Process for rapidly bodying organopolysiloxane resins
Assignee: General Electric Co
•
Filing: 1980-06-16
•
Granted: 1982-05-04
•
Expires: 2000-06-16
Abstract
Abstract There is disclosed a method for effecting the controlled rapid condensation of silanol radicals in silanol-containing organopolysiloxanes such as silicone resins. The process is effected by catalyzing such resin with 5 to 350 ppm stannous salt or soap; heating the catalyzed resin until a preselected viscosity is obtained; generating the first catalyst with a relatively moderate second metal soap catalyst, whereupon a condensed or bodied resin can be diluted to a preselected weight percent solids.
Inventors
- 👤 George F. Medford
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:00
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/16; C08K5/00; C08K5/04; C08K5/09; C08K5/098
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
134 words
A process for effecting the controlled rapid condensation of silanol radicals in a silanol-containing organopolysiloxane comprising the steps of: adding to silanol-containing organopolysiloxane resin solids, 5 to 350 parts calculated as metal by weight of a silanol condensation catalyst per million parts resin solids wherein said silanol condensation catalyst is a stannous salt effective for rapidly bodying said organopolysiloxane resin; heating said catalyzed silanol-containing organopolysiloxane resin to a temperature between 50° C. and 200° C. for an amount of time effective for increasing the molecular weight of said organopolysiloxane resin; quenching said stannous metal catalyzed resin by reacting said silanol condensation catalyst with a metal soap catalyst wherein said metal soap catalyst is effective for quenching said stannous salt catalyst and is a relatively less effective silanol condensation catalyst than said stannous salt catalyst.
Claim 2
Dependent Claim
134 words
A process for effecting the controlled rapid condensation of silanol radicals in a silanol-containing organopolysiloxane comprising the steps of: adding to silanol-containing organopolysiloxane resin solids, 5 to 350 parts calculated as metal by weight of a silanol condensation catalyst per million parts resin solids wherein said silanol condensation catalyst is a stannous salt effective for rapidly bodying said organopolysiloxane resin; heating said catalyzed silanol-containing organopolysiloxane resin to a temperature between 50° C. and 200° C. for an amount of time effective for increasing the molecular weight of said organopolysiloxane resin; quenching said stannous metal catalyzed resin by reacting said silanol condensation catalyst with a metal soap catalyst wherein said metal soap catalyst is effective for quenching said stannous salt catalyst and is a relatively less effective silanol condensation catalyst than said stannous salt catalyst.
Claim 3
Dependent Claim
45 words
A process as in claim 1 wherein said stannous salt condensation catalyst has the general formula: SnX.sub.2 ·yH.sub.2 O wherein X represents a halide, or carboxylate, R represents a monovalent hydrocarbon radical having from one to twenty carbon atoms, an y is a non-negative number.
Claim 4
Dependent Claim
29 words
A process as in claim 2 wherein said stannous salt catalyst is selected from the group consisting of stannous acetate, stannous stearate, stannous 2-ethyl hexoate and stannous chloride dihydrate.
Claim 5
Dependent Claim
92 words
A process as in claim 1 wherein said silicone hydrolyzate resin is composed of chemically combined siloxy units derived from the hydrolysis of halosilanes or alkoxysilanes or a mixture thereof wherein the individual silanes have the formula R' a SiX.sub.(4-a) wherein R' is a substituted or unsubstituted monovalent hydrocarbon radical and a averages approximately 1.2 to 1.8 but on any individual silicon atom a is 1 or 2, and wherein X is a halogen selected from C1 or Br, or an alkoxyradical selected from --OCH 3 or --OC 2 H 5 .
Claim 6
Dependent Claim
22 words
A process as in claim 1 wherein said heating step is effective for decreasing some or all of said water of condensation.
Claim 7
Dependent Claim
24 words
A process as in claim 1 wherein there is utilized at least 1.0 moles metal in said metal soap catalyst per mole tin metal.
Claim 8
Dependent Claim
21 words
A process as in claim 1 wherein said bodied resin is diluted with a hydrocarbon solvent compatible with said bodied resin.
Claim 9
Dependent Claim
22 words
A process as in claim 1 wherein said steps are carried out continuously thereby rapidly bodying a silicone hydrolyzate resin process stream.
Claim 10
Dependent Claim
26 words
A process as in claim 1 wherein said metal soap catalyst is effective for continuing said bodying reaction after quenching said stannous salt catalyzed bodying reaction.
Claim 11
Dependent Claim
24 words
A process as in claim 1 further comprising the step of cooling said bodied resin to a temperature of between 20° to 30° C.
Claim 12
Dependent Claim
42 words
A process as in claim 1 wherein the metal of said metal soap catalyst is selected from the group consisting of calcium, zinc, manganese, cerium, zirconium, and cobalt and said soap is selected from the group consisting of octoates, stearates, and neodecanoates.
Claim 13
Dependent Claim
33 words
A process as in claim 1, further comprising the steps of diluting said bodied resin; halting the catalytic activity of said metal soap catalyst; and obtaining a bodied resin of desired molecular weight.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-05-03 | 1985-11-02 | 1986-05-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-05-03 | 1989-11-02 | 1990-05-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-05-03 | 1993-11-02 | 1994-05-04 | $7700.00 | Window Closed / Lapsed |