Surface sensitized chalcogenide product and process for making and using the same
Assignee: GCA Corp
•
Filing: 1979-12-03
•
Granted: 1982-02-23
•
Expires: 1999-12-03
Abstract
Abstract Surface sensitization of a chalcogenide glass is achieved by depositing an extremely thin silver layer, for example, by depositing a silver halide and developing and fixing in the absence of exposure. The sensitized chalcogenide can then be exposed to light to make it etch-resistant. Further exposure reverses the etch resistance, permitting positive or negative images and permitting erasure. Microlithographic resists such as masks can be formed.
Inventors
- 👤 Joseph I. Masters
- 👤 Gershon M. Goldberg
- 👤 Jerome M. Lavine
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 20:11
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/0042; G03F7/0044
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
76 words
A photosensitive product for the formation of microlithographic resists, masks and the like comprising a substrate, a layer of an etchable chalcogenide glass on said substrate, and an extremely thin deposit of silver on the surface of said chalcogenide glass, said silver deposit being thinner than about 100 A., said silver deposit being formed by depositing binderless silver halide thereon and photographically reducing and fixing said silver halide in the absence of exposure to activating radiation.
Claim 2
Dependent Claim
76 words
A photosensitive product for the formation of microlithographic resists, masks and the like comprising a substrate, a layer of an etchable chalcogenide glass on said substrate, and an extremely thin deposit of silver on the surface of said chalcogenide glass, said silver deposit being thinner than about 100 A., said silver deposit being formed by depositing binderless silver halide thereon and photographically reducing and fixing said silver halide in the absence of exposure to activating radiation.
Claim 3
Dependent Claim
17 words
The photosensitive product of claim 1, wherein said product is essentially free from exposure to activating radiation.
Claim 4
Dependent Claim
52 words
The photosensitive product of claim 1, wherein said product is uniformly fogged by exposure to activating radiation in a quantity to bring about essentially full etch resistance in said chalcogenide glass, said product being characterized by photoresponse to activating radiation to reduce the etch resistance of said chalcogenide glass upon further exposure.
Claim 5
Dependent Claim
16 words
The photosensitive product of claim 1 wherein said chalcogenide glass is As 2 S 3 .
Claim 6
Dependent Claim
37 words
The photosensitive product of claim 4, wherein said layer of As 2 S 3 comprises an under layer of As 2 S 3 exposed to ultraviolet light and a surface layer free from exposure to ultraviolet light.
Claim 7
Dependent Claim
69 words
A photosensitive resist for the formation of microlithographic resists, masks and the like comprising a substrate, a layer of an etchable chalcogenide glass vacuum evaporated on said substrate, and an extremely thin deposit of silver on the surface of said chalcogenide glass, said silver deposit being thinner than about 100 A, said silver deposit being formed by depositing binderless silver halide in the absence of exposure to activating radiation.
Claim 8
Dependent Claim
69 words
A photosensitive resist for the formation of microlithographic resists, masks and the like comprising a substrate, a layer of an etchable chalcogenide glass vacuum evaporated on said substrate, and an extremely thin deposit of silver on the surface of said chalcogenide glass, said silver deposit being thinner than about 100 A, said silver deposit being formed by depositing binderless silver halide in the absence of exposure to activating radiation.
Claim 9
Dependent Claim
13 words
The photosensitive resist of claim 6, wherein said chalcogenide glass is arsenic trisulfide.
Claim 10
Dependent Claim
73 words
As an intermediate product, a product for the formation of microlithographic resists, masks and the like, comprising the product of claim 4 having areas of etch-susceptible As 2 S 3 and areas of etch-resistant As 2 S 3 , the areas of etch resistant As 2 S 3 corresponding to areas which are activated by a history of exposure to the radiation-containing portions of a pattern of light and shadow of said radiation.
Claim 11
Independent Claim
100 words
A method of making a photosensitive product for the formation of microlithographic resists, masks and the like, comprising vacuum evaporating a chalcogenide glass on a substrate, depositing a binderless silver halide on the surface of said chalcogenide glass, partially reducing said silver halide, in the absence of photographic developer quantitatively sufficient to form an extremely thin layer of reduced silver less than 100 A in thickness on said chalcogenide glass surface, and fixing said layer to remove silver halide, whereby a surface sensitized chalcogenide layer results, said layer being reversibly altered in etch resistance by exposure to moderate activating radiation.
Claim 12
Independent Claim
100 words
A method of making a photosensitive product for the formation of microlithographic resists, masks and the like, comprising vacuum evaporating a chalcogenide glass on a substrate, depositing a binderless silver halide on the surface of said chalcogenide glass, partially reducing said silver halide, in the absence of photographic developer quantitatively sufficient to form an extremely thin layer of reduced silver less than 100 A in thickness on said chalcogenide glass surface, and fixing said layer to remove silver halide, whereby a surface sensitized chalcogenide layer results, said layer being reversibly altered in etch resistance by exposure to moderate activating radiation.
Claim 13
Dependent Claim
15 words
The method of claim 9, wherein the chalcogenide glass is As 2 S 3 .
Claim 14
Dependent Claim
118 words
The process of forming a pattern of chalcogenide glass comprising evaporating a layer of chalcogenide glass on a substrate, depositing a binderless silver halide on the surface of said chalcogenide glass to form a unitary product, in the absence of exposure to activiating radiation, developing said silver halide in a photographic developer quantitatively sufficient to form an extremely thin layer of reduced silver less than 100 A in thickness, fixing said unitary product, thereby removing silver halide therefrom, exposing said product to a pattern of light and shadow to be reproduced, and etching said chalcogenide glass to form a pattern of said glass on the substrate, said pattern of glass corresponding to the pattern of light and shadow.
Claim 15
Dependent Claim
118 words
The process of forming a pattern of chalcogenide glass comprising evaporating a layer of chalcogenide glass on a substrate, depositing a binderless silver halide on the surface of said chalcogenide glass to form a unitary product, in the absence of exposure to activiating radiation, developing said silver halide in a photographic developer quantitatively sufficient to form an extremely thin layer of reduced silver less than 100 A in thickness, fixing said unitary product, thereby removing silver halide therefrom, exposing said product to a pattern of light and shadow to be reproduced, and etching said chalcogenide glass to form a pattern of said glass on the substrate, said pattern of glass corresponding to the pattern of light and shadow.
Claim 16
Dependent Claim
15 words
The process of claim 9 wherein said chalcogenide glass is As 2 S 3 .
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-02-22 | 1985-08-24 | 1986-02-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-02-22 | 1989-08-24 | 1990-02-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-02-22 | 1993-08-24 | 1994-02-23 | $7700.00 | Window Closed / Lapsed |