Solid electrolyte

Claim 2

A solid electrolyte having high electron conductivity and high oxide ion conductivity, which is composed of a sintered body consisting substantially of (a) 5 to 85 mole% of an oxide of cobalt, (b) 2 to 70 mole% of an oxide of at least one metal selected from strontium and lanthanum, and (c) 13 to 80 mole% of an oxide of at least one metal selected from bismuth and cerium.

Claim 3

The solid electrolyte of claim 1 which has an electron conductivity of at least 10 -2 ohm -1 .cm -1 .

Claim 4

The solid electrolyte of claim 1 which has an electron conductivity of at least 10 -1 ohm -1 .cm -1 .

Claim 5

The solid electrolyte of claim 1 which has an oxide ion conductivity of at least 10 -4 ohm -1 .cm -1 .

Claim 6

The solid electrolyte of claim 1 which has an oxide ion conductivity of at least 10 -3 ohm -1 .cm -1 .

Claim 7

The solid electrolyte of claim 1 wherein the sintered body consists substantially of (a) 10 to 80 mole% of the oxide of cobalt, (b) 3 to 60 mole% of the oxide of at least one metal selected from strontium and lanthanum, and (c) 15 to 70 mole% of the oxide of at least one metal selected from bismuth and cerium.

Claim 8

The solid electrolyte of claim 1 wherein the sintered body consists substantially of (a) cobalt oxide, (b) lanthanum oxide, and (c) bismuth oxide.

Claim 9

The solid electrolyte of claim 1 wherein the sintered body consists substantially of (a) 15 to 40 mole% of cobalt oxide, (b) 40 to 55 mole% of strontium oxide, and (c) 15 to 40 mole% of cerium oxide.

Claim 10

The solid electrolyte of claim 7 wherein the sintered body consists substantially of (a) 15 to 75 mole% of cobalt oxide, (b) 13 to 45 mole% of lanthanum oxide, and (c) 17 to 50 mole% of bismuth oxide.

Claim 11

A process for producing a solid shaped electrolyte composed of a sintered body consisting substantially of (a) cobalt oxide, (b) at least one of strontium oxide and lanthanum oxide and (c) at least one of bismuth oxide and cerium oxide by the steps of forming a mixture consisting substantially of (i) cobalt, cobalt oxide, or a cobalt compound capable of being decomposed to cobalt oxide under the below defined firing conditions, (ii) at least one of strontium metal, lanthanum metal, strontium oxide, lanthanum oxide and compound of strontium or lanthanum capable of being decomposed to the respective metal oxide of strontium or lanthanum under the below defined firing conditions, and (iii) at least one of bismuth metal, cerium metal, bismuth oxide, cerium oxide, and compounds of bismuth or cerium capable of being decomposed to the respective metal oxide of bismuth or cerium under the below defined firing conditions, press-forming the mixture into a desired shape, and firing the shaped mixture at a temperature of from about 400° C. to about 1400° C. in an oxygen-containing gas atmosphere, wherein said mixture contains components (i), (ii), and (iii) in such proportions as to provide the respective oxides of (a), (b) and (c) in mole percentages of 5 to 85 mole%, 2 to 70 mole% and 13 to 80 mole%, respectively.

Claim 12

A process for producing a solid shaped electrolyte composed of a sintered body consisting substantially of (a) cobalt oxide, (b) at least one of strontium oxide and lanthanum oxide and (c) at least one of bismuth oxide and cerium oxide by the steps of forming a mixture consisting substantially of (i) cobalt, cobalt oxide, or a cobalt compound capable of being decomposed to cobalt oxide under the below defined firing conditions, (ii) at least one of strontium metal, lanthanum metal, strontium oxide, lanthanum oxide and compound of strontium or lanthanum capable of being decomposed to the respective metal oxide of strontium or lanthanum under the below defined firing conditions, and (iii) at least one of bismuth metal, cerium metal, bismuth oxide, cerium oxide, and compounds of bismuth or cerium capable of being decomposed to the respective metal oxide of bismuth or cerium under the below defined firing conditions, press-forming the mixture into a desired shape, and firing the shaped mixture at a temperature of from about 400° C. to about 1400° C. in an oxygen-containing gas atmosphere, wherein said mixture contains components (i), (ii), and (iii) in such proportions as to provide the respective oxides of (a), (b) and (c) in mole percentages of 5 to 85 mole%, 2 to 70 mole% and 13 to 80 mole%, respectively.