Method for removing borosilicate and boron rich oxides from a silicon body prior to doping silicon bodies with a SiB6 solid source
Assignee: International Business Machines Corp
•
Filing: 1980-12-03
•
Granted: 1982-02-02
•
Expires: 2000-12-03
Abstract
Abstract A method for doping silicon bodies by the diffusion of boron into the bodies is described. The method is an improvement of processes where the silicon bodies are exposed in a first heating process to a gas mixture containing a predetermined boron quantity and boron and oxygen in a predetermined quantitative ratio and a second heating process is used to drive the boron into the silicon. In the method, a borosilicate glass layer and a boron-rich silicon dioxide layer are removed by first immersing the silicon body in hydrofluoric acid diluted with water and subsequently in an aqueous sulfuric acid/potassium permanganate solution.
Inventors
- 👤 Marian Briska
- 👤 Gert Metzger
- 👤 Klaus P. Thiel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 18:09
CPC Classifications
C; C30; C30B; C30B31/00; C30B31/02; H; H10; H10P; H10P32/00; H10P32/10; H10P32/12; H10P32/17; H10P32/171; H10P50/00; H10P50/20; H10P50/28; H10P50/282; H10P50/283
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
128 words
In a method for doping silicon bodies where the silicon bodies are exposed in a first heating process to a gas mixture containing a predetermined boron quantity and boron and oxygen in a predetermined quantitative ratio to form a borosilicate glass layer, a boron-rich silicon dioxide layer and a SiB 6 layer, and where in a second heating process at least part of the boron is driven into the silicon, and that prior to the second heating process the borosilicate glass is completely stripped off without the SiB 6 layer being substantially affected, the improvement comprising stripping the borosilicate glass layer and the boron-rich silicon dioxide layer by first immersing the silicon bodies in hydrofluoric acid diluted with water and subsequently in an aqueous sulfuric acid/potassium permanganate solution.
Claim 2
Dependent Claim
128 words
In a method for doping silicon bodies where the silicon bodies are exposed in a first heating process to a gas mixture containing a predetermined boron quantity and boron and oxygen in a predetermined quantitative ratio to form a borosilicate glass layer, a boron-rich silicon dioxide layer and a SiB 6 layer, and where in a second heating process at least part of the boron is driven into the silicon, and that prior to the second heating process the borosilicate glass is completely stripped off without the SiB 6 layer being substantially affected, the improvement comprising stripping the borosilicate glass layer and the boron-rich silicon dioxide layer by first immersing the silicon bodies in hydrofluoric acid diluted with water and subsequently in an aqueous sulfuric acid/potassium permanganate solution.
Claim 3
Dependent Claim
43 words
The method of claim 1 wherein the aqueous sulfuric acid/potassium permanganate solution is obtained by dissolving from about 0.5 to about 5 gm/l of potassium permanganate in aqueous sulfuric acid having from about 5 to about 20 percent by weight of sulfuric acid.
Claim 4
Dependent Claim
28 words
The method of claim 1 wherein the aqueous sulfuric acid/potassium permanganate solution is obtained by dissolving 1.6 g/l potassium permanganate in a 10% by weight aqueous sulfuric acid.
Claim 5
Independent Claim
46 words
The method as claimed in claims 1, 2 or 3, wherein the silicon bodies are immersed for approximately 10 to 30 seconds in hydrofluoric acid diluted with water at a ratio of 1:10 and for 1 to 3 minutes in the aqueous sulfuric acid/potassium permanganate solution.
Claim 6
Independent Claim
33 words
The method as claimed in claims 1 or 4, wherein the stripping of the borosilicate glass layer and of the boron-rich silicon dioxide layer from the silicon bodies is performed at ambient temperature.
Claim 7
Dependent Claim
45 words
The method as claimed in claim 1, wherein the O 2 :boron ratio and the boron quantity added per time unit to the gas mixture are determined in such a manner that borosilicate glass is obtained which is stripped in diluted hydrofluoric acid only incompletely.
Claim 8
Dependent Claim
58 words
The method as claimed in claim 1, wherein a partially masked surface of the silicon bodies is exposed in a first heating process to a carrier gas flow to which is admixed during coating BBr 3 and an oxygen quantity adapted thereto, and that an O 2 :BBr 3 molar ratio between about 20 and 65 is used.
Claim 9
Independent Claim
25 words
The method as claimed in claims 1 and 7 wherein the first heating process is at a temperature of between about 850° and 950° C.
Claim 10
Dependent Claim
36 words
The method as claimed in claim 1, wherein after the first heating process and the stripping of the borosilicate glass the boron is driven into the silicon in an oxidizing atmosphere during a second heating process.
Claim 11
Independent Claim
22 words
The method as claimed in claims 1 and 9, wherein the second heating process is at a temperature of about 925° C.
Claim 12
Independent Claim
24 words
The method as claimed in claims 1 and 10, wherein base zones of bipolar transistors in highly integrated circuits are made by the method.
References Cited (Backward Citations)
US2847287A
Cited
US3061495A
Cited
US3669775A
Cited
US3751314A
Cited
US3784424A
Cited
US4249970A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-02-01 | 1985-08-03 | 1986-02-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-02-01 | 1989-08-03 | 1990-02-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-02-01 | 1993-08-03 | 1994-02-02 | $7700.00 | Window Closed / Lapsed |