Continuous bulk polymerization process for preparing copolymer of aromatic vinyl monomer and maleic anhydride
Assignee: Daicel Corp
•
Filing: 1980-10-14
•
Granted: 1982-05-04
•
Expires: 2000-10-14
Abstract
Abstract In a continuous bulk polymerization process of a styrene type copolymer which is a copolymer consisting of 60 to 95% by weight of an aromatic vinyl monomer and 40 to 5% by weight of maleic anhydride, a continuous bulk polymerization process of a styrene type copolymer characterized in that at the first stage, continuous bulk polymerization is carried out using a vertical agitation system polymerization apparatus to a conversion of 30 to 60% by continuously feeding a mixed monomer of the aromatic vinyl monomer and maleic anhydride having a feed composition ratio corresponding to the copolymer, and at the second stage, and at the third stage, if necessary, continuous bulk polymerization is carried out to a conversion of 60 to 95% using a horizontal apparatus for processing highly viscous substances, equipped with one or two rotary shafts having agitation blade frames or agitation blades impaled thereon, by continuously and dividedly feeding maleic anhydride from plural feed ports disposed on said apparatus for processing highly viscous substances.
Inventors
- 👤 Atsushi Tanaka
- 👤 Toshiyuki Chiba
- 👤 Hirotaka Miyata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 02:36
CPC Classifications
C; C08; C08F; C08F212/00; B; B01; B01J; B01J19/00; B01J19/18; B01J19/20; B01J2219/00; B01J2219/00049; B01J2219/00051; B01J2219/00074; B01J2219/00186; B01J2219/18; B01J2219/182; B01J2219/185
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
377 words
A continuous bulk polymerization process for preparing a substantially uniform copolymer consisting essentially of from 60 to 95% by weight of units of aromatic vinyl monomer, from 40 to 5% by weight of units of maleic anhydride monomer and from 0 to 30 wt. % of units of third copolymerization monomer which is different from said aromatic vinyl monomer and said maleic anhydride monomer, which comprises the steps of continuously feeding a mixture of said monomers having a composition effective to form said copolymer into a vertical, first-stage, polymerization tank means equipped with agitating means, continuously agitating said mixture in said first-stage polymerization tank means and maintaining bulk polymerization reaction conditions in said first-stage polymerization tank means effective to obtain a partial conversion of said monomers to said copolymer and to obtain a polymerization liquid containing from 30 to 60 wt. % of solids of said copolymer; continuously withdrawing said polymerization liquid from said first-stage polymerization tank means and feeding it into one horizontal end of an elongated, horizontal, second-stage apparatus effective for processing highly viscous materials, said second-stage apparatus being equipped with horizontal rotary shaft means having a series of blade members mounted thereon at horizontally spaced-apart locations and extending outwardly therefrom so as to divide said second-stage apparatus into a series of horizontally displaced mixing zones, continuously rotating said shaft means and thereby continuously mixing said polymerization liquid in said mixing zones while moving said polymerization liquid from one mixing zone to the next so that said polymerization liquid moves to the opposite horizontal end of said second-stage apparatus, maintaining bulk polymerization reaction conditions in said second-stage apparatus effective to obtain a further conversion of said monomers to said copolymer as said polymerization liquid moves toward said opposite horizontal end of said second-stage apparatus to obtain a polymerization reaction product containing from 60 to 95 wt. % of solids of said copolymer, and continuously, separately adding divided quantities of maleic anhydride monomer to said polymerization liquid at a plurality of horizontally spaced-apart locations in said second-stage apparatus wherein the amount of maleic anhydride monomer added at said locations progressively diminishes toward said opposite horizontal end of said second-stage apparatus so as to continuously obtain a uniform copolymer containing a substantially constant amount of maleic anhydride.
Claim 2
Dependent Claim
377 words
A continuous bulk polymerization process for preparing a substantially uniform copolymer consisting essentially of from 60 to 95% by weight of units of aromatic vinyl monomer, from 40 to 5% by weight of units of maleic anhydride monomer and from 0 to 30 wt. % of units of third copolymerization monomer which is different from said aromatic vinyl monomer and said maleic anhydride monomer, which comprises the steps of continuously feeding a mixture of said monomers having a composition effective to form said copolymer into a vertical, first-stage, polymerization tank means equipped with agitating means, continuously agitating said mixture in said first-stage polymerization tank means and maintaining bulk polymerization reaction conditions in said first-stage polymerization tank means effective to obtain a partial conversion of said monomers to said copolymer and to obtain a polymerization liquid containing from 30 to 60 wt. % of solids of said copolymer; continuously withdrawing said polymerization liquid from said first-stage polymerization tank means and feeding it into one horizontal end of an elongated, horizontal, second-stage apparatus effective for processing highly viscous materials, said second-stage apparatus being equipped with horizontal rotary shaft means having a series of blade members mounted thereon at horizontally spaced-apart locations and extending outwardly therefrom so as to divide said second-stage apparatus into a series of horizontally displaced mixing zones, continuously rotating said shaft means and thereby continuously mixing said polymerization liquid in said mixing zones while moving said polymerization liquid from one mixing zone to the next so that said polymerization liquid moves to the opposite horizontal end of said second-stage apparatus, maintaining bulk polymerization reaction conditions in said second-stage apparatus effective to obtain a further conversion of said monomers to said copolymer as said polymerization liquid moves toward said opposite horizontal end of said second-stage apparatus to obtain a polymerization reaction product containing from 60 to 95 wt. % of solids of said copolymer, and continuously, separately adding divided quantities of maleic anhydride monomer to said polymerization liquid at a plurality of horizontally spaced-apart locations in said second-stage apparatus wherein the amount of maleic anhydride monomer added at said locations progressively diminishes toward said opposite horizontal end of said second-stage apparatus so as to continuously obtain a uniform copolymer containing a substantially constant amount of maleic anhydride.
Claim 3
Dependent Claim
237 words
A process as claimed in claim 1 in which the polymerization reaction product continuously discharged from said second-stage apparatus is continuously fed into one end of an elongated, horizontal, third-stage apparatus effective for processing highly viscous materials, said third-stage apparatus being equipped with horizontal rotary shaft means having a series of blade members mounted thereon at horizontally spaced-apart locations and extending outwardly therefrom so as to divide said third-stage apparatus into a series of horizontally displaced mixing zones, continuously rotating said shaft means and thereby continuously mixing said polymerization liquid in said mixing zones while moving said polymerization liquid from one mixing zone to the next so that said polymerization liquid moves to the opposite horizontal end of said third-stage apparatus, maintaining bulk polymerization reaction conditions in said third-stage apparatus effective to obtain a further conversion of said monomers to said copolymer as said polymerization liquid moves toward said opposite horizontal end of said third-stage apparatus to obtain a polymerization reaction product containing from 60 to 95 wt. % of solids of said copolymer, and continuously, separately adding divided quantities of maleic anhydride monomer to said polymerization liquid at a plurality of horizontally spaced-apart locations in said third-stage apparatus wherein the amount of maleic anhydride monomer added at said locations progressively diminishes toward said opposite horizontal end of said third-stage apparatus so as to continuously obtain a uniform copolymer containing a substantially constant amount of maleic anhydride.
Claim 4
Dependent Claim
44 words
A process as claimed in claim 1, in which the reaction temperature in the first stage is in the range between 80° C. and 160° C. and the reaction temperature in the second stage is in the range between 80° C. and 180° C.
Claim 5
Dependent Claim
46 words
A process as claimed in claim 2, in which the reaction temperature in the first stage is in the range between 80° C. and 160° C. and the reaction temperatures in the second and third stages are in the range between 80° C. and 180° C.
Claim 6
Dependent Claim
233 words
A process as claimed in claim 1, in which the aromatic vinyl monomer and the maleic anhydride monomer are fed into the first stage in the composition ratio and amount calculated according to formulas IIa and IIb and maleic anhydride is fed into the second stage in the amounts calculated according to formula III, provided that each calculated value can vary with an allowance of 20%: ##EQU6## Amount of introduction: W·r·(1/P-1)/t (II-b) wherein, Sa/Ma=aromatic vinyl monomer-maleic anhydride monomer composition ratio to be continuously introduced P=steady state conversion during continuous polymerization (solid content) W=total feed quantity of monomers r=rate of polymerization (Kg/Kg/unit time) t=the same time as that used as the unit of the rate of polymerization r P 1 =weight percentage of aromatic vinyl monomer units in the copolymer K 1 =weight percentage of aromatic vinyl monomer initially fed Amounts of maleic anhydride to be added = ##EQU7## where: Z o =amount of solution fed to second stage apparatus C o =percentage of polymer content in the solution fed to second stage apparatus n=the number of tanks (n=1, 2 . . . n, the maximum of n corresponds to equivalent number of perfectly mixed tanks in the second stage) P 1 '=weight percentage of aromatic vinyl monomer in copolymer inside second stage apparatus X=average weight percentage of aromatic vinyl monomer in monomers inside second stage apparatus τ=residence time (hr) r'=rate of polymerization (Kg/Kg/hr)
Claim 7
Dependent Claim
246 words
A process as claimed in claim 2, in which the aromatic vinyl monomer and the maleic anhydride monomer are fed into the first stage in the composition ratio and amount calculated according to formulas IIa and IIb and maleic anhydride is fed into the second and third stages in the amounts calculated according to formula III, provided that each calculated value can vary with an allowance of 20%: ##EQU8## Amount of introduction: W·r·(1/P-1)/t (II-b) wherein, Sa/Ma=aromatic vinyl monomer-maleic anhydride monomer composition ratio to be continuously introduced P=steady state conversion during continuous polymerization (solid content) W=total feed quantity of monomers r=rate of polymerization (Kg/Kg/unit time) t=the same time as that used as the unit of the rate of polymerization r P 1 =weight percentage of aromatic vinyl monomer units in the copolymer K 1 =weight percentage of aromatic vinyl monomer initially fed Amounts of maleic anhydride to be added = ##EQU9## where: Z o =amount of solution fed to second or third stage apparatus C o =percentage of polymer content in the solution fed to second or third stage apparatus n=the number of tanks (n=1, 2 . . . n, the maximum of n corresponds to equivalent number of perfectly mixed tanks in the second or third stage apparatus P 1 '=weight percentage of aromatic vinyl monomer in copolymer inside second or third stage apparatus X=average weight percentage of aromatic vinyl monomer in monomers inside second or third stage apparatus τ=residence time (hr) r'=rate of polymerization (Kg/Kg/hr)
Claim 8
Dependent Claim
107 words
A process as claimed in claim 1, in which, during start-up of the process, maleic anhydride monomer is fed into the first stage according to formula I until steady-state operation has been attained, provided that the amount can vary with an allowance of 20% above or below from the calculated value Amount of maleic anhydride to be added = ##EQU10## where: W o =total monomer amount initially fed (Kg) r=rate of polymerization (Kg/Kg/unit time) K 1 =percentage of aromatic vinyl monomer in the monomer initially fed (weight ratio) P 1 =percentage of aromatic vinyl component in the formed copolymer (weight ratio) m=frequency of addition of maleic anhydride
Claim 9
Dependent Claim
21 words
A process as claimed in claim 1, in which two or more vertical polymerization tanks are used in the first stage.
Claim 10
Dependent Claim
37 words
A process as claimed in claim 2 in which the conversion in the second stage is in the range between 40 and 80% and that of the third stage is in the range between 60 and 90%.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-03 | 1985-11-02 | 1986-05-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-03 | 1989-11-02 | 1990-05-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-03 | 1993-11-02 | 1994-05-04 | $7700.00 | Window Closed / Lapsed |