Abstract
Abstract A scrap-free, substantially solid phase, relatively low temperature economical process for rapidly making plastic articles from resinous powders wherein the resultant articles can comprise various polymers including oriented polymers; polymers with a high practical heat distortion temperature; expanded polymers; ultra high molecular weight polymers; blended structures of two or more materials; or multilayered structures. The resinous powders are initially compressed into briquettes, which briquettes are heated to a temperature in the range from about the alpha transition temperature to less than the melting point or melt temperature of the polymer therein to both somewhat soften and sinter the briquettes. The sintered briquettes are forged under conditions which permit substantial plug flow deformation into preforms whereby fusion of the sintered resin powder particles occurs. The resulting preforms can then be cooled for later thermoforming or can be directly transferred to thermoforming molds for forming into desired shaped articles. It is also possible to form at least shallow cans, lids or other items directly in the forging step.
Inventors
- 👤 Norbert L. Bradley
- 👤 Kenneth J. Cleereman
- 👤 Ritchie A. Wessling
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:50
CPC Classifications
B; B29; B29C; B29C43/00; B29C43/006; B29C43/02; B29C43/16; B29C51/00; B29C51/02; B29C67/00; B29C67/20; B29C67/205; B29C2791/00; B29C2791/001; B29C55/00; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2023/0658; B29K2023/0683; B29K2105/00; B29K2105/25; B29K2105/251
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
119 words
A process for forming a plastic article from thermoplastic polymeric resinous powder wherein a sufficient quantity of said powder for making said article is compressed into a briquette having green strength, the improvement comprising the steps of: (a) heating said briquette to a temperature in the range from about the alpha transition temperature to less than the melt temperature thereof; (b) maintaining said temperature for a period sufficient to soften said briquette and sinter the same short of substantial fusion thereof; and (c) forging the briquette into said article while the briquette is at a temperature within said temperature range to effect substantial plug flow deformation of the briquette and obtain substantial fusion of the powder forming said briquette.
Claim 2
Dependent Claim
119 words
A process for forming a plastic article from thermoplastic polymeric resinous powder wherein a sufficient quantity of said powder for making said article is compressed into a briquette having green strength, the improvement comprising the steps of: (a) heating said briquette to a temperature in the range from about the alpha transition temperature to less than the melt temperature thereof; (b) maintaining said temperature for a period sufficient to soften said briquette and sinter the same short of substantial fusion thereof; and (c) forging the briquette into said article while the briquette is at a temperature within said temperature range to effect substantial plug flow deformation of the briquette and obtain substantial fusion of the powder forming said briquette.
Claim 3
Dependent Claim
22 words
The process of claim 1 wherein the briquette is brought to said temperature of step (a) after said briquette has been formed.
Claim 4
Dependent Claim
29 words
The process of claim 1 wherein lubrication between the briquette and forging mold is provided sufficient to permit said plug flow deformation of the briquette during the forging step.
Claim 5
Dependent Claim
34 words
The process of claim 1 wherein said powder is provided prior to step (a) in an arrangement of a plurality of discrete layers by alternatively charging and compressing each layer in a die cavity.
Claim 6
Dependent Claim
28 words
The process of claim 1 wherein said powder includes a copolymer comprising at least seventy weight percent vinylidene chloride and a remainder of olefinically unsaturated monomers copolymerized therewith.
Claim 7
Dependent Claim
124 words
The process of claim 1 wherein said article takes the form of a preform having a center portion and peripheral portion and said process includes additional steps: (d) securing said peripheral portion of said preform in a clamping ring during the forging step of said preform; (e) cooling the peripheral portion of said preform below the alpha transition temperature of said resinous powder without substantially cooling said center portion; (f) immediately transferring said preform and clamping ring to a thermoforming device; (g) thermoforming said preform into another article prior to substantial cooling of said center portion; (h) cooling said other article below the alpha transition temperature of said resinous powder; and (i) removing said other article from said thermoforming device and said clamping ring.
Claim 8
Dependent Claim
39 words
The process of claim 1 wherein said article is a preform and said process includes additional steps: (d) cooling said preform below the alpha transition temperature of said resinous powder; and (e) removing said preform from said forging mold.
Claim 9
Dependent Claim
14 words
The process of claim 1 wherein said powder comprises a high density polyethylene resin.
Claim 10
Dependent Claim
16 words
The process of claim 1 wherein said powder comprises an ultra high molecular weight polyethylene resin.
Claim 11
Dependent Claim
143 words
A process for forming a plastic article comprising the steps of: (a) selecting a thermoplastic polymeric resinous powder having a small particle size, a broad particle size distribution, an irregular shaped particle, low bulk density and high ductility; (b) comprising a sufficient quantity of said powder to form the article into a briquette having a compaction of at least 85 percent; (c) heating said briquette to a temperature in the range from about the alpha transition temperature to less than the melt temperature thereof; (d) maintaining said temperature for a period sufficient to soften said briquette and sinter the same short of substantial fusion thereof; and (e) forging the briquette into said article while the briquette is at a temperature within said temperature range to effect substantial plug flow deformation of the briquette and obtain substantial fusion of the powder forming said briquette.
Claim 12
Dependent Claim
143 words
A process for forming a plastic article comprising the steps of: (a) selecting a thermoplastic polymeric resinous powder having a small particle size, a broad particle size distribution, an irregular shaped particle, low bulk density and high ductility; (b) comprising a sufficient quantity of said powder to form the article into a briquette having a compaction of at least 85 percent; (c) heating said briquette to a temperature in the range from about the alpha transition temperature to less than the melt temperature thereof; (d) maintaining said temperature for a period sufficient to soften said briquette and sinter the same short of substantial fusion thereof; and (e) forging the briquette into said article while the briquette is at a temperature within said temperature range to effect substantial plug flow deformation of the briquette and obtain substantial fusion of the powder forming said briquette.
Claim 13
Dependent Claim
32 words
The process of claim 10 wherein the powder is a high density polyethylene resin and said briquette has a green breaking strength of about 500 pounds or greater at ambient room temperature.
Claim 14
Dependent Claim
25 words
The process of claim 1, wherein the powder forming the briquette is brought to said temperature of step (a) before said briquette has been formed.
Claim 15
Dependent Claim
22 words
The process of claim 1 wherein step (c) a forging mold, having a temperature range maintained at said temperature range, is used.
Claim 16
Dependent Claim
31 words
The process of claim 1 wherein said substantial fusion is caused to occur before the forging of step (c) has been completed in order to increase orientation in the resulting article.
References Cited (Backward Citations)
US2782180A
Cited
US3234313A
Cited
US3287480A
Cited
US3414643A
Cited
US3662052A
Cited
US3723589A
Cited
US3739052A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-04-05 | 1985-10-05 | 1986-04-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-04-05 | 1989-10-05 | 1990-04-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-04-05 | 1993-10-05 | 1994-04-06 | $7700.00 | Window Closed / Lapsed |