-lined molded pulp product which is three-dimensionally contoured with horizontal and sloping but no substantially vertical wall portions to permit like products to be nested one within another in a stack of such products, the product comprising a pre-formed base obtained by molding fibrous pulp from an aqueous slurry thereof against an open-face suction mold to substantially finished contoured shape, and a substantially impervious liner directly bonded to at least one contoured portion of at least one surface of the molded pulp base, the liner consisting essentially of polyethylene terephthalate obtained from a substantially amorphous and substantially unoriented film thereof which will not shrink-separate away from the contoured base as a result of exposure to a temperature of about 400° F.
Claim 13
Dependent Claim
36 words
A product as in claim 10 wherein the pre-formed base is obtained by molding fibrous pulp to substantially finished contoured shape, and then drying the pulp under pressure imposed by a mating pair of heated dies.
Claim 14
Dependent Claim
41 words
A product as in claim 10 wherein the fibrous pulp of which the contoured base is molded will not exhibit significant undesirable browning as a result of exposure to a temperature of about 400° F. for as long as 15 minutes.
Claim 15
Dependent Claim
23 words
A product as in claim 10 wherein the pulp of which the contoured base is molded is substantially 100% bleached kraft wood fibers.
Claim 16
Dependent Claim
33 words
A product as in claim 10 wherein the fibrous pulp of which the contoured base is molded has been treated with a fluorocarbon oil repellant sizing and/or a reactive synthetic water repellant sizing.
Claim 17
Dependent Claim
20 words
A product as in claim 10 wherein the polyethylene terephthalate liner has a molecular weight in excess of about 15,000.
Claim 18
Dependent Claim
25 words
A product as in claim 10 wherein the polyethylene terephthalate liner is not readily bondable to molded pulp at any temperature below about 400° F.
Claim 19
Dependent Claim
19 words
A product as in claim 10 wherein the polyethylene terephthalate liner has a crystallinity of at least about 8%.
References Cited (Backward Citations)
US2986490A
Cited
US3657044A
Cited
US3697369A
Cited
US3453162A
Cited
DE2125978A1
Cited
US3939025A
Cited
US3953283A
Cited
US3932105A
Cited
US4145239A
Cited
US4147836A
Cited
US4202465A
Cited
US4200481A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-28 | 1985-12-28 | 1986-06-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-28 | 1989-12-28 | 1990-06-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-28 | 1993-12-28 | 1994-06-29 | $7700.00 | Window Closed / Lapsed |