Method for producing disc or band-shaped Si crystals with columnar structure for solar cells
Assignee: Siemens AG
•
Filing: 1979-11-08
•
Granted: 1982-03-16
•
Expires: 1999-11-08
Abstract
Abstract Si-crystals with columnar structures are produced by casting a silicon melt through a gap provided in a crucible onto a melt-resistant carrier body having periodically spaced crystallization-seed centers on a surface thereof facing the melt, and allowing the so-cast molten silicon to cool so that crystallization of the melt onto the seed centers occurs. In a preferred embodiment, an elongated traveling band-shaped substrate having a select hole pattern therein functioning as the seed centers, is utilized as the carrier body.
Inventors
- 👤 Josef Grabmaier
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 21:23
CPC Classifications
C; C30; C30B; C30B15/00; C30B15/007; C30B11/00; C30B11/001; C30B11/14
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
107 words
A method of producing disc or band-shaped silicon crystals having a columnar structure and useful in the manufacture of solar cells, comprising: casting molten silicon through a gap located at the bottom of a crucible containing said molten silicon onto a band-shaped carrier body composed of a material which is resistant to said molten silicon, said carrier body having substantially uniform mesh openings which substantially define the crystalline columnar structures in said disc or band-shaped silicon crystals; and cooling said carrier body by directing a stream of inert gas against the underside of said carrier body whereby silicon grows with a columnar structure in said mesh openings.
Claim 2
Independent Claim
107 words
A method of producing disc or band-shaped silicon crystals having a columnar structure and useful in the manufacture of solar cells, comprising: casting molten silicon through a gap located at the bottom of a crucible containing said molten silicon onto a band-shaped carrier body composed of a material which is resistant to said molten silicon, said carrier body having substantially uniform mesh openings which substantially define the crystalline columnar structures in said disc or band-shaped silicon crystals; and cooling said carrier body by directing a stream of inert gas against the underside of said carrier body whereby silicon grows with a columnar structure in said mesh openings.
Claim 3
Dependent Claim
20 words
A method as defined in claim 1, wherein said crucible and said carrier body are moved relative to one another.
Claim 4
Dependent Claim
42 words
A method as defined in claim 2, wherein the rate of movement between said crucible and said carrier body is about one meter per minute whereby a silicon layer having a thickness of about 100 μm is crystallized onto said carrier body.
Claim 5
Dependent Claim
28 words
A method as defined in claim 1, wherein said holes within the carrier body each have an axial width in the range of about 100 to 300 μm.
Claim 6
Dependent Claim
42 words
A method as defined in claim 1, wherein said holes within the carrier body are spaced from one another so that the distance from one hole center to an adjacent hole center is in the range of about 150 to 350 μm.
Claim 7
Dependent Claim
17 words
A method as defined in claim 1, wherein said holes within said carrier body are hexagonally arranged.
Claim 8
Dependent Claim
38 words
A method as defined in claim 1, wherein said carrier body is composed of a material selected from the group consisting of quartz glass, graphite and zirconium oxide and comprises a compressed mat or foil of such material.
Claim 9
Dependent Claim
35 words
A method as defined in claim 1, wherein said carrier body comprises a net-like body having substantially uniform mesh openings therein, said openings being of a size adapted to the columnar structure of silicon crystal.
Claim 10
Dependent Claim
40 words
A method as defined in claim 1, wherein said carrier body with a layer of molten silicon thereon is guided through a select size aparture so as to achieve a uniform silicon layer thickness and strip-off any excess silicon melt.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-15 | 1985-09-14 | 1986-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-15 | 1989-09-14 | 1990-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-15 | 1993-09-14 | 1994-03-16 | $7700.00 | Window Closed / Lapsed |