Method of sintering tubular ceramic parts
Assignee: Alcatel Lucent SAS
•
Filing: 1980-07-28
•
Granted: 1982-05-18
•
Expires: 2000-07-28
Abstract
Abstract A tubular ceramic part is formed with a shoulder at an open end of the part, the tubular part is inserted in an opening provided in a horizontal plate which is disposed inside a sintering chamber so that the part is kept suspended in the chamber by means of the shoulder which rests against the edge of the opening, a shouldered cylindrical plug is inserted into the open end of the tubular part until the shoulder of the plug bears against the end of the tubular part, and the chamber is brought to sintering temperature. The invention is implemented to produce solid beta sodium alumina electrolyte tubes for sodium-sulphur electric cells.
Inventors
- 👤 Gerard Desplanches
- 👤 Gerard LeClerc
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:55
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/113; C04B35/622; C04B35/64; H; H01; H01M; H01M10/00; H01M10/36; H01M10/39; H01M10/3909; H01M10/3918; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/131
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
178 words
A method of making a tubular part of sintered ceramic, the method including forming a tubular part of ceramic material, said tubular part having one open end, placing the part in a sintering chamber, and bringing the chamber up to sintering temperature, wherein the improvement comprises: during said forming step, imparting an extra thickness to the outer wall of the tubular part for a predetermined length adjacent to the said open end; inserting a plug into said open end of the tubular part, said plug having a body of predetermined length slidably fitting within, and a shoulder bearing against, said open end of the tubular part; and suspending the tubular part substantially vertically within the chamber from a support encircling at least part of the circumference of the tubular member such that the thickened outer wall rests on the support and the other end of the tubular member does not touch the bottom of the chamber, prior to bringing the chamber to sintering temperature, whereby the tubular part is free to shrink during the sintering process wthout distortion.
Claim 2
Independent Claim
178 words
A method of making a tubular part of sintered ceramic, the method including forming a tubular part of ceramic material, said tubular part having one open end, placing the part in a sintering chamber, and bringing the chamber up to sintering temperature, wherein the improvement comprises: during said forming step, imparting an extra thickness to the outer wall of the tubular part for a predetermined length adjacent to the said open end; inserting a plug into said open end of the tubular part, said plug having a body of predetermined length slidably fitting within, and a shoulder bearing against, said open end of the tubular part; and suspending the tubular part substantially vertically within the chamber from a support encircling at least part of the circumference of the tubular member such that the thickened outer wall rests on the support and the other end of the tubular member does not touch the bottom of the chamber, prior to bringing the chamber to sintering temperature, whereby the tubular part is free to shrink during the sintering process wthout distortion.
Claim 3
Dependent Claim
37 words
A method according to claim 1, wherein the ratio between the predetermined length of said extra thickness of the outer wall of the tubular part and the entire length of the part is between 0.1% and 5%.
Claim 4
Dependent Claim
35 words
A method according to claim 1, wherein the predetermined length of the body of said plug is approximately equal to the predetermined length of said extra thickness of the outer wall of the tubular part.
Claim 5
Dependent Claim
33 words
A method according to claim 1, wherein said extra thickness of the outer wall of the tubular part is in the form of a circumferential lip at said open end of said part.
Claim 6
Dependent Claim
51 words
A method according to claim 1, wherein said support comprises a horizontal plate having at least one hole therethrough, the diameter of the hole being smaller than the maximum cross dimension of the extra thickness of the outer wall of the tubular part, said tubular part being inserted through said hole.
Claim 7
Dependent Claim
21 words
A method according to claim 1, wherein said tubular part, said plug, and said support have substantially the same ceramic composition.
Claim 8
Dependent Claim
28 words
A method according to claim 6, wherein said tubular part and said support are made of alkaline beta alumina, and said plug is made of alkaline alpha alumina.
Claim 9
Dependent Claim
93 words
A tubular part made of sintered ceramic material, said part having an open end formed with an extra thickness of the outer wall adjacent thereto, wherein, after being formed, said part was sintered at a high temperature while being vertically suspended from an encircling support against which said extra thickness of the outer wall rested, with a plug being inserted into the open end of the tubular part to prevent collapse of the open end during the sintering process, whereby the shape of said tubular part was not deformed during the sintering thereof.
Claim 10
Dependent Claim
93 words
A tubular part made of sintered ceramic material, said part having an open end formed with an extra thickness of the outer wall adjacent thereto, wherein, after being formed, said part was sintered at a high temperature while being vertically suspended from an encircling support against which said extra thickness of the outer wall rested, with a plug being inserted into the open end of the tubular part to prevent collapse of the open end during the sintering process, whereby the shape of said tubular part was not deformed during the sintering thereof.
References Cited (Backward Citations)
US2914834A
Cited
US2948949A
Cited
US4068048A
Cited
FR2317067B3
Cited
FR2341533A1
Cited
FR2397376B1
Cited
US4263381A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-17 | 1985-11-16 | 1986-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-17 | 1989-11-16 | 1990-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-17 | 1993-11-16 | 1994-05-18 | $7700.00 | Window Closed / Lapsed |