Titanium trihalide catalyst and process for its production

Claim 2

A process for producing titanium trihalide solids product having an average particle size diameter greater than 35 microns and a narrow particle size distribution comprising: (a) adding an organometallic reducing compound with stirring to a solution of titanium tetrahalide in a suitable diluent at a temperature of about -50° C. to about +10° C., in a mole ratio of between about 1:3 to about 1.2:1 and at a rate such that the reduction of titanium tetrahalide to titanium trihalide is about 0.03 to about 0.2 m moles per liter per second to obtain titanium trihalide solids product in the diluent having a narrow particle size distribution and an average particle size greater than about 20 microns; (b) continuously and simultaneously adding with stirring to the titanium trihalide solids product in the diluent an organometallic reducing compound and titanium tetrahalide in a mole ratio of about 1:3 to about 1.2:1, the simultaneous addition being made at a rate such that the reduction of titanium tetrahalide to titanium trihalide is about 6×10 -4 to about 0.02 m moles per liter per second per m 2 of available preformed titanium trihalide surface area until solids product of desired size are obtained, and (c) recovering titanium trihalide solids product.

Claim 3

The process of claim 1 wherein step (a) is followed by step (b) without interruption.

Claim 4

The process of claim 1 wherein the titanium tetrahalide is titanium tetrachloride and the organometallic reducing compound is one of AlR 3 , AlR 2 X, AlRX 2 or R 3 Al 2 X 3 , wherein R is a hydrocarbyl group having from 1 to 18 carbon atoms and X is a halogen atom.

Claim 5

The process of claim 3 wherein R is an alkyl or aryl group having from 1 to 6 carbon atoms and X is chlorine.

Claim 6

The process of claim 4 wherein R is ethyl.

Claim 7

A process for producing TiCl 3 solids product having an average particle size diameter greater than 35μ and a narrow particle size distribution comprising: (a) adding R 2 AlX or mixtures thereof with RAlX 2 slowly and with stirring to a solution of titanium tetrachloride in a suitable diluent at a temperature from about -5° C. to about +10° C. and based on total moles of organoaluminum compound per mole titanium tetrachloride in a mole ratio of between about 0.9:1.0 to about 1.2:1.0 and in the presence of about 0 to about 1.0 mole of added RAlX 2 per mole of R 2 AlX, 0.0 mole to all of added RAlX 2 being in solution with titanium tetrachloride prior to the addition of R 2 AlX the remainder of the added RAlX 2 being added with R 2 AlX to the titanium tetrachloride solution, wherein R is a hydrocarbyl group having from 1 to 18 carbon atoms and X is a halogen atom, the rate of addition of the R 2 AlX to the titanium tetrachloride solution being controlled to maintain the reduction of titanium tetrachloride to titanium trichloride at about 0.03 to about 0.2 m mole per liter per second whereby there is obtained titanium trichloride solids product in the diluent having a narrow particle size distribution and an average particle size greater than about 20μ; (b) slowly simultaneously and continuously adding with stirring to the titanium trichloride solids products in the diluent R 2 AlX or mixtures thereof with RAlX 2 and titanium tetrachloride at a mole ratio based on total moles organoaluminum compound per mole titanium tetrachloride of about 0.1:1.0 to about 1.2:1.0; wherein R and X are as defined above, and wherein the stimultaneous and continuous addition is at a rate such that the reduction of titanium tetrachloride to titanium trichloride is about 6×10 -4 to about 7×10 -3 m moles per liter per second per m 2 of available preformed titanium trichloride surface area until solids product of desired size are obtained; and (c) recovering titanium trichloride solids product.

Claim 8

A process for producing TiCl 3 solids product having an average particle size diameter greater than 35μ and a narrow particle size distribution comprising: (a) adding R 2 AlX or mixtures thereof with RAlX 2 slowly and with stirring to a solution of titanium tetrachloride in a suitable diluent at a temperature from about -5° C. to about +10° C. and based on total moles of organoaluminum compound per mole titanium tetrachloride in a mole ratio of between about 0.9:1.0 to about 1.2:1.0 and in the presence of about 0 to about 1.0 mole of added RAlX 2 per mole of R 2 AlX, 0.0 mole to all of added RAlX 2 being in solution with titanium tetrachloride prior to the addition of R 2 AlX the remainder of the added RAlX 2 being added with R 2 AlX to the titanium tetrachloride solution, wherein R is a hydrocarbyl group having from 1 to 18 carbon atoms and X is a halogen atom, the rate of addition of the R 2 AlX to the titanium tetrachloride solution being controlled to maintain the reduction of titanium tetrachloride to titanium trichloride at about 0.03 to about 0.2 m mole per liter per second whereby there is obtained titanium trichloride solids product in the diluent having a narrow particle size distribution and an average particle size greater than about 20μ; (b) slowly simultaneously and continuously adding with stirring to the titanium trichloride solids products in the diluent R 2 AlX or mixtures thereof with RAlX 2 and titanium tetrachloride at a mole ratio based on total moles organoaluminum compound per mole titanium tetrachloride of about 0.1:1.0 to about 1.2:1.0; wherein R and X are as defined above, and wherein the stimultaneous and continuous addition is at a rate such that the reduction of titanium tetrachloride to titanium trichloride is about 6×10 -4 to about 7×10 -3 m moles per liter per second per m 2 of available preformed titanium trichloride surface area until solids product of desired size are obtained; and (c) recovering titanium trichloride solids product.

Claim 9

The process of claim 6 wherein added RAlX 2 is present in step (a).

Claim 10

The process of claim 6 wherein step (a) is followed by step (b) without interruption.

Claim 11

The process of claim 6 wherein X is chlorine and R can be an alkyl or aryl group having from 1 to 6 carbon atoms.

Claim 12

The process of claim 9 wherein R is ethyl.

Claim 13

The process of claim 10 wherein the mole ratio of organoaluminum compound(s) to titanium tetrachloride in step (a) is about 1.0:1.0 to about 1.2:1.0, in step (b) about 0.9:1.0 to about 1.1:1.0 and the mole ratio of added ethyl aluminum dichloride to diethylaluminum chloride is about 0.0:1.0 to about 1.0:1.0.

Claim 14

The process of claim 11 wherein the mole ratio of organoaluminum compound(s) to titanium tetrachloride in each of steps (a) and (b) is about 1:1 and the mole ratio of added ethylaluminum dichloride to diethylaluminum chloride is about 0.1:1.

Claim 15

The process of claim 11 wherein the rate of addition in step (a) is about 0.08 m moles per liter per second and the rate of reduction in step (b) is about 2.5×10 -3 m moles per liter per second per m 2 of available preformed titanium trichloride surface area.

Claim 16

The process of claim 11 wherein the temperature in step (a) and (b) is about 0° C. and the temperature is raised to 65° C. in step (c) at the rate of about 1° per minute.

Claim 17

The process of claim 11 wherein from about 0.1 to about 0.3 moles of added ethylaluminum dichloride is in solution with the titanium tetrachloride prior to the addition of diethylaluminum chloride.

Claim 18

The process of claim 15 wherein from about 0.14 to about 0.2 moles per liter of added ethylaluminum dichloride is in solution with titanium tetrachloride prior to the addition of diethylaluminum chloride.

Claim 19

The process of claim 15 wherein all the added ethylaluminum dichloride is added with the diethylaluminum chloride to the titanium tetrahalide solution.

Claim 20

The process of claim 1 or 6 wherein the titanium trihalide product in the diluent obtained in step (b) is held at about 0° C. for about one to about two hours prior to step (c).

Claim 21

The process of claim 1 or 6 wherein the recovered titanium trihalide solids product are activated to violet-type crystalline titanium halide by one of heat treatment at an activating temperature, treating under activating conditions with chlorinated hydrocarbon or treating under activating conditions with titanium tetrachloride.

Claim 22

A process for producing titanium trihalide solids product catalyst component having an average particle size diameter greater than 35 microns and a narrow particle size distribution comprising: (a) adding an organometallic reducing compound with stirring to a solution of titanium tetrahalide in a suitable diluent at a temperature of about -50° C. to about +10° C. and in a mole ratio of between about 1.0:3.0 to about 1.2:1.0 and at a rate such that the reduction of titanium tetrahalide to titanium trihalide is about 0.03 to about 0.2 m moles per liter per second to obtain titanium trihalide solids product in the diluent having a narrow particle size distribution and an average particle size greater than about 20 microns; (b) continuously, simultaneously and slowly adding with stirring to the titanium trihalide solids product in the diluent an organometallic reducing compound and titanium tetrahalide in a mole ratio of about 1.0:3.0 to about 1.2:1.0, the simultaneous addition being made at a rate such that the reduction of titanium tetrahalide to titanium trihalide is about 6×10 -4 to about 0.02 m moles per liter per second per m 2 of available preformed titanium trihalide surface area until solids product of desired size are obtained; (c) slowly raising the temperature to about 60° C. to about 70° C. and recovering titanium trihalide solids product; (d) contacting the titanium trihalide solids product with a minor amount of an alpha-olefin having at least two carbon atoms under polymerization conditions to obtain a reduced titanium trihalide solids product containing about 1 to about 1,000 wt.% of prepolymerized alpha-olefin based on the weight of titanium trihalide; and (e) treating said prepolymerized reduced solid with one of (a) a chlorinated hydrocarbon having at least 2 carbon atoms and a Lewis base complexing agent or (b) TiCl 4 and a Lewis base complexing agent to convert the prepolymerized titanium trihalide reduced solid to a substantially non-friable highly active, crystalline prepolymerized trihalide composition.

Claim 23

A process for producing titanium trihalide solids product catalyst component having an average particle size diameter greater than 35 microns and a narrow particle size distribution comprising: (a) adding an organometallic reducing compound with stirring to a solution of titanium tetrahalide in a suitable diluent at a temperature of about -50° C. to about +10° C. and in a mole ratio of between about 1.0:3.0 to about 1.2:1.0 and at a rate such that the reduction of titanium tetrahalide to titanium trihalide is about 0.03 to about 0.2 m moles per liter per second to obtain titanium trihalide solids product in the diluent having a narrow particle size distribution and an average particle size greater than about 20 microns; (b) continuously, simultaneously and slowly adding with stirring to the titanium trihalide solids product in the diluent an organometallic reducing compound and titanium tetrahalide in a mole ratio of about 1.0:3.0 to about 1.2:1.0, the simultaneous addition being made at a rate such that the reduction of titanium tetrahalide to titanium trihalide is about 6×10 -4 to about 0.02 m moles per liter per second per m 2 of available preformed titanium trihalide surface area until solids product of desired size are obtained; (c) slowly raising the temperature to about 60° C. to about 70° C. and recovering titanium trihalide solids product; (d) contacting the titanium trihalide solids product with a minor amount of an alpha-olefin having at least two carbon atoms under polymerization conditions to obtain a reduced titanium trihalide solids product containing about 1 to about 1,000 wt.% of prepolymerized alpha-olefin based on the weight of titanium trihalide; and (e) treating said prepolymerized reduced solid with one of (a) a chlorinated hydrocarbon having at least 2 carbon atoms and a Lewis base complexing agent or (b) TiCl 4 and a Lewis base complexing agent to convert the prepolymerized titanium trihalide reduced solid to a substantially non-friable highly active, crystalline prepolymerized trihalide composition.

Claim 24

The process of claim 20 wherein step (a) is followed by step (b) without interruption.

Claim 25

The process of claim 20 wherein the titanium halide is titanium chloride and the organometallic reducing compound is one of AlR 3 , AlR 2 X, AlRX 2 or R 3 Al 2 X 3 , wherein R is a hydrocarbyl group having from 1 to 18 carbon atoms and X is a halogen atom.

Claim 26

The process of claim 22 wherein R is an alkyl or aryl group having from 1 to 6 carbon atoms and X is chlorine.

Claim 27

The process of claim 23 wherein R is ethyl.

Claim 28

The process of claim 20 wherein the titanium trihalide solids obtained in step (c) are directly contacted with the alpha-olefin under polymerization conditions.

Claim 29

A process for producing titanium trichloride solids product catalyst component having an average particle size diameter greater than 35μ and a narrow particle size distribution comprising: (a) adding R 2 AlX or mixtures thereof with RAlX 2 slowly and with stirring to a solution of titanium tetrachloride in a suitable diluent at a temperature from about -5° C. to about +10° C. and based on total moles of organoaluminum compound per mole of titanium tetrachloride in a mole ratio of between about 0.9:1.0 to about 1.2:1.0 and in the presence of about 0 to about 1.0 mole added RAlX 2 per mole of R 2 AlX, 0.0 mole to all of added RAlX 2 being in solution with titanium tetrachloride prior to the addition of R 2 AlX the remainder of added RAlX 2 being added with R 2 AlX to the titanium tetrahalide solution, wherein R is a hydrocarbyl group having from 1 to 18 carbon atoms and X is a halogen atom, the rate of addition of the R 2 AlX to the titanium tetrachloride solution being controlled to maintain the reduction of titanium tetrachloride to titanium trichloride at about 0.03 to about 0.2 m moles per liter per second whereby there is obtained titanium trichloride solids product in the diluent having a narrow particle size distribution and an average particle size greater than about 20μ; (b) slowly, simultaneously and continuously adding with stirring to the titanium trichloride solids product in the diluent R 2 AlX or mixtures thereof with RAlX 2 and titanium tetrachloride at a mole ratio based on total moles organoaluminum compound per mole titanium tetrachloride of about 0.9:1.0 to about 1.2:1.0; wherein R and X are as defined above, and wherein the simultaneous and continuous addition is at a rate such that the reduction of titanium tetrahalide to titanium trihalide is about 6×10 -4 to about 7×10 -3 m moles per liter per second per m 2 of available preformed titanium halide surface area until solids product of desired size are obtained; (c) slowly raising the temperature to about 60° C. to about 70° C. and recovering titanium trichloride solids product; (d) contacting the TiCl 3 solids product with a minor amount of an alpha-olefin having at least two carbon atoms under polymerization conditions to obtain a reduced TiCl 3 solids product containing about 1 to about 1,000 wt.% or prepolymerized alpha-olefin based on the weight of TiCl 3 ; and (e) treating said prepolymerized reduced solid with one of (a) a chlorinated hydrocarbon having at least 2 carbon atoms and a Lewis base complexing agent or (b) TiCl 4 and a Lewis base complexing agent to convert the prepolymerized TiCl 3 reduced solid to a substantially non-friable highly active, crystalline prepolymerized TiCl 3 composition.

Claim 30

A process for producing titanium trichloride solids product catalyst component having an average particle size diameter greater than 35μ and a narrow particle size distribution comprising: (a) adding R 2 AlX or mixtures thereof with RAlX 2 slowly and with stirring to a solution of titanium tetrachloride in a suitable diluent at a temperature from about -5° C. to about +10° C. and based on total moles of organoaluminum compound per mole of titanium tetrachloride in a mole ratio of between about 0.9:1.0 to about 1.2:1.0 and in the presence of about 0 to about 1.0 mole added RAlX 2 per mole of R 2 AlX, 0.0 mole to all of added RAlX 2 being in solution with titanium tetrachloride prior to the addition of R 2 AlX the remainder of added RAlX 2 being added with R 2 AlX to the titanium tetrahalide solution, wherein R is a hydrocarbyl group having from 1 to 18 carbon atoms and X is a halogen atom, the rate of addition of the R 2 AlX to the titanium tetrachloride solution being controlled to maintain the reduction of titanium tetrachloride to titanium trichloride at about 0.03 to about 0.2 m moles per liter per second whereby there is obtained titanium trichloride solids product in the diluent having a narrow particle size distribution and an average particle size greater than about 20μ; (b) slowly, simultaneously and continuously adding with stirring to the titanium trichloride solids product in the diluent R 2 AlX or mixtures thereof with RAlX 2 and titanium tetrachloride at a mole ratio based on total moles organoaluminum compound per mole titanium tetrachloride of about 0.9:1.0 to about 1.2:1.0; wherein R and X are as defined above, and wherein the simultaneous and continuous addition is at a rate such that the reduction of titanium tetrahalide to titanium trihalide is about 6×10 -4 to about 7×10 -3 m moles per liter per second per m 2 of available preformed titanium halide surface area until solids product of desired size are obtained; (c) slowly raising the temperature to about 60° C. to about 70° C. and recovering titanium trichloride solids product; (d) contacting the TiCl 3 solids product with a minor amount of an alpha-olefin having at least two carbon atoms under polymerization conditions to obtain a reduced TiCl 3 solids product containing about 1 to about 1,000 wt.% or prepolymerized alpha-olefin based on the weight of TiCl 3 ; and (e) treating said prepolymerized reduced solid with one of (a) a chlorinated hydrocarbon having at least 2 carbon atoms and a Lewis base complexing agent or (b) TiCl 4 and a Lewis base complexing agent to convert the prepolymerized TiCl 3 reduced solid to a substantially non-friable highly active, crystalline prepolymerized TiCl 3 composition.

Claim 31

The process of claim 26 wherein step (a) is followed by step (b) without interruption.

Claim 32

The process of claim 26 wherein X is chlorine and R can be an alkyl or aryl group having from 1 to 6 carbon atoms.

Claim 33

The process of claim 28 wherein R is ethyl.

Claim 34

The process of claim 29 wherein the mole ratio of organoaluminum compounds to titanium tetrachloride in step (a) is about 1.0:1.0 to about 1.2:1.0, in step (b) about 0.9:1.0 to about 1.1:1.0 and the mole ratio of ethylaluminum dichloride to diethylaluminum chloride is about 0.0:1.0 to about 1.0:1.0.

Claim 35

The process of claim 26 wherein said alpha-olefin contains from 2 to 22 carbon atoms said alpha-olefin containing no branching on the vinylic carbon atom and is present in amounts so as to provide a TiCl 3 solid product prepolymerized with about 3 wt.% to about 100 wt.% of said alpha-olefin based on the weight of TiCl 3 .

Claim 36

The process of claim 31 wherein said alpha-olefin has from 3 to 8 carbon atoms and is present in amounts so as to provide a reduced solid TiCl 3 product prepolymerized with about 6 wt.% to 30 wt.% of said alpha-olefin based on the weight of TiCl 3 .

Claim 37

The process of claim 26 wherein said prepolymerized TiCl 3 reduced solid is treated with the chlorinated hydrocarbon and Lewis base complexing agent.

Claim 38

The process of claim 33 wherein the treatment is at a temperature in the range of about 50° C. to about 100° C. for about 1 to about 10 hours, the chlorinated hydrocarbon being present in an amount at least about 0.2 mole per gram atom of titanium and the Lewis base being present in an amount of at least 0.1 mole per mole of titanium.

Claim 39

The process of claim 34 wherein the chlorinated hydrocarbon is present in an amount of about 0.5 mole to about 1.5 mole per gram atom of titanium in the prepolymerized reduced solid and the Lewis base is present in a range of about 0.1 mole to about 2.5 moles per mole titanium.

Claim 40

The process of claim 26 wherein said Lewis base complexing agent is dialkyl ether.

Claim 41

The process of claim 33 wherein said chlorinated hydrocarbon has from 2 to 8 carbon atoms and is selected from chlorinated saturated hydrocarbons, chlorinated unsaturated hydrocarbons or mixtures thereof.

Claim 42

The process of claim 37 wherein said chlorinated hydrocarbon is selected from chlorinated aliphatic hydrocarbons, chlorinated aromatic hydrocarbons or mixtures thereof.

Claim 43

The process of claim 38 wherein said chlorinated hydrocarbon is selected from hexachloroethane, pentachloroethane, trichloroethane, dichloroethane, tetrachloroethane, hexachloropropane, pentachloropropane, tetrachloropropane, dichlorobutane and mixtures thereof.

Claim 44

The process of claim 36 wherein said complexing agent is selected from the group consisting of di-n-butyl ether, di-n-amyl ether, diisoamyl ether, di-n-heptyl ether, di-2-ethylhexyl ether or mixtures thereof.

Claim 45

The process of claim 39 wherein the chlorinated hydrocarbon is hexachloroethane.

Claim 46

The process of claim 40 wherein said complexing agent is di-n-butyl ether.

Claim 47

The process of claim 29 wherein the titanium trihalide solids obtained in step (c) are directly contacted with the alpha-olefin under polymerization conditions.

Claim 48

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 19.

Claim 49

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 20.

Claim 50

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 21.

Claim 51

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 22.

Claim 52

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 23.

Claim 53

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 24.

Claim 54

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 25.

Claim 55

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 26.

Claim 56

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 27.

Claim 57

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 28.

Claim 58

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 29.

Claim 59

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 30.

Claim 60

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 31.

Claim 61

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 32.

Claim 62

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 33.

Claim 63

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 34.

Claim 64

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the tiCl 3 solids product obtained by the process of claim 35.

Claim 65

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 36.

Claim 66

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 37.

Claim 67

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 38.

Claim 68

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 39.

Claim 69

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 40.

Claim 70

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 41.

Claim 71

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 42.

Claim 72

A catalyst system for the polymerization of olefins comprising: (a) an organometal compound co-catalyst; and (b) the TiCl 3 solids product obtained by the process of claim 43.