Assignee: Kuraray Co Ltd
•
Filing: 1979-12-20
•
Granted: 1982-05-18
•
Expires: 1999-12-20
Abstract
Abstract Mixing (a) a carboxylic acid, (b) a divalent or trivalent metal oxide or hydroxide and (c) a foundry molding sand in the presence of an aqueous solution of (d) a carboxyl-group-containing polymer or (e) water followed by shaping and curing can provide sand molds having sufficiently high green strength without contamination of the working environment. The molding sand composition has excellent processability, which means filling of shapes or molds with the sand can be done with ease. The sand molds manufactured in this way can be disintegrated by a simple procedure. Therefore the molding sand can be used over and over again and does not cause environmental pollution due to disposal of the molding sand.
Inventors
- 👤 Hideo Takahashi
- 👤 Keishiro Igi
- 👤 Hisashi Ogawara
- 👤 Haruo Nakayasu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 01:11
CPC Classifications
B; B22; B22C; B22C1/00; B22C1/16; B22C1/20; B22C1/22; B22C1/2206; C; C08; C08K; C08K13/00; C08K13/02
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
130 words
A method of manufacturing foundry sand molds which comprises mixing (a) 0.0015-0.2 parts by weight of a polycarboxylic acid having 2-20 carbon atoms and containing two or more carboxyl groups per molecule or a hydroxyl carboxylic acid having 2-20 carbon atoms and containing at least one carboxyl group and one hydroxyl group; (b) 0.001-0.05 parts by weight of an oxide or hydroxide of magnesium, aluminum, calcium, zinc or iron and (c) one part by weight of a foundry molding sand in the presence of water and (d) 0.006-0.055 parts by weight of a carboxyl group containing polymer selected from the group consisting of homopolymers and copolymers of unsaturated aliphatic carboxylic acids, polyvinyl alcohols containing side chains into which carboxyl groups have been introduced, and carboxymethylcellulose followed by shaping and curing.
Claim 2
Independent Claim
130 words
A method of manufacturing foundry sand molds which comprises mixing (a) 0.0015-0.2 parts by weight of a polycarboxylic acid having 2-20 carbon atoms and containing two or more carboxyl groups per molecule or a hydroxyl carboxylic acid having 2-20 carbon atoms and containing at least one carboxyl group and one hydroxyl group; (b) 0.001-0.05 parts by weight of an oxide or hydroxide of magnesium, aluminum, calcium, zinc or iron and (c) one part by weight of a foundry molding sand in the presence of water and (d) 0.006-0.055 parts by weight of a carboxyl group containing polymer selected from the group consisting of homopolymers and copolymers of unsaturated aliphatic carboxylic acids, polyvinyl alcohols containing side chains into which carboxyl groups have been introduced, and carboxymethylcellulose followed by shaping and curing.
Claim 3
Dependent Claim
33 words
The method of claim 1, wherein the carboxylic acid (a) is a saturated aliphatic dicarboxylic acid selected from the group consisting of oxalic, malonic, succinic, glutaric, adipic, pimelic, suberic, azelaic and sebacic acid.
Claim 4
Dependent Claim
13 words
The method of claim 1, wherein the carboxylic acid (a) is tricarballylic acid.
Claim 5
Dependent Claim
37 words
The method of claim 1, wherein the carboxylic acid (a) is an unsaturated aliphatic dicarboxylic acid selected from the group consisting of maleic acid, maleic anhydride, fumaric acid, citraconic acid, mesaconic acid, itaconic acid and itaconic anhydride.
Claim 6
Dependent Claim
29 words
The method of claim 1, wherein the carboxylic acid (a) is an unsaturated aliphatic tri- or polycarboxylic acid selected from the group consisting of 2-carboxymaleic acid and 2-carboxyglutaconic acid.
Claim 7
Dependent Claim
30 words
The method of claim 1, wherein the carboxylic acid (a) is an aromatic dicarboxylic acid selected from the group consisting of phthalic acid, isophthalic acid, terephthalic acid and phthalic anhydride.
Claim 8
Dependent Claim
34 words
The method of claim 1, wherein the carboxylic acid (a) is an aromatic tri- or polycarboxylic acid selected from the group consisting of trimellitic acid, trimellitic anhydride, pyromellitic acid, 1,2,4,5-benzenetetracarboxylic dianhydride and benzenepentacarboxylic acid.
Claim 9
Dependent Claim
30 words
The method of claim 1, wherein the carboxylic acid (a) is an aliphatic hydroxycarboxylic acid selected from the group consisting of glycolic, malic, lactic, trihydroxyglutaric, tartaric, citric and hydroxyacrylic acid.
Claim 10
Dependent Claim
27 words
The method of claim 1, wherein the carboxylic acid (a) is an aromatic hydroxycarboxylic acid selected from the group consisting of hydroxybenzoic, 2-hydroxyisophthalic, 4,5-dihydroxyphthalic and 2,5-dihydroxyterephthalic acid.
Claim 11
Dependent Claim
13 words
The method of claim 1, wherein the carboxylic acid (a) is maleic anhydride.
Claim 12
Dependent Claim
16 words
The method of claim 1, wherein the carboxylic acid (a) is citric acid or malic acid.
Claim 13
Dependent Claim
42 words
The method of claim 1, wherein the divalent or trivalent metal oxide or hydroxide (b) is a metal compound selected from the group consisting of magnesium oxide, calcium oxide, zinc oxide, aluminum oxide, magnesium hydroxide, calcium hydroxide, aluminum hydroxide and iron oxide.
Claim 14
Dependent Claim
17 words
The method of claim 1, wherein the divalent or trivalent metal oxide or hydroxide is magnesium oxide.
Claim 15
Dependent Claim
39 words
The method of claim 1, wherein the divalent or trivalent metal oxide or hydroxide is magnesium oxide that has a size of 220 to 320 angstroms in the [200] direction of the crystal thereof as measured by X-ray diffractometry.
Claim 16
Dependent Claim
43 words
The method of claim 1, wherein the carboxyl-group-containing polymer (d) is a polymer selected from the group consisting of polyacrylic acid, acrylic acid copolymers, methacrylic acid copolymers, alpha-olefin-maleic anhydride copolymers, styrenemaleic anhydride copolymer, vinyl acetate-maleic anhydride copolymer and methy vinyl ether-maleic anhydride copolymer.
Claim 17
Dependent Claim
20 words
The method of claim 1, wherein the carboxyl-group-containing polymer is a homopolymer or copolymer of an unsaturated aliphatic carboxylic acid.
Claim 18
Dependent Claim
29 words
The method of claim 16, wherein the unsaturated aliphatic carboxylic acid is an acid selected from the group consisting of acrylic, methacrylic, crotonic, itaconic, maleic, citraconic and mesaconic acid.
Claim 19
Independent Claim
104 words
A method of manufacturing foundry sand molds, which comprises: (a) mixing maleic anhydride, magnesium oxide and a foundry molding sand in amounts such that the weight ratio of maleic anhydride to sand ranges from 0.00015 to 0.2 and the weight ratio of magnesium oxide to sand ranges from 0.001 to 0.05 in the presence of an aqueous solution of polyacrylic acid, wherein the proportion by weight of said polyacrylic acid to sand ranges from 0.0006 to 0.055 and the proportion by weight of water in said solution to sand ranges from 0.005 to 0.05; (b) shaping the mixture; and (c) curing the shaped mixture.
Claim 20
Independent Claim
104 words
A method of manufacturing foundry sand molds, which comprises: (a) mixing maleic anhydride, magnesium oxide and a foundry molding sand in amounts such that the weight ratio of maleic anhydride to sand ranges from 0.00015 to 0.2 and the weight ratio of magnesium oxide to sand ranges from 0.001 to 0.05 in the presence of an aqueous solution of polyacrylic acid, wherein the proportion by weight of said polyacrylic acid to sand ranges from 0.0006 to 0.055 and the proportion by weight of water in said solution to sand ranges from 0.005 to 0.05; (b) shaping the mixture; and (c) curing the shaped mixture.
Claim 21
Independent Claim
104 words
A method of manufacturing foundry sand molds, which comprises: (a) mixing citric acid, magnesium oxide and a foundry molding sand in amounts such that the weight ratio of citric acid to sand ranges from 0.00015 to 0.2 and the weight ratio of magnesium oxide to sand ranges from 0.001 to 0.05 in the presence of an aqueous solution of polyacrylic acid, wherein the proportion by weight of said polyacrylic acid to sand ranges from 0.0006 to 0.055 and the proportion by weight of water in said solution to sand ranges from 0.005 to 0.05; (b) shaping the mixture; and (c) curing the shaped mixture.
Claim 22
Independent Claim
104 words
A method of manufacturing foundry sand molds, which comprises: (a) mixing citric acid, magnesium oxide and a foundry molding sand in amounts such that the weight ratio of citric acid to sand ranges from 0.00015 to 0.2 and the weight ratio of magnesium oxide to sand ranges from 0.001 to 0.05 in the presence of an aqueous solution of polyacrylic acid, wherein the proportion by weight of said polyacrylic acid to sand ranges from 0.0006 to 0.055 and the proportion by weight of water in said solution to sand ranges from 0.005 to 0.05; (b) shaping the mixture; and (c) curing the shaped mixture.
References Cited (Backward Citations)
DE656254C
Cited
US2765507A
Cited
US3330674A
Cited
US3640826A
Cited
US3947392A
Cited
GB1334695A
Cited
US4106944A
Cited
GB1504708A
Cited
US4203771A
Cited
US4183759A
Cited
GB1530641A
Cited
DE2814357A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-17 | 1985-11-16 | 1986-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-17 | 1989-11-16 | 1990-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-17 | 1993-11-16 | 1994-05-18 | $7700.00 | Window Closed / Lapsed |