Electric contact material and method of producing the same
Assignee: NTT Inc
•
Filing: 1981-04-10
•
Granted: 1982-05-18
•
Expires: 2001-04-10
Abstract
Abstract An electrical contact material and method of producing the same are provided. The material is an internally oxidized silver eutectic alloy system with a main component of silver to which at least one of silicon and germanium is added and, for characteristic improvement purpose, at least one selected from at least one of the groups consisting respectively of gold, platinum and the like, titanium, rhenium and the like, and iron, cobalt and the like is further added. In producing the material, an ingot of said alloy is hot-worked and then internally oxidized at a temperature in a range from 250 DEG C. to the eutectic temperature of the alloy.
Inventors
- 👤 Koichi Fujiwara
- 👤 Goro Yamauchi
- 👤 Kishio Arita
- 👤 Shigeyuki Tsurumi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 12:55
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/10; C22C1/1078; H; H01; H01H; H01H1/00; H01H1/02; H01H1/021; H01H1/023; H01H1/0237; H01H2001/0208
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
92 words
A method of producing an electrical contact material comprising a silver eutectic alloy comprising Ag as the main component in which fine oxide particles are uniformly dispersed, said method comprising the steps of: (a) admixing with Ag at least one element selected from the group consisting of Si and Ge; (b) melting said admixture of Ag and said at least one element to form an alloy; (c) quenching said alloy; (d) annealing said quenched alloy in a vacuum; (e) plastically working said annealed alloy; and (f) internally oxidizing said plastically worked alloy.
Claim 2
Independent Claim
92 words
A method of producing an electrical contact material comprising a silver eutectic alloy comprising Ag as the main component in which fine oxide particles are uniformly dispersed, said method comprising the steps of: (a) admixing with Ag at least one element selected from the group consisting of Si and Ge; (b) melting said admixture of Ag and said at least one element to form an alloy; (c) quenching said alloy; (d) annealing said quenched alloy in a vacuum; (e) plastically working said annealed alloy; and (f) internally oxidizing said plastically worked alloy.
Claim 3
Dependent Claim
30 words
The method according to claim 1 wherein said at least one element is present in a concentration of 1 to 17 at. % based on the weight of the material.
Claim 4
Dependent Claim
28 words
The method according to claim 1 wherein said at least one element comprises Si, and said alloy is internally oxidized at a temperature of 250° to 840° C.
Claim 5
Dependent Claim
28 words
The method according to claim 1 wherein said at least one element comprises Si, and said alloy is internally oxidized at a temperature of 250° to 651° C.
Claim 6
Dependent Claim
30 words
The method according to claim 1 wherein said at least one element comprises Si and Ge, and said alloy is internally oxidized at a temperature of 250° to 840° C.
Claim 7
Independent Claim
144 words
A method of producing an electrical contact material comprising a silver eutectic alloy comprising Ag as the main component in which fine oxide particles are uniformly dispersed, said method comprising the steps of: (a) admixing with Ag at least one element selected from the group consisting of Si and Ge and at least one additional element selected from at least one of the following groups wherein: the first group consists of Au, Pt, Pd, Rh, Ru, Os and Ir, and the second group consists of Ti, V, Zr, Nb, Mo, Ta, W and Re, and the third group consists of Fe, Co, Ni and Cu; (b) melting said admixture of Ag and said elements to form an alloy; (c) quenching said alloy; (d) annealing said quenched alloy in a vacuum; (e) plastically working said annealed alloy; and (f) internally oxidizing said plastically worked alloy.
Claim 8
Independent Claim
144 words
A method of producing an electrical contact material comprising a silver eutectic alloy comprising Ag as the main component in which fine oxide particles are uniformly dispersed, said method comprising the steps of: (a) admixing with Ag at least one element selected from the group consisting of Si and Ge and at least one additional element selected from at least one of the following groups wherein: the first group consists of Au, Pt, Pd, Rh, Ru, Os and Ir, and the second group consists of Ti, V, Zr, Nb, Mo, Ta, W and Re, and the third group consists of Fe, Co, Ni and Cu; (b) melting said admixture of Ag and said elements to form an alloy; (c) quenching said alloy; (d) annealing said quenched alloy in a vacuum; (e) plastically working said annealed alloy; and (f) internally oxidizing said plastically worked alloy.
Claim 9
Dependent Claim
30 words
The method according to claim 6 wherein said at least one element is present in a concentration of 1 to 17 at. % based on the weight of the material.
Claim 10
Dependent Claim
53 words
The method according to claim 6 wherein said at least one element is present in a concentration of 1 to 17 at. % and said at least one additional element selected from said first group is present in a concentration of 1 to 10 at. % based on the weight of the material.
Claim 11
Dependent Claim
53 words
The method according to claim 6 wherein said at least one element is present in a concentration of 1 to 17 at. % and said at least one additional element selected from said second group is present in a concentration of 1 to 5 at. % based on the weight of the material.
Claim 12
Dependent Claim
53 words
The method according to claim 6 wherein said at least one element is present in a concentration of 1 to 17 at. % and said at least one additional element selected from said third group is present in a concentration of 1 to 5 at. % based on the weight of the material.
Claim 13
Dependent Claim
76 words
The method according to claim 6 wherein said at least one element is present in a concentration of 1 to 17 at. % and said at least one additional element selected from said first group is present in a concentration of 1 to 10 at. % and said at least one additional element selected from said second group is present in a concentration of 1 to 5 at. % based on the weight of the material.
Claim 14
Dependent Claim
76 words
The method according to claim 6 wherein said at least one element is present in a concentration of 1 to 17 at. % and said at least one additional element selected from said first group is present in a concentration of 1 to 10 at. % and said at least one additional element selected from said third group is present in a concentration of 1 to 5 at. % based on the weight of the material.
Claim 15
Dependent Claim
28 words
The method according to claim 6 wherein said at least one element comprises Si, and said alloy is internally oxidized at a temperature of 250° to 840° C.
Claim 16
Dependent Claim
28 words
The method according to claim 6 wherein said at least one element comprises Ge, and said alloy is internally oxidized at a temperature of 250° to 651° C.
Claim 17
Dependent Claim
30 words
The method according to claim 6 wherein said at least one element comprises Si and Ge, and said alloy is internally oxidized at a temperature of 250° to 840° C.
Claim 18
Dependent Claim
20 words
The method according to claim 1 wherein said melting step is performed at a temperature of 1,100° to 1,200° C.
Claim 19
Dependent Claim
20 words
The method according to claim 6 wherein said melting step is performed at a temperature of 1,100° to 2,000° C.
Claim 20
Dependent Claim
46 words
The method according to claim 1 wherein said annealing step is performed at a temperature of 300° to 800° C. for a period of time ranging from 20 to 60 minutes, and said plastically working step is performed at a temperature of 300° to 600° C.
Claim 21
Dependent Claim
46 words
The method according to claim 6 wherein said annealing step is performed at a temperature of 300° to 800° C. for a period of time ranging from 20 to 60 minutes, and said plastically working step is performed at a temperature of 300° to 600° C.
References Cited (Backward Citations)
US2861155A
Cited
GB909349A
Cited
US3258829A
Cited
US3515542A
Cited
US3811876A
Cited
DE2639107A1
Cited
US4131458A
Cited
US4124380A
Cited
US4150982A
Cited
US4279649A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-17 | 1985-11-16 | 1986-05-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-17 | 1989-11-16 | 1990-05-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-17 | 1993-11-16 | 1994-05-18 | $7700.00 | Window Closed / Lapsed |