Method for optical monitoring in materials fabrication
Assignee: AT&T Inc
•
Filing: 1980-02-29
•
Granted: 1982-06-01
•
Expires: 2000-02-29
Abstract
Abstract It has been found that the dielectric function ε(ν) of materials is strongly dependent on the microstructure of the material, i.e., on the volume fractions that are crystalline, amorphous, and void, respectively. This sensitivity makes it possible to conveniently and nondestructively determine by optical methods, typically a form of spectroscopic ellipsometry, the microstructure of layers of material that are typically bounded by a free surface. The determination of actual volume fractions is made by fitting the result of a model calculation, typically in an effective medium approximation, to the measured dielectric function over an appropriate range of frequencies, e.g. frequencies corresponding to photon energies of approximately 1.5 eV-6 eV. Alternatively, the measured dielectric function, or selected features or functions thereof, can be compared to preselected standard values. In either case, if this is done in a manufacturing context then the information derived allows appropriate adjustment of some manufacturing parameter or step. This can for instance be done by means of in situ monitoring and feedback, or by means of measurements after completion of the deposition of the material, resulting in the ability to tailor subsequent processing steps to the actually existing material state. The method is applicable to dielectrics, doped and undoped semiconductors, and to metals.
Inventors
- 👤 David E. Aspnes
- 👤 Brian G. Bagley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 19:48
CPC Classifications
G; G01; G01N; G01N21/00; G01N21/17; G01N21/21; G01N21/211; G01N21/84; G01N21/8422
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
104 words
Method for fabricating an article by a sequence of fabrication steps, one of the steps comprising forming a polycrystalline or amorphous material, the method comprising (a) determining a measured dielectric function ε m (ν) at a multiplicity of frequencies within a frequency range in which the dielectric function of the material ε(ν) is substantially affected by interband or intraband transitions of electrons in the material, (b) comparing the value of a function of ε m (ν) at one or more frequencies to predetermined values, and (c) modifying at least one of the sequence of fabrication steps in accordance with the result of the comparison.
Claim 2
Dependent Claim
104 words
Method for fabricating an article by a sequence of fabrication steps, one of the steps comprising forming a polycrystalline or amorphous material, the method comprising (a) determining a measured dielectric function ε m (ν) at a multiplicity of frequencies within a frequency range in which the dielectric function of the material ε(ν) is substantially affected by interband or intraband transitions of electrons in the material, (b) comparing the value of a function of ε m (ν) at one or more frequencies to predetermined values, and (c) modifying at least one of the sequence of fabrication steps in accordance with the result of the comparison.
Claim 3
Dependent Claim
106 words
Method for fabricating an article by a sequence of fabrication steps, one of the steps comprising forming a polycrystalline or amorphous material, the method comprising (a) determining a measured dielectric function ε m (ν) at a multiplicity of frequencies within a frequency range in which the dielectric function of the material ε(ν) is substantially affected by interband or intraband transitions of electrons in the material, (b) determining from ε m (ν) the volume fractions of the material that are amorphous, crystalline, and void, respectively, and (c) modifying at least one of the sequence of fabrication steps in accordance with the result of the determination in (b).
Claim 4
Dependent Claim
106 words
Method for fabricating an article by a sequence of fabrication steps, one of the steps comprising forming a polycrystalline or amorphous material, the method comprising (a) determining a measured dielectric function ε m (ν) at a multiplicity of frequencies within a frequency range in which the dielectric function of the material ε(ν) is substantially affected by interband or intraband transitions of electrons in the material, (b) determining from ε m (ν) the volume fractions of the material that are amorphous, crystalline, and void, respectively, and (c) modifying at least one of the sequence of fabrication steps in accordance with the result of the determination in (b).
Claim 5
Dependent Claim
23 words
Method according to claim 1 wherein the function of ε m (ν) is a derivative of ε m (ν) with respect to frequency.
Claim 6
Dependent Claim
16 words
Method according to claim 1 wherein the function of ε m (ν) is ε m (ν).
Claim 7
Dependent Claim
16 words
Method according to claim 1 or 2 wherein the material comprises a doped or undoped semiconductor.
Claim 8
Dependent Claim
10 words
Method according to claim 5 wherein the semiconductor is silicon.
Claim 9
Dependent Claim
13 words
Method according to claim 1 or 2 wherein the material comprises a dielectric.
Claim 10
Dependent Claim
19 words
Method according to claim 7 wherein the dielectric is SiO x or SiN y , with 0<x≦2, and 0<y≦4/3
Claim 11
Dependent Claim
13 words
Method according to claim 1 or 2 wherein the material comprises a metal.
Claim 12
Dependent Claim
12 words
Method according to claim 9 wherein the metal comprises aluminum or gold.
Claim 13
Dependent Claim
17 words
Method according to claim 1 or 2 wherein ε m (ν) is determined by photometric spectroscopic ellipsometry.
Claim 14
Dependent Claim
24 words
Method according to claim 11 wherein the frequency range extends from frequencies corresponding to photon energies of approximately 1.5 eV to approximately 6 eV.
Claim 15
Dependent Claim
24 words
Method according to claim 1 or 2 wherein the temperature at which at least one of the fabrication steps is carried out is modified.
Claim 16
Dependent Claim
24 words
Method according to claim 1 or 2 wherein the flow rate of a gas in at least one of the fabrication steps is modified.
Claim 17
Dependent Claim
26 words
Method according to claim 1 or 2 wherein a time of exposure of the article to electromagnetic radiation in at least one fabrication step is modified.
Claim 18
Dependent Claim
19 words
Method according to claim 1 or 2 wherein an etching condition in at least one fabrication step is modified.
Claim 19
Dependent Claim
16 words
Method according to claim 1 or 2 wherein the material is formed by chemical vapor deposition.
Claim 20
Dependent Claim
18 words
Method according to claim 1 or 2 wherein the material is formed by low pressure chemical vapor deposition.
Claim 21
Dependent Claim
14 words
Method according to claim 1 or 2 wherein the material is formed by sputtering.
Claim 22
Dependent Claim
18 words
Method according to claim 1 or 2 wherein the material is formed by evaporation from an evaporation source.
References Cited (Backward Citations)
US4197632A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-31 | 1985-11-30 | 1986-06-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-31 | 1989-11-30 | 1990-06-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-31 | 1993-11-30 | 1994-06-01 | $7700.00 | Window Closed / Lapsed |