Additive composition for Portland cement materials

Claim 2

An additive composition to decrease the normal setting time and increase the normal compressive strength of a portland cement containing composition such as mortar and concrete, consisting essentially of, an aqueous solution of (i) calcium nitrate present in an amount of at least 30 parts by weight per 100 parts of said solution, and (ii) a polyalkanolamine of a lower alkanol having from 2 to about 5 carbon atoms, said polyalkanolamine being present in an amount in the range from about 0.05 parts to about 5 parts per 100 parts by weight of said solution, said solution being stable in storage in the temperature range from about 32° F. to about 140° F.

Claim 3

The additive composition of claim 1 including in addition an alkali metal salt or alkaline earth metal salt of an organic stabilizer selected from the group consisting of an aliphatic polyhydroxy compound having from about 5 to about 9 carbon atoms, and lignosulfonic acid, said stabilizer being present in an amount in the range from about 0.010 parts to about 5 parts per 100 parts by weight of said solution.

Claim 4

The additive composition of claim 2 wherein said polyalkanolamine is a mixture of polyethanolamines including a major amount of triethanolamine and a minor amount of diethanolamine.

Claim 5

The additive composition of claim 3 wherein said polyethanolamines are present in a triethanol bottoms waste stream containing from 50-80 percent by weight of triethanolamine, and from about 10 to 15 percent by weight of diethanolamine.

Claim 6

The additive composition of claim 3 wherein said organic stabilizer is selected from sodium glucoheptonate and sodium lignosulfonic acid.

Claim 7

The additive composition of claim 4 wherein said aqueous solution consists essentially of (i) a calcium nitrate solution containing from about 40 to 60 parts by weight of calcium nitrate per 100 parts of said solution, (ii) said polyethanolamines are present in a waste polyethanolamine stream comprising a major amount of triethanolamine by weight, said waste stream being present in an amount in the range from about 0.05 part to about 15 parts by weight per 100 parts by weight of said aqueous solution, and (iii) said organic stabilizer is present in an amount in the range from about 0.05 part to about 10 parts by weight per 100 parts of said aqueous solution.

Claim 8

The additive composition of claim 6 having a pH in the range from about 7 to about 10, and a specific gravity in the range from about 1.4 to about 1.5.

Claim 9

A concrete mix comprising a portland cement and a set-accelerating additive composition consisting essentially of (i) Ca(NO 3 ) 2 in an amount from about 0.5 percent to about 3 percent by weight of said cement as an aqueous solution free of CaCl 2 to which solution is added (ii) diethanolamine, triethanolamine, or a mixture of polyethanolamines, in an amount in the range from about 0.005% to about 0.3% by wt of said cement, and optionally, (iii) an alkali metal salt or an alkaline earth metal salt of an organic stabilizer selected from the group consisting of an aliphatic polyhydroxy cpmpound having from about 5 to about 9 carbon atoms and lignosulfonic acid, in an amount in the range from about 0.005% to about 0.1% by wt of said cement, whereby the concrete formed will develop a compressive strength of at least about 2500 psi at the end of 3 days.

Claim 10

A concrete mix comprising a portland cement and a set-accelerating additive composition consisting essentially of (i) Ca(NO 3 ) 2 in an amount from about 0.5 percent to about 3 percent by weight of said cement as an aqueous solution free of CaCl 2 to which solution is added (ii) diethanolamine, triethanolamine, or a mixture of polyethanolamines, in an amount in the range from about 0.005% to about 0.3% by wt of said cement, and optionally, (iii) an alkali metal salt or an alkaline earth metal salt of an organic stabilizer selected from the group consisting of an aliphatic polyhydroxy cpmpound having from about 5 to about 9 carbon atoms and lignosulfonic acid, in an amount in the range from about 0.005% to about 0.1% by wt of said cement, whereby the concrete formed will develop a compressive strength of at least about 2500 psi at the end of 3 days.

Claim 11

The concrete mix of claim 8 wherein said salt of said aliphatic polyhydroxy compound is sodium glucoheptonate and said salt of lignosulfonic acid is sodium lignosulfonic acid.

Claim 12

A process for reducing the setting time of a concrete mixture made with a portland cement composition and for increasing the compressive strength of a set concrete mixture at the end of a predetermined period of time, which process comprises adding to the cement composition an effective amount of an aqueous additive composition consisting essentially of, (i) Ca(NO 3 ) 2 in an amount from about 0.5 percent to about 3 percent by weight of said cement as an aqueous solution free of CaCl 2 to which solution is added (ii) diethanolamine, triethanolamine, or a mixture of polyethanolamines, in a combined amount in the range from about 0.005% to about 0.3% by wt of said cement, and, optionally, (iii) an alkali metal salt or an alkaline earth metal salt of an organic stabilizer selected from the group consisting of an aliphatic polyhydroxy compound having from about 5 to about 9 carbon atoms and lignosulfonic acid, in an amount in the range from about 0.005% to about 0.1% by wt of said cement, whereby the concrete formed will develop a compressive strength of at least about 2500 psi at the end of 3 days.

Claim 13

A process for reducing the setting time of a concrete mixture made with a portland cement composition and for increasing the compressive strength of a set concrete mixture at the end of a predetermined period of time, which process comprises adding to the cement composition an effective amount of an aqueous additive composition consisting essentially of, (i) Ca(NO 3 ) 2 in an amount from about 0.5 percent to about 3 percent by weight of said cement as an aqueous solution free of CaCl 2 to which solution is added (ii) diethanolamine, triethanolamine, or a mixture of polyethanolamines, in a combined amount in the range from about 0.005% to about 0.3% by wt of said cement, and, optionally, (iii) an alkali metal salt or an alkaline earth metal salt of an organic stabilizer selected from the group consisting of an aliphatic polyhydroxy compound having from about 5 to about 9 carbon atoms and lignosulfonic acid, in an amount in the range from about 0.005% to about 0.1% by wt of said cement, whereby the concrete formed will develop a compressive strength of at least about 2500 psi at the end of 3 days.