Process for preparing chemically platable thermosetting powder coating
Assignee: Resonac Corp
•
Filing: 1980-03-19
•
Granted: 1982-02-16
•
Expires: 2000-03-19
Abstract
Abstract A process for preparing a chemically platable thermosetting powder coating characterized by preliminarily kneading a composition comprising 3 to 50% by weight of a thermosetting resin, 5 to 60% by weight of an inorganic filler and up to 80% by weight of a rubber component comprising at least 10% by weight of a rubber having ethylenic double bonds and polar groups in the molecule, the amount of which rubber component constitutes the total amount of rubber component in the final powder coating, the rubber component content of the composition to be subjected to the preliminary kneading being at least twice the rubber component content of the final powder coating, said composition being heated at a temperature of at least the melting point of the thermosetting resin at least once during the course of the preliminary kneading, thereby to effect efficient dispersion of the components. The powder coating prepared according to the process of the present invention is substantially homogeneous due to the uniform dispersion of its components, thus providing good applicability thereof on an article, excellent levelling of a coated film of the powder coating when molten in the step of heat hardening and an improved peeling strength between the coated and heat-hardened film of the powder coating and a metal deposited thereon by chemical plating. The chemically platable thermosetting powder coating prepared according to the process of the present invention may further comprise a catalyst for chemical plating, at least 50% by weight of catalyst in the final powder coating being kneaded together with the above-mentioned composition in the step of preliminary kneading.
Inventors
- 👤 Hiroshi Takahashi
- 👤 Koichi Tsuyama
- 👤 Nobuo Uozu
- 👤 Makoto Fujikura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 17:50
CPC Classifications
H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/05; H05K1/056; C; C09; C09D; C09D5/00; C09D5/03; H05K2201/00; H05K2201/02; H05K2201/0203; H05K2201/0206; H05K2201/0209; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/38; H05K3/386; Y; Y10; Y10S; Y10S524/00; Y10S524/904
Claims Analysis
Total Claims: 27
Claim 1
Independent Claim
309 words
A process for preparing a chemically platable thermosetting powder coating comprising an intimate mixture of components in the following proportions: 100 parts by weight of at least one thermosetting resin having a melting point of up to 150° C., 1 to 30 parts by weight of a rubber component comprising at least 10% by weight of at least one rubber having ethylenic double bonds and polar groups in the molecule and up to 200 parts by weight of at least one inorganic filler, said powder coating having a melt viscosity of up to 10 5 centipoises at least once during the course of heat hardening, the lower limit of the amount of the inorganic filler in the powder coating corresponding to that amount of the inorganic filler used in step (1) of preliminary kneading as described below, which process comprises the steps of: (1) preliminarily kneading a composition comprising 3 to 50% by weight of at least one thermosetting resin having a melting point of up to 150° C., 5 to 60% by weight of at least one inorganic filler and up to 80% by weight of a rubber component as defined above, the amount of which constitutes the total amount of rubber component in the final powder coating, the minimum rubber component content of the composition being at least twice the rubber component content of the final powder coating, said composition being heated at a temperature of at least the melting point of the thermosetting resin at least once during the course of the preliminary kneading, thereby to effect efficient dispersion of the components; (2) further kneading said composition together with at least one thermosetting resin having a melting point of up to 150° C. and other components which constitute the powder coating, thereby to effect intimate mixing of the components; and (3) pulverizing the resulting kneaded mass.
Claim 2
Dependent Claim
309 words
A process for preparing a chemically platable thermosetting powder coating comprising an intimate mixture of components in the following proportions: 100 parts by weight of at least one thermosetting resin having a melting point of up to 150° C., 1 to 30 parts by weight of a rubber component comprising at least 10% by weight of at least one rubber having ethylenic double bonds and polar groups in the molecule and up to 200 parts by weight of at least one inorganic filler, said powder coating having a melt viscosity of up to 10 5 centipoises at least once during the course of heat hardening, the lower limit of the amount of the inorganic filler in the powder coating corresponding to that amount of the inorganic filler used in step (1) of preliminary kneading as described below, which process comprises the steps of: (1) preliminarily kneading a composition comprising 3 to 50% by weight of at least one thermosetting resin having a melting point of up to 150° C., 5 to 60% by weight of at least one inorganic filler and up to 80% by weight of a rubber component as defined above, the amount of which constitutes the total amount of rubber component in the final powder coating, the minimum rubber component content of the composition being at least twice the rubber component content of the final powder coating, said composition being heated at a temperature of at least the melting point of the thermosetting resin at least once during the course of the preliminary kneading, thereby to effect efficient dispersion of the components; (2) further kneading said composition together with at least one thermosetting resin having a melting point of up to 150° C. and other components which constitute the powder coating, thereby to effect intimate mixing of the components; and (3) pulverizing the resulting kneaded mass.
Claim 3
Dependent Claim
70 words
A process according to claim 1, wherein said chemically platable thermosetting powder coating further comprises 0.006 to 1.2 parts by weight, per 100 parts by weight of the thermosetting resin, of a catalyst for chemical plating and wherein said composition to be preliminarily kneaded further comprises a catalyst for chemical plating, the amount of which is at least 50% by weight the amount of catalyst in the final powder coating.
Claim 4
Dependent Claim
19 words
A process according to claim 1 or 2, wherein said at least one thermosetting resin is an epoxy resin.
Claim 5
Dependent Claim
31 words
A process according to claim 3, wherein said epoxy resin is a member selected from the group consisting of bisphenolepichlorohydrin type epoxy resins, novolak type epoxy resins and alicyclic epoxy resins.
Claim 6
Dependent Claim
34 words
A process according to claim 1 or 2, wherein said at least one rubber having ethylenic double bonds and polar groups in the molecule has nitrile groups as the polar groups in the molecule.
Claim 7
Dependent Claim
26 words
A process according to claim 5, wherein said at least one rubber having ethylenic double bonds and polar groups in the molecule is an acrylonitrile-butadiene rubber.
Claim 8
Dependent Claim
61 words
A process according to claim 1 or 2, wherein said at least one rubber having ethylenic double bonds and polar groups in the molecule has at least 30% by weight, based on the total of monomer units, of conjugated double bond-containing monomer units and at least 15% by weight, based on the total of monomer units, of polar group-containing monomer units.
Claim 9
Dependent Claim
28 words
A process according to claim 1 or 2, wherein said rubber component consists of at least one rubber having ethylenic double bonds and polar groups in the molecule.
Claim 10
Dependent Claim
50 words
A process according to claim 1 or 2, wherein said rubber component consists of at least one rubber having ethylenic double bonds and polar groups in the molecule and a member selected from the group consisting of butadiene rubbers, styrene-butadiene rubbers, chloroprene rubbers, isoprene rubbers, natural rubber and combinations thereof.
Claim 11
Dependent Claim
32 words
A process according to claim 1 or 2, wherein said rubber component has a Mooney viscosity of up to 90 ML 1+4 as measured at 100° C. in accordance with ASTM D1646-63.
Claim 12
Dependent Claim
42 words
A process according to claim 2, wherein said catalyst for chemical plating is a member selected from the group consisting of metals belonging to Groups VIII and IB of Periodic Table, oxides, chlorides, nitrates and sulfates of said metal, and combinations thereof.
Claim 13
Dependent Claim
39 words
A process according to claim 11, wherein said catalyst for chemical plating is a member selected from the group consisting of palladium, gold, platinum, copper, palladium chloride, gold chloride, platinum chloride, copper oxide and their combinations with stannous chloride.
Claim 14
Dependent Claim
39 words
A process according to claim 1, wherein said composition is heated at a temperature in the range of from the melting point of the thermosetting resin to 200° C. at least once during the course of the preliminary kneading.
Claim 15
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 1 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 16
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 2 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 17
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 3 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 18
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 4 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 19
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 5 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 20
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 6 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 21
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 7 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 22
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 8 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 23
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 9 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 24
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 10 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 25
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 11 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 26
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 12 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
Claim 27
Dependent Claim
32 words
A chemically platable thermosetting powder coating produced by the process of claim 13 wherein the amount of the inorganic filler of the final powder coating is up to 100 parts by weight.
References Cited (Backward Citations)
US4131590A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-02-15 | 1985-08-17 | 1986-02-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-02-15 | 1989-08-17 | 1990-02-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-02-15 | 1993-08-17 | 1994-02-16 | $7700.00 | Window Closed / Lapsed |