Cutting tip for metal-removing processing

Claim 2

A cutting tip for shaping and metal removal during the manufacture of metal parts comprising the following composition: 70-90 weight percent of aluminum oxide; 10-30 weight percent of zirconium oxide; 0.1-0.5 weight percent of magnesium oxide; wherein the amount of other oxide impurities is less than 0.6 weight percent and the proportions of components add up to 100, said composition being sintered at high temperatures and having a porosity of less than 2%; an average particle size of less than 1.7 μm; and a fracture toughness K Ic at room temperature of at least 190 N/mm 3 / 2 and of at least 140 N/mm 3 / 2 at 1000° C., measured on prismatic rods 2.5 mm wide, 3.5 mm high and 12 mm long, cut from the cutting tips and provided with a saw cut 120 μm wide, 0.8±0.1 mm deep and having a notch radius of between 50 and 60 μm.

Claim 3

The cutting tip of claim 1 wherein the average particle size is between 1.4 and 1.6 μm and 90% of all particles lie within this size range.

Claim 4

The cutting tip of claim 1 or 2 wherein the fracture toughness K Ic is at least 200 N/mm 3 / 2 at room temperature and at least 150 N/mm 3 / 2 at 1000° C.

Claim 5

The cutting tip of claim 1 or 2 wherein the zirconium oxide content is from about 13 to 17 weight percent and the density is at least 4.1 g/cm 3 .

Claim 6

The cutting tip of claim 1 or 2 wherein the porosity is less than about 1%.

Claim 7

The cutting tip of claims 1 or 2 wherein the median pore size is less than 2 μm.

Claim 8

A process for the production of a cutting tip comprising intimately mixing: 70-90 weight percent of aluminum oxide with an Al 2 O 3 content of at least 99% and an average particle size of a median value of less than 1.0 μm; 10-30 weight percent of zirconium oxide with a ZrO 2 content of at least 99% and an average particle size of a median value of less than 1.0 μm; and 0.1-0.5 weight percent of pure magnesium oxide, the oxide impurities of this starting powder mixture amounting to less than 0.6 weight percent; molding cutting tips of the desired geometrical shape from the mixture and sintering the molded mixture at a temperature of 1500° to 1600° C. for a period of at least 3 hours and then cooling the sintered product.

Claim 9

A process for the production of a cutting tip comprising intimately mixing: 70-90 weight percent of aluminum oxide with an Al 2 O 3 content of at least 99% and an average particle size of a median value of less than 1.0 μm; 10-30 weight percent of zirconium oxide with a ZrO 2 content of at least 99% and an average particle size of a median value of less than 1.0 μm; and 0.1-0.5 weight percent of pure magnesium oxide, the oxide impurities of this starting powder mixture amounting to less than 0.6 weight percent; molding cutting tips of the desired geometrical shape from the mixture and sintering the molded mixture at a temperature of 1500° to 1600° C. for a period of at least 3 hours and then cooling the sintered product.

Claim 10

The process of claim 7 wherein the molded mixture is sintered at a temperature from 1520° to 1560° C. for a period of from 6 to 10 hours.

Claim 11

The process of claim 7 or 8 wherein the rate of heating to the sintering temperature and the rate of cooling to room temperature after sintering is about 200° C. per hour.

Claim 12

The process of claim 7 or 8 wherein the sintering is carried out in an oxidizing atmosphere.

Claim 13

The process of claim 7 or 8 wherein the median value of the particle size of the zirconium oxide is less than about 0.5 μm.

Claim 14

The process of claims 7 or 8 wherein the mixture is molded at a pressure of at least 6000 N/cm 2 .

Claim 15

The process of claim 7 or 8 wherein the mixture is molded at a pressure of at least 12,000 to 16,000 N/cm 2 .

Claim 16

The process of claims 7 or 8 wherein a molding auxiliary is mixed into the mixture prior to molding.

Claim 17

The process of claim 14 wherein the molding auxiliary is a polyvinyl alcohol.

Claim 18

In a method for manufacturing an article from a metal selected from the group consisting of case-hardened steel, quenched steel and tempered steel, wherein the steel is processed with a cutting tip, at cutting speeds greater than 500 m/min, the improvement which comprises said cutting tip being composed of the following composition 70-90 weight percent of aluminum oxide, 10-30 weight percent of zirconium oxide, 0.1-0.5 weight percent of magnesium oxide, wherein the amount of other oxide impurities is less than 0.6 weight percent and the proportions of components add up to 100, said composition being sintered at high temperatures and having a porosity of less than 2%, an average particle size of less than 1.7 μm, and a fracture toughness K Ic at room temperature of at least 190 N/mm 3 / 2 and of least 140 N/mm 3 / 2 at 1000° C., measured on prismatic rods 2.5 mm wide, 3.5 mm high and 12 mm long, cut from the cutting tips and provided with a saw cut 120 μm wide, 0.8±0.1 mm deep and having a notch radius of between 50 and 60 μm.

Claim 19

In a method for manufacturing an article from a metal selected from the group consisting of case-hardened steel, quenched steel and tempered steel, wherein the steel is processed with a cutting tip, at cutting speeds greater than 500 m/min, the improvement which comprises said cutting tip being composed of the following composition 70-90 weight percent of aluminum oxide, 10-30 weight percent of zirconium oxide, 0.1-0.5 weight percent of magnesium oxide, wherein the amount of other oxide impurities is less than 0.6 weight percent and the proportions of components add up to 100, said composition being sintered at high temperatures and having a porosity of less than 2%, an average particle size of less than 1.7 μm, and a fracture toughness K Ic at room temperature of at least 190 N/mm 3 / 2 and of least 140 N/mm 3 / 2 at 1000° C., measured on prismatic rods 2.5 mm wide, 3.5 mm high and 12 mm long, cut from the cutting tips and provided with a saw cut 120 μm wide, 0.8±0.1 mm deep and having a notch radius of between 50 and 60 μm.

Claim 20

A composition comprising 70 to 90 weight percent of aluminum oxide; 10 to 30 weight percent of zirconium oxide; 0.1 to 0.5 weight percent of magnesium oxide; wherein the amount of other oxide impurities is less than 0.6 weight percent and the proportions of components add up to 100, said composition being sintered at high temperatures and having a porosity of less than 2%, an average particle size of less than 1.7 μm, and a fracture toughness K Ic at room temperature of at least 190 N/mm 3 / 2 and of at least 140 N/mm 3 / 2 at 1000° C., measured on prismatic rods of said sintered composition 2.5 mm wide, 3.5 mm high and 12 mm long and provided with a saw cut 120 μm wide, 0.8±0.1 mm deep and having a notch radius of between 50 and 60 μm.

Claim 21

A composition comprising 70 to 90 weight percent of aluminum oxide; 10 to 30 weight percent of zirconium oxide; 0.1 to 0.5 weight percent of magnesium oxide; wherein the amount of other oxide impurities is less than 0.6 weight percent and the proportions of components add up to 100, said composition being sintered at high temperatures and having a porosity of less than 2%, an average particle size of less than 1.7 μm, and a fracture toughness K Ic at room temperature of at least 190 N/mm 3 / 2 and of at least 140 N/mm 3 / 2 at 1000° C., measured on prismatic rods of said sintered composition 2.5 mm wide, 3.5 mm high and 12 mm long and provided with a saw cut 120 μm wide, 0.8±0.1 mm deep and having a notch radius of between 50 and 60 μm.