US4324829A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Laminate film structures from chlorinated polyethylenes
Assignee: Dow Chemical Co
•
Filing: 1980-04-09
•
Granted: 1982-04-13
•
Expires: 2000-04-09
Abstract
Abstract An easily processable, dimensionally stable laminate film structures which are particularly adopted for use in lining ponds, pits, dams and canals and other systems employed for water handling. More particularly, it is directed to laminate film structures comprising, in generally planar coextensive relationship, (A) a first outer layer of substantially linear chlorinated polyethylene containing from about 25 to about 50 weight percent of chemically combined chlorine, (B) an internal layer of substantially linear chlorinated polyethylene containing from about 5 to about 15 percent by weight of chemically combined chlorine, and (C) a second outer layer of the nature of the first outer layer which second outer layer is disposed adjacent the internal layer and remote from the first outer layer, the first and second outer layers being substantially amorphous and the internal layer being substantially crystalline.
Inventors
- 👤 Ronald J. Hayes
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 18:44
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/14; B32B27/06; B32B27/08; B32B27/32; B32B5/00; B32B5/16; B32B2270/00; B32B2307/00; B32B2307/70; B32B2307/702; B32B2307/704; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/31504; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/31928
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
265 words
A laminate film structure comprising, in a planar coextensive relationship, (A) an amorphous first outer layer of linear chlorinated olefin polymer containing from about 25 to about 50 weight percent of chemically combined chlorine and having a thickness of from about 0.005 to about 0.05 of an inch; (B) a crystalline internal layer of linear chlorinated olefin polymer containing from about 5 to about 15 percent by weight of chemically combined chlorine and having a thickness of from about 0.005 to about 0.03 of an inch, said internal layer being a film formed from a linear chlorinated high density olefin polymer, said polymer, in particulate form, having a flowability, measured as angle of repose of from about 24° to about 28°, a bulk density in the range of from about 25 to about 35 pounds/cubic foot, a surface area in the range of from about 2 to about 4 square meters/gram, particles sizes predominantly in the range of from about 300 to about 600 microns and a porosity sufficient to provide an average free volume within individual particles in the range of from about 20 to about 40 volume percent based on total particle volume, said polymer being chlorinated while in particulate form in a heterogeneous system at a temperature of less than about 90° C., said internal layer having a heat of fusion of from about 20 to about 40 calories/gram; and (C) an amorphous second outer layer of the nature of said first outer layer, said second outer layer being disposed ajacent to said internal layer and remote from said first outer layer.
Claim 2
Dependent Claim
265 words
A laminate film structure comprising, in a planar coextensive relationship, (A) an amorphous first outer layer of linear chlorinated olefin polymer containing from about 25 to about 50 weight percent of chemically combined chlorine and having a thickness of from about 0.005 to about 0.05 of an inch; (B) a crystalline internal layer of linear chlorinated olefin polymer containing from about 5 to about 15 percent by weight of chemically combined chlorine and having a thickness of from about 0.005 to about 0.03 of an inch, said internal layer being a film formed from a linear chlorinated high density olefin polymer, said polymer, in particulate form, having a flowability, measured as angle of repose of from about 24° to about 28°, a bulk density in the range of from about 25 to about 35 pounds/cubic foot, a surface area in the range of from about 2 to about 4 square meters/gram, particles sizes predominantly in the range of from about 300 to about 600 microns and a porosity sufficient to provide an average free volume within individual particles in the range of from about 20 to about 40 volume percent based on total particle volume, said polymer being chlorinated while in particulate form in a heterogeneous system at a temperature of less than about 90° C., said internal layer having a heat of fusion of from about 20 to about 40 calories/gram; and (C) an amorphous second outer layer of the nature of said first outer layer, said second outer layer being disposed ajacent to said internal layer and remote from said first outer layer.
Claim 3
Dependent Claim
121 words
The laminate film structure of claim 1 wherein said first and second outer layers are formed from a linear chlorinated olefin polymer having a relative crystallinity of between about 15 and 28 weight percent and a heat of fusion of less than about 8 calorie/gram when containing about 25 weight percent chlorine and a relative crystallinity of less than about 10 weight percent and a heat of fusion of less than about 3 calorie/gram when containing about 34 or more weight percent chlorine, said layers having a tensile strength of at least about 1100 pounds per square inch, an elongation of between about 350 to 900 weight percent and a 100 weight percent modulus of between about 150 and 1500 psi.
Claim 4
Dependent Claim
29 words
The laminate film structure of claim 1 wherein said first and second outer layers are formed from a linear chlorinated polyethylene containing about 42 percent of chemically combined chlorine.
Claim 5
Dependent Claim
27 words
The laminate structure of claim 3 wherein said internal layer is formed from a linear chlorinated polyethylene containing about 8 percent by weight of chemically combined chlorine.
Claim 6
Dependent Claim
48 words
The laminate film structure of claim 4 wherein said internal layer has a thickness of about 0.005 of an inch and said laminate film structure has a total thickness of from about 0.020 to about 0.045 of an inch and a width of up to about 60 inches.
Claim 7
Dependent Claim
128 words
A laminate film structure comprising in planar coextensive relationship (A) an amorphous first outer layer of linear olefin polymer containing from about 25 to about 50 weight percent of chemically combined chlorine and having a thickness of from about 0.005 to about 0.05 of an inch, (B) a crystalline internal layer comprising a blend of a high density polyethylene in admixture with a chlorinated polyethylene, said blend containing from about 5 to about 15 percent by weight of chemically combined chlorine, and having a thickness of from about 0.005 to about 0.03 of an inch, and (C) an amorphous second outer layer of the nature of said first outer layer, said second outer layer being disposed adjacent to said internal layer and remote from said first outer layer.
Claim 8
Dependent Claim
128 words
A laminate film structure comprising in planar coextensive relationship (A) an amorphous first outer layer of linear olefin polymer containing from about 25 to about 50 weight percent of chemically combined chlorine and having a thickness of from about 0.005 to about 0.05 of an inch, (B) a crystalline internal layer comprising a blend of a high density polyethylene in admixture with a chlorinated polyethylene, said blend containing from about 5 to about 15 percent by weight of chemically combined chlorine, and having a thickness of from about 0.005 to about 0.03 of an inch, and (C) an amorphous second outer layer of the nature of said first outer layer, said second outer layer being disposed adjacent to said internal layer and remote from said first outer layer.
Claim 9
Dependent Claim
28 words
The laminate film structure of claim 6 wherein said first and second outer layers are formed from a linear polyethylene containing about 42 percent of chemically combined chlorine.
Claim 10
Dependent Claim
48 words
The laminate film structure of claim 7 wherein said internal layer has a thickness of about 0.005 of an inch and said laminate film structure has a total thickness of from about 0.020 to about 0.045 of an inch and a width of up to about 60 inches.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-04-12 | 1985-10-12 | 1986-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-04-12 | 1989-10-12 | 1990-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-04-12 | 1993-10-12 | 1994-04-13 | $7700.00 | Window Closed / Lapsed |