Molybdenum substrate thick film circuit
Assignee: Lockheed Martin Corp
•
Filing: 1979-12-17
•
Granted: 1982-02-02
•
Expires: 1999-12-17
Abstract
Abstract An improved multilayered circuit is disclosed comprising a molybdenum substrate with alternating layers of dielectric and conducting thick film materials deposited thereon. The molybdenum substrate has the advantages of being its own chassis, having a coefficient of thermal expansion that is well matched to the thick film materials and component ceramic chip carriers, and having a high thermal conductivity so as to act as its own heat sink.
Inventors
- 👤 Norman S. Barnes
- 👤 Rodman A. Mogle
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 15:40
CPC Classifications
H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/05; H05K1/053; H10; H10W; H10W70/00; H10W70/01; H10W70/05; H10W70/098; H10W70/60; H10W70/611; H10W70/67; H10W70/68; H10W70/685; H10W70/6875; H10W90/00; H05K1/09; H05K1/092; H05K3/00; H05K3/46; H05K3/4644; H10W70/62; H10W70/63; H10W90/701; H10W90/751; H10W90/754; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49128; Y10T29/4913; Y10T29/49144; Y10T29/49155
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
162 words
A method of making a large area multilayer printed circuit structure comprising: a. providing a substrate material made of molybdenum; b. screen printing a first layer of dielectric material and allowing said dielectric to dry; c. firing said first dielectric layer; d. repeating steps b and c until the desired number of dielectric layers have been printed, said dielectric layers having an uppermost dielectric layer with a top surface; e. screen printing a first conductor circuit over the top surface of the uppermost dielectric layer and allowing said first conductor to dry; f. firing said first conductor, said first conductor having a top surface; g. screen printing a second layer of dielectric material over the top surface of said first conductor and the uppermost layer of said first dielectric layers and allowing said second dielectric layer to dry; h. firing said second dielectric; and i. repeating steps e, f, g and h until the desired number of dielectric-conductor layers have been printed.
Claim 2
Independent Claim
162 words
A method of making a large area multilayer printed circuit structure comprising: a. providing a substrate material made of molybdenum; b. screen printing a first layer of dielectric material and allowing said dielectric to dry; c. firing said first dielectric layer; d. repeating steps b and c until the desired number of dielectric layers have been printed, said dielectric layers having an uppermost dielectric layer with a top surface; e. screen printing a first conductor circuit over the top surface of the uppermost dielectric layer and allowing said first conductor to dry; f. firing said first conductor, said first conductor having a top surface; g. screen printing a second layer of dielectric material over the top surface of said first conductor and the uppermost layer of said first dielectric layers and allowing said second dielectric layer to dry; h. firing said second dielectric; and i. repeating steps e, f, g and h until the desired number of dielectric-conductor layers have been printed.
Claim 3
Dependent Claim
72 words
A method of making a multilayer structure as set forth in claim 1, wherein said repeated steps of screen printing the dielectric involves first printing two layers of dielectric with a patterned screen which patterns many voids in the dielectric so as to create many vias therein, screen printing to fill the vias with conductor material, and then screen printing layers of dielectric before screen printing of the printed circuit conductor layer.
Claim 4
Dependent Claim
36 words
The method of fabricating a multilayer structure as set forth in claim 1, wherein components are bonded or soldered to the top surface of the multilayer structure and thus interconnected to at least one exposed conductor.
Claim 5
Dependent Claim
28 words
The method of fabricating a multilayer structure as set forth in claim 1, where said drying steps include exposure to air at 125° C. for approximately 15 minutes.
Claim 6
Dependent Claim
105 words
The method of fabricating a multilayer structure as set forth in claim 1, where said firing of each of said dielectric layers includes: (a) utilizing a continuous belt furnace consisting of a plurality of temperature zones; (b) burning out an organic binder in said dielectric at temperatures from 0° to 400° C. in a nitrogen atmosphere of from 0 to 600 parts per million of oxygen; (c) firing said dielectric at a peak temperature of from 850° to 925° for 4 to 10 minutes during a total furnace cycle time of 30-60 minutes in nitrogen atmosphere of less than 15 parts per million of oxygen.
Claim 7
Dependent Claim
102 words
The method of fabricating a multilayer structure as set forth in claim 1, where said firing of said conductor layer includes: (a) utilizing a continuous belt furnace consisting of a plurality of temperature zones; (b) burning out an organic binder in said conductor at temperatures from 0° to 400° C. in a nitrogen atmosphere of less than 15 parts per million of oxygen; (c) firing said conductor at a peak temperature of from 850°-925° C. for 4 to 10 minutes during a total furnace cycle time of 30-60 minutes in a nitrogen atmosphere of less than 15 parts per million of oxygen.
References Cited (Backward Citations)
GB776970A
Cited
US3838204A
Cited
US3531579A
Cited
US3852877A
Cited
US3770529A
Cited
US3689684A
Cited
US3798762A
Cited
US3922777A
Cited
GB1441526A
Cited
US3912849A
Cited
US3999004A
Cited
US4130855A
Cited
US4109377A
Cited
US4107837A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-02-01 | 1985-08-03 | 1986-02-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-02-01 | 1989-08-03 | 1990-02-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-02-01 | 1993-08-03 | 1994-02-02 | $7700.00 | Window Closed / Lapsed |