Polysulfide rubbers suitable for hot application

Claim 2

A curable composition comprising a thiol terminated liquid polysulfide polymer, a curing amount of zinc oxide, and a sulfur containing compound selected from 2-mercaptobenzothiazole, zinc diloweralkyldithiocarbamate, and alkyl thiuram polysulfides of the formula: ##STR3## wherein x is from about 2 to about 6 and R' is alkyl of from 1 to about 10 carbon atoms either straight chain, branched chain or cyclic, or the R' moieties attached to the same nitrogen atom may be concatenated and taken together with said nitrogen atom form a heterocyclic ring, and at least one extrudability improver selected from copolymers of styrene with alkylenes, phenolic resins, coumarone-indene resins, polyalkylene polymers, factice, terpene resins, terpene resin esters, benzothiazyl disulfide and diphenyl guanidine.

Claim 3

A curable composition as defined in claim 1 comprising from about 2 to about 25 parts by weight zinc oxide per hundred parts by weight liquid polysulfide polymer, and from about 0.1 to about 50 parts by weight of sulfur containing compound per hundred parts by weight liquid polysulfide polymer.

Claim 4

A curable composition as defined in claim 2 comprising from about 3 to about 10 parts by weight zinc oxide per hundred parts liquid polysulfide polymer, and from 0.5 to about 10 parts by weight sulfur containing compound per hundred parts by weight liquid polysulfide polymer.

Claim 5

A curable composition as defined in claim 1 wherein the extrudability improver is a styrene-isoprene-styrene block copolymer.

Claim 6

A curable composition as defined in claim 1 wherein the extrudability improver is a mixture comprising benzothiazyl disulfide and diphenyl guanidine.

Claim 7

A curable composition as defined in claim 1 wherein the sulfur containing compound is 2-mercaptobenzothiazole.

Claim 8

A curable composition as defined in claim 1 wherein the sulfur containing compound is a zinc diloweralkyldithiocarbamate.

Claim 9

A curable composition as defined in claim 7 wherein the zinc diloweralkyldithiocarbamate is zinc dimethyldithiocarbamate.

Claim 10

A curable composition as defined in claim 1 wherein the sulfur containing compound has the formula: ##STR4## wherein x is from about 2 to about 6 and R' is alkyl of from 1 to about 10 carbon atoms either straight chain, branched chain or cyclic, or the R' moieties attached to the same nitrogen atom may be concatenated and taken together with said nitrogen atom form a heterocyclic ring.

Claim 11

A curable composition as defined in claim 9 wherein R' is methyl and x is 2.

Claim 12

A curable composition as defined in claim 9 wherein R' is ethyl and x is 2.

Claim 13

A curable composition as defined in claim 9 where the R' pairs bonded to a common nitrogen atom are concatenated to form pentamethylene moieties and x is 6.

Claim 14

A cured rubber composition which is capable of being extruded after heating at a temperature of about 220° F. to about 390° F. with substantial recovery of its pre-extrusion physical properties upon cooling, said cured rubber composition comprising a thiol terminated liquid polysulfide polymer cured with zinc oxide and a sulfur containing compound selected from 2-mercaptobenzothiazole, zinc diloweralkyldithiocarbamate, and alkyl thiuram polysulfides of the formula: ##STR5## wherein x is from about 2 to about 6 and R' is alkyl of from 1 to about 10 carbon atoms either straight chain, branched chain or cyclic, or the R' moieties attached to the same nitrogen atom may be concatenated and taken together with said nitrogen atom form a heterocyclic ring, and at least one extrudability improver selected from copolymers of styrene with alkylenes, phenolic resins, coumarone-indene resins, polyalkylene polymers, factice, terpene resins, terpene resin esters, benzothiazyl disulfide and diphenyl guanidine.

Claim 15

A cured rubber composition which is capable of being extruded after heating at a temperature of about 220° F. to about 390° F. with substantial recovery of its pre-extrusion physical properties upon cooling, said cured rubber composition comprising a thiol terminated liquid polysulfide polymer cured with zinc oxide and a sulfur containing compound selected from 2-mercaptobenzothiazole, zinc diloweralkyldithiocarbamate, and alkyl thiuram polysulfides of the formula: ##STR5## wherein x is from about 2 to about 6 and R' is alkyl of from 1 to about 10 carbon atoms either straight chain, branched chain or cyclic, or the R' moieties attached to the same nitrogen atom may be concatenated and taken together with said nitrogen atom form a heterocyclic ring, and at least one extrudability improver selected from copolymers of styrene with alkylenes, phenolic resins, coumarone-indene resins, polyalkylene polymers, factice, terpene resins, terpene resin esters, benzothiazyl disulfide and diphenyl guanidine.

Claim 16

A cured rubber composition as defined in claim 13 wherein the extrudability improver is a styrene-isoprenestyrene block copolymer.

Claim 17

A cured rubber composition as defined in claim 13 wherein the extrudability improver is a mixture of benzothiazyl disulfide and diphenyl guanidine.

Claim 18

A cured rubber composition as defined in claim 13 wherein the sulfur containing compound is 2-mercaptothiazole.

Claim 19

A cured composition as defined in claim 13 wherein the sulfur containing compound is a zinc diloweralkyldithiocarbamate.

Claim 20

A cured rubber composition as defined in claim 17 wherein the diloweralkyldithiocarbamate is dimethyldithiocarbamate.

Claim 21

A cured rubber composition as defined in claim 13 wherein the sulfur containing compound has the formula: ##STR6## wherein x is from about 2 to about 6 and R' is alkyl of from 1 to about 10 carbon atoms either straight chain, branched chain or cyclic, or the R' moieties attached to the same nitrogen atom may be concatenated and taken together with said nitrogen atom form a heterocyclic ring.

Claim 22

A cured rubber composition as defined in claim 19 wherein R' is methyl and x is 2.

Claim 23

A cured rubber composition as defined in claim 19 wherein R' is ethyl and x is 2.

Claim 24

A cured rubber composition as defined in claim 19 wherein the R' pairs bonded to a common nitrogen atom are concatenated to form a pentamethylene moiety and x is 6.