Method for producing cobalt metal powder
Assignee: Osram Sylvania Inc
•
Filing: 1980-08-18
•
Granted: 1982-05-11
•
Expires: 2000-08-18
Abstract
Abstract Fine particle size cobalt metal powder is prepared absent tailings by heating an aqueous solution of soluble cobaltic ammine halide to a temperature of at least about 120 degrees centigrade for a sufficient period of time to decompose said cobaltic ammine halide and form a cobalt containing precipitate. The precipitate is separated from the solution and reduced in a reducing atmosphere to produce fine metal cobalt powder.
Inventors
- 👤 Richard G. W. Gingerich
- 👤 Richard A. Scheithauer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 05:18
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/16; B22F9/18; B22F9/20; B22F9/22
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
144 words
A method for producing a fine metal powder comprising heating an aqueous solution of soluble cobaltic ammine halide to a temperature of at least 120 degrees centigrade for a sufficient period of time to decompose substantially all of said cobaltic ammine halide to form an amorphous hydrated cobalt oxide containing precipitate, said heating being carried out at a suitable pressure in a sufficiently closed vessel to permit said temperature being attained in said solution, said aqueous solution of soluble cobaltic ammine halide consist essentially from about 5 grams per liter cobaltic ammine chloride based on cobalt present in solution up to the limits of solubility of cobaltic ammine chloride, water, and less than 2 percent by weight impurities based on cobalt present in solution, separating the cobalt containing precipitate from the resulting solution, reducing said cobalt containing precipitate to form fine particles of cobalt.
Claim 2
Independent Claim
144 words
A method for producing a fine metal powder comprising heating an aqueous solution of soluble cobaltic ammine halide to a temperature of at least 120 degrees centigrade for a sufficient period of time to decompose substantially all of said cobaltic ammine halide to form an amorphous hydrated cobalt oxide containing precipitate, said heating being carried out at a suitable pressure in a sufficiently closed vessel to permit said temperature being attained in said solution, said aqueous solution of soluble cobaltic ammine halide consist essentially from about 5 grams per liter cobaltic ammine chloride based on cobalt present in solution up to the limits of solubility of cobaltic ammine chloride, water, and less than 2 percent by weight impurities based on cobalt present in solution, separating the cobalt containing precipitate from the resulting solution, reducing said cobalt containing precipitate to form fine particles of cobalt.
Claim 3
Dependent Claim
29 words
A method according to claim 1 wherein said soluble cobaltic ammine halide is selected from the group consisting of cobaltic hexammine halide and cobaltic pentammine halide and mixtures thereof.
Claim 4
Dependent Claim
19 words
A method according to claim 2 wherein said cobaltic ammine halide comprises a major portion of cobaltic hexammine halide.
Claim 5
Dependent Claim
18 words
A method according to claim 2 wherein said cobaltic ammine halide comprises a substantially all cobaltic hexammine halide.
Claim 6
Dependent Claim
26 words
A method according to claim 4 wherein said aqueous solution consist essentially of less than about 0.2 percent by weight based on cobalt present in solution.
Claim 7
Dependent Claim
17 words
A method according to claim 5 wherein said cobalt containing precipitate comprises a black wet cobalt hydrate.
Claim 8
Dependent Claim
28 words
A method according to claim 6 wherein substantially all of said cobalt containing precipitate is reducible to cobalt particles having a particle size less than about 2 microns.
References Cited (Backward Citations)
US2734821A
Cited
US2728636A
Cited
US3967958A
Cited
US4002719A
Cited
US4214895A
Cited
US4233063A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-10 | 1985-11-09 | 1986-05-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-10 | 1989-11-09 | 1990-05-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-10 | 1993-11-09 | 1994-05-11 | $7700.00 | Window Closed / Lapsed |