High strength insulation materials
Assignee: Lebanon Steel Foundry
•
Filing: 1980-09-10
•
Granted: 1982-06-22
•
Expires: 2000-09-10
Abstract
Abstract Novel perlite-silicate type insulation materials are provided having improved physical strength qualities. More particularly, such materials are provided having high flexural or transverse strength as measured by A.S.T.M. standard C-203. According to a preferred embodiment, amounts of phosphate within a limited proportioned range are added to insulation mixtures to yield shaped insulating bodies having a flexural strength in excess of about 60 lb./in. 2 . Addition of clay is made according to another preferred embodiment, whereby substantial reduction in shrinkage is accomplished.
Inventors
- 👤 Edward G. Vogel
- 👤 Rodney C. Westlund
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 09:49
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/24; C04B28/26; C04B28/34; C04B28/344; F; F16; F16L; F16L59/00; F16L59/02; F16L59/021; F16L59/024; C04B2111/00; C04B2111/34; Y; Y10; Y10S; Y10S106/00; Y10S106/02
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
105 words
A coherent, rigid, solid material made from a mixture said mixture comprising by weight a. from about 20 to about 50 parts of expanded perlite, b. from about 9.5 to about 19 parts of sodium or potassium silicate in the form of an aqueous solution thereof, c. an amount sufficient to improve the transverse strength of said solid material, of a phosphate, said phosphate being capable of substantially dissolving in said aqueous solution, said amount being between about 0.05% and about 5.0% by weight of said mixture and; d. from about 21 to about 67 parts of water, including that found in said aqueous solution.
Claim 2
Dependent Claim
105 words
A coherent, rigid, solid material made from a mixture said mixture comprising by weight a. from about 20 to about 50 parts of expanded perlite, b. from about 9.5 to about 19 parts of sodium or potassium silicate in the form of an aqueous solution thereof, c. an amount sufficient to improve the transverse strength of said solid material, of a phosphate, said phosphate being capable of substantially dissolving in said aqueous solution, said amount being between about 0.05% and about 5.0% by weight of said mixture and; d. from about 21 to about 67 parts of water, including that found in said aqueous solution.
Claim 3
Dependent Claim
29 words
The material of claim 1 further comprising an amount equal to from about 20% to about 25% of the total weight taken together with said silicate of a clay.
Claim 4
Dependent Claim
10 words
The material of claim 2 wherein said clay is Kaolin.
Claim 5
Dependent Claim
17 words
The material of claim 1 further comprising from about 0.5 to about 3 parts of fiberous material.
Claim 6
Dependent Claim
12 words
The material of claim 4 wherein said fiberous material is a polyester.
Claim 7
Dependent Claim
30 words
The material of claim 1, 2, 3, 4 or 5 wherein said phosphate is selected from the group consisting of mono-, di-, and tri-sodium or potassium phosphate and mixtures thereof.
Claim 8
Dependent Claim
20 words
The material of claim 1 wherein said phosphate is present in an amount of from about 0.1% to about 2%.
Claim 9
Dependent Claim
20 words
The material of claim 1 wherein said phosphate is present in an amount of from about 0.3% to about 1.5%.
Claim 10
Dependent Claim
13 words
The material of claim 1 which has been formed into a shaped body.
Claim 11
Dependent Claim
16 words
The material of claim 1 having a flexural strength in excess of 60 lb/in 2 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-06-21 | 1985-12-21 | 1986-06-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-06-21 | 1989-12-21 | 1990-06-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-06-21 | 1993-12-21 | 1994-06-22 | $7700.00 | Window Closed / Lapsed |