Method of cleaning cathodes
Assignee: Montanwerke Brixlegg GmbH
•
Filing: 1980-10-02
•
Granted: 1982-05-18
•
Expires: 2000-10-02
Abstract
Abstract A method for the removal of impurities from copper cathodes withdrawn from a copper electrorefining bath in which the cathodes are subjected to ultrasonic vibrations in the KHz. range in heated water which is circulated or subjected to jets and under conditions in which cavitation bubbles can develop along the surfaces of the cathode.
Inventors
- 👤 Helmut Worz
- 👤 Hermann Leuprecht
- 👤 Jakob Biechl
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:52
CPC Classifications
B; B08; B08B; B08B3/00; B08B3/04; B08B3/10; B08B3/12
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
81 words
A method of cleaning the surfaces of a copper cathode removed from an electrorefining bath comprising the steps of: (a) supporting said cathode on an ultrasonic transducer immersed in a cleaning bath of heated degassed water with said surfaces of said cathode in contact therewith; (b) subjecting said cathode in contact with said transducer to direct ultrasonic vibrations therefrom; and (c) subjecting said surfaces of said cathode immersed in said cleaning bath to ultrasonic vibrations therefrom transmitted through said cleaning bath.
Claim 2
Independent Claim
81 words
A method of cleaning the surfaces of a copper cathode removed from an electrorefining bath comprising the steps of: (a) supporting said cathode on an ultrasonic transducer immersed in a cleaning bath of heated degassed water with said surfaces of said cathode in contact therewith; (b) subjecting said cathode in contact with said transducer to direct ultrasonic vibrations therefrom; and (c) subjecting said surfaces of said cathode immersed in said cleaning bath to ultrasonic vibrations therefrom transmitted through said cleaning bath.
Claim 3
Dependent Claim
57 words
The method definded in claim 1 wherein in steps b and c said cathode is subjected to ultrasonic vibrations at a frequency of about 20 to about 100 KHz for a period of up to two minutes to form cavitation bubbles along the surfaces thereof while directing jets of water upwardly along the surfaces of said cathode.
References Cited (Backward Citations)
US3701677A
Cited
US4103519A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-17 | 1985-11-16 | 1986-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-17 | 1989-11-16 | 1990-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-17 | 1993-11-16 | 1994-05-18 | $7700.00 | Window Closed / Lapsed |