Method of producing optical waveguide
Assignee: Sumitomo Electric Industries Ltd
•
Filing: 1979-09-28
•
Granted: 1982-04-27
•
Expires: 1999-09-28
Abstract
Abstract A method for producing an optical waveguide by melt-drawing a transparent glass rod which has been produced by collapsing a porous glass rod after being doped with a dopant material by depositing said material on the surface of the micro pores in order to enhance the refractive index of the collapsed glass rod, wherein a waveguide having higher mechanical strength and lower transmission is attained by drawing said glass rod at a temperature very close to the melting point of the outermost portion of the fiber without causing any overmelting or bubbling in the core portion, said drawing being facilitates by matching the viscosity and characteristics of the outermost lower-refractive-index portion to those of the central higher-refractive-index portion.
Inventors
- 👤 Shiro Kurosaki
- 👤 Minoru Watanabe
- 👤 Yuichi Usui
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 13:35
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/02; C03B37/025; C03B37/027; C03B37/012; C03B37/01205; C03B37/01211; C03B37/014; C03B37/018; C03B2205/00; C03B2205/08
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
226 words
A method of producing an optical waveguide by melt-drawing a glass preform composite comprising a transparent glass rod having a core portion and a cladding portion and a high refractive index glass jacket for said transparent rod, which comprises the steps of (a) depositing a dopant material for raising the refractive index of glass on the internal surfaces of the pores of a porous glass rod; (b) forming a radial dopant concentration gradient decreasing from the central to the peripheral portions of said porous glass; (c) collapsing the doped rod by the application of heat to form said transparent glass rod having a core portion exhibiting a high index of refraction and an outer cladding exhibiting a low index of refraction; (d) providing said high index of refraction, circumferential jacket layer for said transparent rod of a glass matched to have a viscosity and coefficient of expansion at melt-drawing temperatures substantially similar to the viscosity of said core portion of said transparent rod and the index of refraction being higher than the cladding portion by inserting said rod into a pipe of said matched glass; (e) collapsing said pipe around said transparent rod by the application of heat to form said preform composite; and (f) melt-drawing and heat-treating said composite to form said optical waveguide having a smooth outer surface, moisture resistance and improved mechanical strength.
Claim 2
Independent Claim
226 words
A method of producing an optical waveguide by melt-drawing a glass preform composite comprising a transparent glass rod having a core portion and a cladding portion and a high refractive index glass jacket for said transparent rod, which comprises the steps of (a) depositing a dopant material for raising the refractive index of glass on the internal surfaces of the pores of a porous glass rod; (b) forming a radial dopant concentration gradient decreasing from the central to the peripheral portions of said porous glass; (c) collapsing the doped rod by the application of heat to form said transparent glass rod having a core portion exhibiting a high index of refraction and an outer cladding exhibiting a low index of refraction; (d) providing said high index of refraction, circumferential jacket layer for said transparent rod of a glass matched to have a viscosity and coefficient of expansion at melt-drawing temperatures substantially similar to the viscosity of said core portion of said transparent rod and the index of refraction being higher than the cladding portion by inserting said rod into a pipe of said matched glass; (e) collapsing said pipe around said transparent rod by the application of heat to form said preform composite; and (f) melt-drawing and heat-treating said composite to form said optical waveguide having a smooth outer surface, moisture resistance and improved mechanical strength.
Claim 3
Dependent Claim
25 words
The method of claim 1, wherein said transparent glass rod is covered, on the periphery, by a jacket layer of borosilicate glass or alumina-silicate glass.
Claim 4
Dependent Claim
142 words
The method of producing optical waveguide in accordance with claim 1, wherein the rod is provided with a core portion and a cladding portion having high and low index of refraction respectively by means of stuffing and unstuffing processes in which a dopant is, respectively, deposited on or removed from the surface of the micro pores of porous glass, said rod being inserted into a borosilicate or alumina-silicate glass pipe which has higher index of refraction than the cladding and similar viscosity to the core portion, whereby the viscosity of the jacket portion made of said borosilicate or alumina-silicate glass is lower than the cladding portion, and finally, the melt-drawing process of the combination of said rod and pipe is carried out at a temperature at which the jacket glass is so soft as to make the surface of the fiber smooth.
Claim 5
Dependent Claim
41 words
The method of claim 2, wherein said transparent glass rod doped with dopant material is inserted in said pipe and the combination of the rod and pipe is simultaneously melt-drawn while the gap between said rod and pipe is being collapsed.
Claim 6
Dependent Claim
44 words
The method of claim 2, wherein said melt-drawing process is carried out after said transparent glass rod doped with a dopant material is inserted in said pipe and subsequently assembled into a single perform by collapsing the gap between said rod and said pipe.
References Cited (Backward Citations)
US3938974A
Cited
US4110093A
Cited
US4110096A
Cited
JPS5156642A
Cited
US4078910A
Cited
US4165222A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-04-26 | 1985-10-26 | 1986-04-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-04-26 | 1989-10-26 | 1990-04-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-04-26 | 1993-10-26 | 1994-04-27 | $7700.00 | Window Closed / Lapsed |