Assignee: Hitachi Ltd
•
Filing: 1980-06-17
•
Granted: 1982-04-13
•
Expires: 2000-06-17
Abstract
Abstract During recyclic use of a chemical copper plating solution, counter anions to copper ions, anions formed by oxidation of a reducing agent, and carbon dioxide by absorption of carbon dioxide from air, which all have an inhibiting effect upon the plating, and also sodium ions having no inhibiting effect are accumulated in the plating solution. These accumulated ions can be removed by electrodialysis. Particularly, regeneration can be satisfactorily regenerated by adjusting the pH of used chemical plating solution to 2-11 before the electrodialysis, and using a selectively monovalent anion permeable membrane as an anion exchange membrane at the electrodialysis.
Inventors
- 👤 Hitoshi Oka
- 👤 Hiroshi Kikuchi
- 👤 Hitoshi Yokono
- 👤 Haruo Suzuki
- 👤 Toyofusa Yoshimura
- 👤 Akira Matsuo
- 👤 Osamu Miyazawa
- 👤 Isamu Tanaka
- 👤 Tokio Isogai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 17:14
CPC Classifications
B; B01; B01D; B01D61/00; B01D61/42; B01D61/44; C; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1617; B01D2311/00; B01D2311/04; Y; Y10; Y10S; Y10S204/00; Y10S204/13
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
134 words
A process for regenerating a chemical copper plating solution, which comprises adjusting pH of a solution containing copper ions, a reducing agent for copper ions, a chelating agent for copper ions and an alkali metal hydroxide as essential components, used in chemical copper plating, to 2-11, leading the plating solution to desalting compartments of an electrodialysis cell, provided alternately with anion exchange membranes and cation exchange membranes, and removing counter ions to copper ions, ions formed by oxidation reaction of the reducing agent, and CO 3 -2 or HCO 3 - formed from carbon dioxide dissolved in the plating solution, which have an inhibiting effect upon chemical copper plating, and alkali metal ions which is free from inhibition of chemical copper plating, accumulated in the solution used in the chemical copper plating by electrodialysis.
Claim 2
Dependent Claim
134 words
A process for regenerating a chemical copper plating solution, which comprises adjusting pH of a solution containing copper ions, a reducing agent for copper ions, a chelating agent for copper ions and an alkali metal hydroxide as essential components, used in chemical copper plating, to 2-11, leading the plating solution to desalting compartments of an electrodialysis cell, provided alternately with anion exchange membranes and cation exchange membranes, and removing counter ions to copper ions, ions formed by oxidation reaction of the reducing agent, and CO 3 -2 or HCO 3 - formed from carbon dioxide dissolved in the plating solution, which have an inhibiting effect upon chemical copper plating, and alkali metal ions which is free from inhibition of chemical copper plating, accumulated in the solution used in the chemical copper plating by electrodialysis.
Claim 3
Dependent Claim
85 words
A process according to claim 1, wherein the counter ions to copper ions are at least one of SO 4 -2 , HCOO -1 , CO 3 -2 and OH - ; the reducing agent is HCHO, the ions formed by the oxidation of the reducing agent is HCOO - , the alkali metal ions are Na + or K + , the anion exchange membranes are monovalent and divalent anion permeable membranes and the cation exchange membranes are monovalent and divalent cation permeable membranes.
Claim 4
Dependent Claim
101 words
A process according to claim 1, wherein the pH-controlling acid is at least one of sulfuric acid, perchloric acid, formic acid and acetic acid, the counter ions to copper ions are at least one of SO 4 -2 , HCOO -1 , CO 3 -2 and OH - ; the reducing agent is HCHO, the ions formed by the oxidation of the reducing agent is HCOO - , the alkali metal ions are Na + or K + , the anion exchange membranes are selectively monovalent anion permeable membranes, and the cation exchange membranes are monovalent and divalent cation permeable membranes.
Claim 5
Dependent Claim
60 words
A process according to claim 2, 1 or 3, wherein the pH of the solution is adjusted to 2-8 to remove CO 3 -2 having a low selective permeability at the electrodialysis and at the same time to make the selective permeabilities of a group of the accumulated ions in the plating solution substantially equal to one another in advance.
Claim 6
Dependent Claim
37 words
A process according to claim 2, 1 or 3, wherein the pH of the solution is adjusted to values higher than 8 but not higher than 11 to convert CO 3 -2 to HCO 3 - .
Claim 7
Dependent Claim
28 words
A process according to claim 1, wherein the anion exchange membranes are selectively monovalent anion permeable membranes and the cation exchange membranes are selectively monovalent cation permeable membranes.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-04-12 | 1985-10-12 | 1986-04-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-04-12 | 1989-10-12 | 1990-04-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-04-12 | 1993-10-12 | 1994-04-13 | $7700.00 | Window Closed / Lapsed |