Method for selective etching of titaniumdioxide relative to aluminum
Assignee: USPHILIPS Corp A CORPOF DE
•
Filing: 1981-03-06
•
Granted: 1982-03-30
•
Expires: 2001-03-06
Abstract
Abstract A method of selectively etching a titanium oxide layer with a view to the formation of a mask for the localization of the anodic oxidation of an underlying metallic layer. The method is characterized in that the material comprising the said titanium oxide layer is dipped in a solution of hydrogen peroxide and ammonia. Application to the formation of contacts on semiconductor devices.
Inventors
- 👤 Jean-Pierre Rioult
- 👤 Raymond Fabien
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:43
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/064; H10W20/065; H10P; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
109 words
A method of selectively etching a titanium oxide film covering an aluminum or an aluminum alloy substrate, relative to said substrate, comprising applying to selected portions of the exposed surface of said titanium oxide film an aqueous solution consisting essentially of an aqueous mixture of a 30% aqueous solution by weight of hydrogen peroxide and from 10 to 50% by volume of a unit of volume of said hydrogen peroxide solution of an aqueous solution of ammonia of a specific weight of 0.90 for a time sufficient for said solution to dissolve said selected portions of said titanium dioxide film while having a substantial little effect on said substrate.
Claim 2
Independent Claim
109 words
A method of selectively etching a titanium oxide film covering an aluminum or an aluminum alloy substrate, relative to said substrate, comprising applying to selected portions of the exposed surface of said titanium oxide film an aqueous solution consisting essentially of an aqueous mixture of a 30% aqueous solution by weight of hydrogen peroxide and from 10 to 50% by volume of a unit of volume of said hydrogen peroxide solution of an aqueous solution of ammonia of a specific weight of 0.90 for a time sufficient for said solution to dissolve said selected portions of said titanium dioxide film while having a substantial little effect on said substrate.
Claim 3
Dependent Claim
49 words
In the method of formation of aluminum contacts in a semiconductive device wherein an aluminum film protected by titanium dioxide mask is selectively anodized, the improvement wherein the titanium dioxide mask is formed from a titanium dioxide film by selective etching in accordance with the method of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-29 | 1985-09-28 | 1986-03-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-29 | 1989-09-28 | 1990-03-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-29 | 1993-09-28 | 1994-03-30 | $7700.00 | Window Closed / Lapsed |