Bi-metallic thermo-barrier material and method of welding
Assignee: Rohr Inc
•
Filing: 1980-07-02
•
Granted: 1982-03-09
•
Expires: 2000-07-02
Abstract
Abstract The manufacturing of multi-layer bi-metallic thermo-barrier material utilizing combined brazing and difussion bonding methods of joining together the components of the barrier material.
Inventors
- 👤 Winford Blair
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:23
CPC Classifications
F; F16; F16L; F16L59/00; F16L59/06; B; B23; B23K; B23K1/00; B23K1/008; B23K20/00; B64; B64G; B64G1/00; B64G1/22; B64G1/52; B64G1/58; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/1234; Y10T428/12347
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
261 words
A method of manufacturing thermo-barrier material comprising at least three stacked cellular core structures with nodes projecting in opposite directions from a midplane and flat plate material sandwiched between each of the stacked cellular core structures and positioned on the outer surfaces of the outermost cellular core structure to form outer surface thereon, comprising the steps of: selecting component material of selected size; providing a plating material between the node and flat plate material contacting surfaces of at least one of the cellular core structures; applying a braze alloy to the nodes of the remaining cellular core material; securing together the cellular core material with braze alloy coated nodes and their associated flat sheet material; placing the secured together components on a reference surface; placing the secured together components and reference surface into a furnace; providing means for applying pressure to the secured components; evacuating the furnace; elevating the furnace temperature for melting the braze material; cooling the furnace and removing the now brazed together components; securing together the now brazed together components and the remaining components; placing the secured brazed together and remaining components on a reference surface; placing the secured brazed together components, remaining components and reference surface into a furnace; applying a pressure between the brazed together components, remaining components and the reference furnace; evacuating the furnace; and elevating the temperature within the furnace and maintaining that elevated temperature sufficiently long to cause a eutectic melt of the plating materials and diffuse that plating material into the base material of the adjacent components creating a diffusion bond thereby.
Claim 2
Independent Claim
261 words
A method of manufacturing thermo-barrier material comprising at least three stacked cellular core structures with nodes projecting in opposite directions from a midplane and flat plate material sandwiched between each of the stacked cellular core structures and positioned on the outer surfaces of the outermost cellular core structure to form outer surface thereon, comprising the steps of: selecting component material of selected size; providing a plating material between the node and flat plate material contacting surfaces of at least one of the cellular core structures; applying a braze alloy to the nodes of the remaining cellular core material; securing together the cellular core material with braze alloy coated nodes and their associated flat sheet material; placing the secured together components on a reference surface; placing the secured together components and reference surface into a furnace; providing means for applying pressure to the secured components; evacuating the furnace; elevating the furnace temperature for melting the braze material; cooling the furnace and removing the now brazed together components; securing together the now brazed together components and the remaining components; placing the secured brazed together and remaining components on a reference surface; placing the secured brazed together components, remaining components and reference surface into a furnace; applying a pressure between the brazed together components, remaining components and the reference furnace; evacuating the furnace; and elevating the temperature within the furnace and maintaining that elevated temperature sufficiently long to cause a eutectic melt of the plating materials and diffuse that plating material into the base material of the adjacent components creating a diffusion bond thereby.
Claim 3
Dependent Claim
14 words
The method of claim 1, wherein said plating is applied to the node surface.
Claim 4
Dependent Claim
17 words
The method of claim 1, wherein the plating comprises sequentially applying layers of nickel, copper and silver.
Claim 5
Dependent Claim
16 words
The method of claim 2, wherein the layers of plating materials are substantially equal by weight.
Claim 6
Dependent Claim
44 words
The method of claim 1, wherein the braze material is applied by first spray wetting the surfaces to which the braze material is to be applied with an acrylic binder, and secondly, while the binder is still wet applying a powdered braze alloy thereto.
Claim 7
Dependent Claim
20 words
The method of claim 1, wherein the various components are secured together prior to entering the furnace by resistance welding.
Claim 8
Dependent Claim
28 words
The method of claim 1, comprising an additional step of providing bonding pressure control means to the secured together components prior to the step of evacuating the furnace.
Claim 9
Dependent Claim
21 words
The method of claim 1, wherein the temperature in the last step of elevating furnace temperature is approximately 940 deg C.
Claim 10
Dependent Claim
18 words
The method of claim 1 including the additional step of evacuating the inner structure of the termo-barrier material.
Claim 11
Dependent Claim
12 words
A thermo-barrier material manufactured by the method of claims 1 or 9.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-08 | 1985-09-07 | 1986-03-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-08 | 1989-09-07 | 1990-03-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-08 | 1993-09-07 | 1994-03-09 | $7700.00 | Window Closed / Lapsed |