Method to manufacture soft magnetic pressed bodies
Assignee: ERIC MCMILLAN Inc
•
Filing: 1980-10-03
•
Granted: 1982-03-16
•
Expires: 2000-10-03
Abstract
Abstract To permit use of less expensive iron powder material and manufacture of more complex shapes, a mixture of iron powder, of an approximate grain size of between 30 to 450 μm, and containing preferably 5 to 50% of carbonyl iron powder or from 5 to 50%, by weight, of soft ferrite powder of a grain size of from 10 to 200 μm, and a thermosetting resin, in which the thermosetting resin is about 50% by volume of the overall mixture, is filled into a die. Pressure is built up in the die, which is heated, permitting excess binder to escape during the build-up phase thereof, the pressure then being held so that the resin can set in the heated die. The pressures needed are substantially less than heretofore required, in the order of from between 500 to 5000 bar.
Inventors
- 👤 Friedrich Esper
- 👤 Hans-Martin Wiedenmann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 15:11
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/20; H01F1/22; H01F1/24; H01F1/26; H01F1/28; H01F1/33; H01F1/34; H01F1/36; H01F1/37; Y; Y10; Y10S; Y10S264/00; Y10S264/58
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
107 words
Method to manufacture soft magnetic pressed bodies comprising a mixture of soft magnetic material and a resin binder, comprising the steps of preparing a mixture of iron powder which includes atomized, sponge or electrolytic iron powder and a liquid component consisting essentially of a liquid thermosetting resin having a viscosity of at least 1,000 cpoises; filling the mixture into a die; heating said die; building up pressure in said die to squeeze out excess liquid and permit escape thereof through the clearance between die walls and adjacent punch side walls during build-up of the pressure; and keeping the pressure for final compacting until the resin has cured.
Claim 2
Dependent Claim
107 words
Method to manufacture soft magnetic pressed bodies comprising a mixture of soft magnetic material and a resin binder, comprising the steps of preparing a mixture of iron powder which includes atomized, sponge or electrolytic iron powder and a liquid component consisting essentially of a liquid thermosetting resin having a viscosity of at least 1,000 cpoises; filling the mixture into a die; heating said die; building up pressure in said die to squeeze out excess liquid and permit escape thereof through the clearance between die walls and adjacent punch side walls during build-up of the pressure; and keeping the pressure for final compacting until the resin has cured.
Claim 3
Dependent Claim
18 words
Method according to claim 1, wherein the mixture is filled into a heated die, and is then compacted.
Claim 4
Dependent Claim
14 words
Method according to claim 1, wherein the iron powder further includes carbonyl iron powder.
Claim 5
Dependent Claim
24 words
Method according to claim 3, wherein the carbonyl iron powder is present in an amount up to 50%, by weight, of the iron powder.
Claim 6
Dependent Claim
19 words
Method according to claim 1, wherein the carbonyl iron powder at least partially is replaced by soft ferrite powder.
Claim 7
Dependent Claim
27 words
Method according to claim 5, wherein the soft ferrite powder is present in a quantity of from 5 to 50% by weight of the iron powder mixture.
Claim 8
Dependent Claim
20 words
Method according to claim 1, wherein the iron powder has a grain size of from about 30 to 450 micrometers.
Claim 9
Dependent Claim
20 words
Method according to claim 5, wherein the soft ferrite powder has a grain size of between 10 to 200 micrometers.
Claim 10
Dependent Claim
25 words
Method according to claim 1, wherein the thermosetting resin comprises at least one resin selected from the group consisting of polyester resin and phenol resin.
Claim 11
Dependent Claim
25 words
Method according to claim 1, wherein the step of building up pressure in the die comprises applying a pressure of between 200 to 5000 bar.
Claim 12
Dependent Claim
42 words
Method according to claim 1, wherein the step of buildig up pressure comprises building up the pressure during a period of from 1 to 30 seconds; and then holding the pressure during the time required for the thermosetting resin to completely set.
Claim 13
Dependent Claim
36 words
Method according to claim 1, wherein the step of mixing the iron powder with the thermosetting resin comprises mixing the iron powder with liquid thermosetting resin in a proportion (by volume) of 20% to 60% resin.
Claim 14
Dependent Claim
45 words
Method according to any one of claims 1, 4, 6, 7, 8, 9, 10 or 11, wherein the step of mixing the iron powder with the thermosetting resin comprises mixing the iron powder with liquid thermosetting resin in a proportion (by volume) of about 50%.
Claim 15
Dependent Claim
119 words
Method of manufacturing soft magnetic pressed bodies comprising a mixture of soft magnetic materials and a resin binder, comprising the steps of: admixing iron powder having a grain size of from about 30 to 450 micrometers and a liquid component consisting essentially of a liquid thermosetting resin having a viscosity of at least 1,000 cpoises; filling said mixture into a die; heating said die; applying a pressure in the die of between 200 and 5,000 bar during a period of from one to thirty seconds to squeeze out excess liquid and permit escape thereof through the clearance between the die walls and punch side walls during build-up of the pressure, and maintaining the pressure until said resin has cured.
Claim 16
Dependent Claim
119 words
Method of manufacturing soft magnetic pressed bodies comprising a mixture of soft magnetic materials and a resin binder, comprising the steps of: admixing iron powder having a grain size of from about 30 to 450 micrometers and a liquid component consisting essentially of a liquid thermosetting resin having a viscosity of at least 1,000 cpoises; filling said mixture into a die; heating said die; applying a pressure in the die of between 200 and 5,000 bar during a period of from one to thirty seconds to squeeze out excess liquid and permit escape thereof through the clearance between the die walls and punch side walls during build-up of the pressure, and maintaining the pressure until said resin has cured.
Claim 17
Dependent Claim
45 words
Method according to claim 14 wherein said thermosetting resin is selected from a group consisting of polyester and phenol resins and wherein said liquid thermosetting resin is in a proportion (by volume) of about 50% of the mixture of iron powders and liquid thermosetting resins.
Claim 18
Dependent Claim
33 words
Method according to claim 14 or 15 wherein from 5 to 50% of said carbonyl iron powder is replaced by soft ferrite powder having a grain size of between 10 and 20 micro-meters.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-15 | 1985-09-14 | 1986-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-15 | 1989-09-14 | 1990-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-15 | 1993-09-14 | 1994-03-16 | $7700.00 | Window Closed / Lapsed |