Magnetic recording medium
Assignee: Fujifilm Holdings Corp
•
Filing: 1980-02-08
•
Granted: 1982-03-16
•
Expires: 2000-02-08
Abstract
Abstract The present invention relates to a magnetic recording medium having on a non-magnetic support a magnetic layer comprising a ferromagnetic fine powder in a binder, in which a colloidal silica having a diameter of 7 to 50 mμ and methyl groups on the surface thereof is added in a proportion of 2 to 20 parts by weight to 100 parts by weight of the ferromagnetic fine powder during dispersion of the coating composition of the ferromagnetic fine powder.
Inventors
- 👤 Hiroshi Ogawa
- 👤 Hiromi Nakahara
- 👤 Yasuo Tamai
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 00:21
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/708; G11B5/702; G11B5/7028; Y; Y10; Y10S; Y10S428/00; Y10S428/90; Y10T; Y10T428/00; Y10T428/25; Y10T428/259; Y10T428/26; Y10T428/266; Y10T428/269; Y10T428/29; Y10T428/2982; Y10T428/31504; Y10T428/31507; Y10T428/31678; Y10T428/31681; Y10T428/31703
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
172 words
In a magnetic recording medium comprising a magnetic layer supported on a non-magnetic support and wherein the magnetic layer comprises a ferromagnetic fine powder, a binder and a colloidal silica, the improvement comprising employing as the magnetic layer, a composition prepared by dispersing the ferromagnetic fine powder in from 10 to 400 parts by weight, per 100 parts by weight of the ferromagnetic fine powder, of the binder while simultaneously adding thereto 2 to 20 parts by weight, based on 100 parts by weight of the ferromagnetic powder, of a colloidal silica having a diameter of 7 to 50 mμ and methyl groups on the surface thereof and which is prepared by treating a colloidal silica having silanol groups on the surface thereof with methanol, trimethylmonochlorosilane or dimethyldichlorosilane to replace at least 70% of the silanol groups with methyl groups; the ferromagnetic fine powder being one in which the ferromagnetic metal consists essentially of at least one metal selected from the group consisting of Fe, Co, Ni, Fe-Co, Fe-Ni, Co-Ni and Fe-Co-Ni.
Claim 2
Dependent Claim
172 words
In a magnetic recording medium comprising a magnetic layer supported on a non-magnetic support and wherein the magnetic layer comprises a ferromagnetic fine powder, a binder and a colloidal silica, the improvement comprising employing as the magnetic layer, a composition prepared by dispersing the ferromagnetic fine powder in from 10 to 400 parts by weight, per 100 parts by weight of the ferromagnetic fine powder, of the binder while simultaneously adding thereto 2 to 20 parts by weight, based on 100 parts by weight of the ferromagnetic powder, of a colloidal silica having a diameter of 7 to 50 mμ and methyl groups on the surface thereof and which is prepared by treating a colloidal silica having silanol groups on the surface thereof with methanol, trimethylmonochlorosilane or dimethyldichlorosilane to replace at least 70% of the silanol groups with methyl groups; the ferromagnetic fine powder being one in which the ferromagnetic metal consists essentially of at least one metal selected from the group consisting of Fe, Co, Ni, Fe-Co, Fe-Ni, Co-Ni and Fe-Co-Ni.
Claim 3
Dependent Claim
26 words
The magnetic recording medium as claimed in claim 1, wherein the colloidal silica is obtained by heating a colloidal silica in methanol at the boiling point.
Claim 4
Dependent Claim
29 words
The magnetic recording medium as claimed in claim 1, wherein the colloidal silica is obtained by treating a colloidal silica in methanol vapor for 30 minutes to 6 hours.
Claim 5
Dependent Claim
31 words
The magnetic recording medium as claimed in claim 1, wherein the colloidal silica is obtained by treating a colloidal silica and tetrachlorosilane with methanol vapor for 30 minutes to 6 hours.
Claim 6
Dependent Claim
42 words
The magnetic recording medium as claimed in claim 1, wherein the colloidal silica is obtained by heating a colloidal silica with dimethyldichlorosilane and steam at 400° C. in a fluidized bed using an inert gas such as nitrogen gas as a carrier.
Claim 7
Dependent Claim
28 words
The magnetic recording medium as claimed in claim 1, wherein the binder is at least one material selected from the group consisting of thermoplastic resins and thermosetting resins.
Claim 8
Dependent Claim
29 words
The magnetic recording medium as claimed in claim 1, wherein the magnetic layer further contains additives selected from the group consisting of dispersing agents, lubricants, abrasives, and antistatic agents.
Claim 9
Dependent Claim
38 words
The magnetic recording medium as claimed in claim 1, wherein the non-magnetic support is of a material selected from the group consisting of polyethylene terephthalate, polyethylene-2,6-naphthalate, polypropylene, cellulose triacetate, cellulose diacetate, polycarbonate, copper, aluminum, zinc, glass and ceramics.
Claim 10
Dependent Claim
48 words
The magnetic recording medium as claimed in claim 1, wherein the non-magnetic support has a thickness of 2 to 50 mμ in the case of a film, a tape or sheet and a thickness of 0.5 to 10 mm in the case of a disk or a card.
Claim 11
Dependent Claim
20 words
The magnetic recording medium as claimed in claim 1, wherein the colloidal has a diameter of 10 to 30 mμ.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-15 | 1985-09-14 | 1986-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-15 | 1989-09-14 | 1990-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-15 | 1993-09-14 | 1994-03-16 | $7700.00 | Window Closed / Lapsed |