Rare earth oxyhalide phosphor and x-ray image converters utilizing same

Claim 2

An improved brightness oxyhalide phosphor having the following structured formula: LnOX:T x wherein Ln is one or more of La and Gd, X is one or more of Cl and Br, and T x is an activator ion selected from Tb and Tm, including mixtures thereof; consisting essentially of recrystallized phosphor crystals in the average median particle size range not below about 2 microns and not greater than about 16 microns and being shaped as plate-like particles having a length to thickness ratio no greater than about 10 to 1, said phosphor exhibiting less light scattering and absorption by reason of said crystalline characteristics.

Claim 3

An improved brightness phosphor as in claim 1 wherein T x is Tb at a concentration in the range from about 0.0001 to about 0.10 mole per mole of the selected oxyhalide.

Claim 4

An improved brightness phosphor as in claim 1 wherein T x is Tm at a concentration in the range from about 0.0001 to about 0.10 mole per mole of the selected oxyhalide.

Claim 5

An improved brightness phosphor as in claim 1 wherein the selected oxyhalide is lanthanum oxybromide.

Claim 6

An x-ray image converter including the phosphor of claim 1 supported on a base member, said phosphor converting x-radiation to radiation of a longer wavelength with improved image sharpness.

Claim 7

An improved multilayer x-ray screen construction which comprises: (a) a photographic film having emulsion layers disposed on each major surface and separated by an optically transparent support, (b) a pair of phosphor layers being positioned on each side of said photographic film to form a sandwich configuration, and (c) each of said phosphor layers comprising an improved brightness oxyhalide phosphor having the following structural formula: LnOX:T x wherein Ln is one or more of La and Gd, X is one or more of Cl and Br, and T x is an activator ion selected from Tb and Tm, including mixtures thereof; consisting essentially of recrystallized phosphor crystals in the average median particle size range not below about 2 microns and not greater than about 16 microns and being shaped as plate-like particles having a length to thickness ratio no greater than about 10 to 1, said phosphor exhibiting improved image sharpness and reduced crossover problem.

Claim 8

An improved multilayer x-ray screen construction which comprises: (a) a photographic film having emulsion layers disposed on each major surface and separated by an optically transparent support, (b) a pair of phosphor layers being positioned on each side of said photographic film to form a sandwich configuration, and (c) each of said phosphor layers comprising an improved brightness oxyhalide phosphor having the following structural formula: LnOX:T x wherein Ln is one or more of La and Gd, X is one or more of Cl and Br, and T x is an activator ion selected from Tb and Tm, including mixtures thereof; consisting essentially of recrystallized phosphor crystals in the average median particle size range not below about 2 microns and not greater than about 16 microns and being shaped as plate-like particles having a length to thickness ratio no greater than about 10 to 1, said phosphor exhibiting improved image sharpness and reduced crossover problem.

Claim 9

An improved x-ray screen as in claim 6 wherein T x is Tb at a concentration in the range from about 0.001 to about 0.005 mole per mole of the selected oxyhalide.

Claim 10

An improved x-ray screen as in claim 6 wherein T x is Tm at a concentration in the range from about 0.001 to about 0.004 mole per mole of the selected oxyhalide.

Claim 11

An improved x-ray screen as in claim 6 wherein the selected oxyhalide is lanthanum oxybromide.

Claim 12

A process for the production of lanthanum and gadolinium oxyhalide phosphor crystals selected from the group consisting of oxychlorides and oxybromides activated with a rare earth ion selected from terbium and thulium, including mixtures thereof, consisting essentially of recrystallized phosphor crystals with average median particle size range not below about 2 microns and not greater than about 16 microns and being shaped as plate-like particles having a length to thickness ratio no greater than about 10 to 1, comprising the following steps: (a) heating mixtures of particles of the oxides of the selected oxyhalide and rare earth ions with ammonium halide whose halide is that of the selected oxyhalide for a time and a temperature sufficient to form the selected oxyhalide phosphor and (b) heating a mixture of said selected oxyhalide phosphor with an alkali halide mixture whose halide is that of the selected oxyhalide for a time of at least about one hour at a temperature above the eutectic melting temperature of the selected alkali halide mixture to recrystallize said selected oxyhalide phosphor.

Claim 13

A process for the production of lanthanum and gadolinium oxyhalide phosphor crystals selected from the group consisting of oxychlorides and oxybromides activated with a rare earth ion selected from terbium and thulium, including mixtures thereof, consisting essentially of recrystallized phosphor crystals with average median particle size range not below about 2 microns and not greater than about 16 microns and being shaped as plate-like particles having a length to thickness ratio no greater than about 10 to 1, comprising the following steps: (a) heating mixtures of particles of the oxides of the selected oxyhalide and rare earth ions with ammonium halide whose halide is that of the selected oxyhalide for a time and a temperature sufficient to form the selected oxyhalide phosphor and (b) heating a mixture of said selected oxyhalide phosphor with an alkali halide mixture whose halide is that of the selected oxyhalide for a time of at least about one hour at a temperature above the eutectic melting temperature of the selected alkali halide mixture to recrystallize said selected oxyhalide phosphor.

Claim 14

A process as in claim 10 in which the alkali metal carbonates of the selected alkali halide mixture are added to the starting materials before the initial heating step so that said alkali metal carbonates will react with said ammonium halide to form the selected alkali halide mixture in the initial step.

Claim 15

A process as in claim 10 in which divalent metal halides whose halide is that of the selected oxyhalide is added to the alkali halide mixture.

Claim 16

A process as in claim 10 in which a rare earth halide selected from lanthanum halide and gadolinium halide whose halide is that of the selected oxyhalide is added to the alkali halide mixture.

Claim 17

A process as in claim 10 in which divalent metal halides whose halide is that of the selected oxyhalide is added to the alkali halide mixture with a rare earth halide selected from lanthanum halide and gadolinium halide whose halide is also that of the selected oxyhalide.

Claim 18

A process as in claim 10 in which the mixture heated to recrystallize said selected oxyhalide phosphor comprises: uAX+wMX.sub.2 +yRX.sub.3 +zROX wherein X is the selected halide, A is one or more of Li, Na, K and Cs, M is one or more of Mg, Ca, Sr, Ba, Zn, Mn and Cd, R is one or more of La and Gd, u is from a small but effective amount up to about 50 weight percent, w is from 0 up to about 20 weight percent, y is from a small but effective amount up to about 50 weight percent, and z is at least 40 weight percent.

Claim 19

A process as in claim 10 in which an alkali metal halide whose halide is that of the selected oxyhalide and selected from halides of Li, Na, K, and Cs is added to the starting materials before the initial heating step with a divalent metal halide whose halide is that of the selected oxyhalide and selected from halides of Mg, Ca, Sr, Ba, Zn, Mn and Cd.