Method for the preparation of silicone-modified polyoxyalkylene polyethers and room temperature-curable compositions therewith
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1980-03-14
•
Granted: 1982-04-06
•
Expires: 2000-03-14
Abstract
Abstract The present invention provides a novel room temperature-curable composition based on a polyoxyalkylene polyether, e.g. polyoxypropylene, admixed with a curing agent which is very stable when kept in a dry atmosphere or in a hermetically sealed condition but is readily cured when exposed to atmospheric air containing moisture into a rubber-like elastomer. The polyoxyalkylene polyether is terminated at both molecular chain ends with organosilyl groups having alkenyloxy groups bonded to the silicon atoms and can be prepared by the addition reaction of an allyl-terminated polyoxyalkylene polyether with an organosilane or organopolysiloxane compound having at least one silicon-bonded hydrogen atom and at least one silicon-bonded alkenyloxy group in a molecule in the presence of a platinum catalyst.
Inventors
- 👤 Toshio Takago
- 👤 Masatoshi Arai
- 👤 Koji Futatsumori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 13:37
CPC Classifications
C; C08; C08L; C08L83/00; C08L83/10; C08L83/12; C08G; C08G65/00; C08G65/02; C08G65/32; C08G65/329; C08G65/336; C08G77/00; C08G77/42; C08G77/46; C08L3/00; C08L3/12; Y; Y10; Y10S; Y10S528/00; Y10S528/901
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
131 words
A room temperature-curable composition which comprises (a) 100 parts by weight of a polyoxyalkylene polyether modified with alkenyloxy-containing organosilicon groups at the chain terminals represented by the general formula ##STR11## where R 1 is a substituted or unsubstituted monovalent hydrocarbon group or a triorganosiloxy group, R 2 is a hydrogen atom or a substituted or unsubstituted monovalent hydrocarbon group, R 3 is a substituted or unsubstituted monovalent hydrocarbon group, R 4 is a divalent hydrocarbon group, R 5 is a divalent hydrocarbon group having from 1 to 4 carbon atoms, a is a number of zero, 1 or 2 and n is a positive integer, and having an average molecular weight in the range from 400 to 15,000, and (b) from 0.01 to 10 parts by weight of a curing agent.
Claim 2
Dependent Claim
131 words
A room temperature-curable composition which comprises (a) 100 parts by weight of a polyoxyalkylene polyether modified with alkenyloxy-containing organosilicon groups at the chain terminals represented by the general formula ##STR11## where R 1 is a substituted or unsubstituted monovalent hydrocarbon group or a triorganosiloxy group, R 2 is a hydrogen atom or a substituted or unsubstituted monovalent hydrocarbon group, R 3 is a substituted or unsubstituted monovalent hydrocarbon group, R 4 is a divalent hydrocarbon group, R 5 is a divalent hydrocarbon group having from 1 to 4 carbon atoms, a is a number of zero, 1 or 2 and n is a positive integer, and having an average molecular weight in the range from 400 to 15,000, and (b) from 0.01 to 10 parts by weight of a curing agent.
Claim 3
Dependent Claim
29 words
The room temperature-curable composition as claimed in claim 1 where R 3 is selected from the class consisting of a hydrogen atom, a methyl group and an ethyl group.
Claim 4
Dependent Claim
20 words
The room temperature-curable composition as claimed in claim 1 wherein R 1 is a methyl group or a phenyl group.
Claim 5
Dependent Claim
52 words
The room temperature-curable composition as claimed in claim 1 wherein the polyoxyalkylene polyether terminated at both chain ends with the alkenyloxy-containing organosilicon groups has at least three alkenyloxy groups represented by the general formula ##STR12## where R 2 and R 3 each have the same meaning as defined above, in a molecule.
Claim 6
Dependent Claim
18 words
The composition of claim 1 wherein the curing agent is a curing accelerator, curing catalyst, or crosslinking agent.
Claim 7
Dependent Claim
38 words
The composition of claim 5 wherein the curing accelerator is a metal salt of a carboxylic acid, organic ester of titanic acid, aminoalkyl substituted alkoxysilane, amine, amine salt, quaternary ammonium salt, guanidine compounds, guanidyl-containing organosilane or guanidyl-containing organopolysiloxane.
Claim 8
Dependent Claim
20 words
The composition of claim 5 wherein the crosslinking agent is an alkenyloxy-containing silane selected from the group consisting of ##STR13##
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-04-05 | 1985-10-05 | 1986-04-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-04-05 | 1989-10-05 | 1990-04-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-04-05 | 1993-10-05 | 1994-04-06 | $7700.00 | Window Closed / Lapsed |