Assignee: International Business Machines Corp
•
Filing: 1979-12-17
•
Granted: 1982-03-09
•
Expires: 1999-12-17
Abstract
Abstract A laminated conductor includes a lower thin film of nickel deposited upon a substrate containing silicon. Upon the film of nickel, a thicker film of gold is deposited as the conductive portion of the conductor. On the upper surface of the gold layer is deposited a thin film of nickel. Failure of the conductor because of electromigration is reduced dramatically as compared with use of molybdenum instead of nickel in the laminated structure.
Inventors
- 👤 Amitava Gangulee
- 👤 Paul S. Ho
- 👤 James K. Howard
- 👤 Robert J. Miller
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 16:00
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/40; H10W20/41; H10W20/44; H10W20/4403; H10W20/4432; H10P; H10P14/00; H10P14/40; H10P14/412; H10W20/425
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
161 words
A conductor line for a solid state circuit supported by a substrate comprising a first layer of nickel deposited upon said substrate as the base of said conductor line, an intermediate layer of gold deposited upon said first layer, and a third layer of nickel deposited upon said layer of gold, said first layer of nickel and said third layer of nickel being within the range from on the order of 10×10 -9 to on the order of 100×10 -9 meters thick and said gold layer being on the order of micrometers wide and within the range from on the order of 100×10 -9 to on the order of 2000×10 -9 thick, for a conductor line having a width for said thickenesses adapted for carrying current densities reaching to on the order of the mid-10 6 amperes/cm 2 range, whereby the electromigration lifetime of such a conductor is lengthened by the interaction of the nickel and gold atoms in the structure.
Claim 2
Dependent Claim
161 words
A conductor line for a solid state circuit supported by a substrate comprising a first layer of nickel deposited upon said substrate as the base of said conductor line, an intermediate layer of gold deposited upon said first layer, and a third layer of nickel deposited upon said layer of gold, said first layer of nickel and said third layer of nickel being within the range from on the order of 10×10 -9 to on the order of 100×10 -9 meters thick and said gold layer being on the order of micrometers wide and within the range from on the order of 100×10 -9 to on the order of 2000×10 -9 thick, for a conductor line having a width for said thickenesses adapted for carrying current densities reaching to on the order of the mid-10 6 amperes/cm 2 range, whereby the electromigration lifetime of such a conductor is lengthened by the interaction of the nickel and gold atoms in the structure.
Claim 3
Dependent Claim
30 words
A conductor in accordance with claim 1 deposited upon a substrate composed of a material containing silicon with the lower nickel layer of said conductor in contact with said substrate.
Claim 4
Dependent Claim
37 words
A conductor in accordance with claim 1 or 2 wherein said layers of nickel are on the order of 25×10 -9 meters thick and said layer of gold is on the order of 400×10 -9 meters thick.
Claim 5
Dependent Claim
50 words
A conductor in accordance with claim 1 or 2 wherein said layers of nickel are on the order of 25×10 -9 meters thick and said layer of gold is on the order of 400×10 -9 meters thick, and said conductor has a width on the order of 7×10 -6 meters.
Claim 6
Dependent Claim
26 words
A conductor in accordance with claim 1 or 2 wherein said layers of nickel and gold were deposited by electron beam evaporation in a vacuum chamber.
Claim 7
Dependent Claim
60 words
A conductor in accordance with claim 1 or 2 wherein said layers of nickel and gold were deposited by electron beam evaporation in a vacuum chamber and were patterned by means of ion milling while employing a photoresist stencil as a mask, followed by annealing at about 300° C. in forming gas for several hours to diffuse Ni into Au.
Claim 8
Dependent Claim
19 words
A conductor in accordance with claim 1 wherein said gold layer includes nickel atoms dissolved into said gold layer.
Claim 9
Dependent Claim
26 words
A conductor in accordance with claim 7 wherein said nickel and gold layers comprise annealed layers with diffusion of said nickel atoms into said gold layer.
Claim 10
Dependent Claim
113 words
A conductor line for a solid state circuit supported by a substrate, comprising: a first layer of nickel deposited upon said substrate; an intermediate layer of gold deposited upon said first layer of nickel; and a third layer of nickel deposited upon said intermediate layer of gold; said intermediate layer of gold having a thickness greater than the thickness of each of said first and third layers of nickel, and being adapted for carrying current densities reaching to on the order of the mid-10 6 amperes per cm 2 range; whereby the electromigration lifetime of said conductor line is lengthened by the interaction of the nickel and gold atoms in said conductor line.
Claim 11
Dependent Claim
113 words
A conductor line for a solid state circuit supported by a substrate, comprising: a first layer of nickel deposited upon said substrate; an intermediate layer of gold deposited upon said first layer of nickel; and a third layer of nickel deposited upon said intermediate layer of gold; said intermediate layer of gold having a thickness greater than the thickness of each of said first and third layers of nickel, and being adapted for carrying current densities reaching to on the order of the mid-10 6 amperes per cm 2 range; whereby the electromigration lifetime of said conductor line is lengthened by the interaction of the nickel and gold atoms in said conductor line.
References Cited (Backward Citations)
US3362851A
Cited
US3396454A
Cited
US3419765A
Cited
US3409974A
Cited
US3551842A
Cited
US3645785A
Cited
US3663184A
Cited
US3617816A
Cited
US3631304A
Cited
US3679472A
Cited
US3715234A
Cited
US3717563A
Cited
US3743894A
Cited
US3781596A
Cited
DE2440481C3
Cited
US3959522A
Cited
US3982908A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-08 | 1985-09-07 | 1986-03-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-08 | 1989-09-07 | 1990-03-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-08 | 1993-09-07 | 1994-03-09 | $7700.00 | Window Closed / Lapsed |