High yield silicon carbide pre-polymers

Claim 1

A method of preparing a polysilane having the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} (I) in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom or a hydrogen atom such that the polysilane contains from 0.3 to 2.1 weight percent of hydrogen attached to silicon, based on the weight of the polysilane, which method consists of (A) reducing a polysilane having the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} (II) in which there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom, a chlorine atom or a bromine atom such that the polysilane contains from 10-43 weight percent, based on the weight of the polysilane, of hydrolyzable chlorine or 21-62 weight percent based on the weight of the polysilane of hydrolyzable bromine, with at least a stoichiometric quantity, based on the halogen present, of a reducing agent, under anhydrous conditions, at a temperature of from 0° to 120° C. for a period of from 4 to 48 hours., in a suitable solvent, and (B) thereafter recovering the polysilane (I).

Claim 2

A method of preparing a polysilane having the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} (I) in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom or a hydrogen atom such that the polysilane contains from 0.3 to 2.1 weight percent of hydrogen attached to silicon, based on the weight of the polysilane, which method consists of (A) reducing a polysilane having the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} (II) in which there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom, a chlorine atom or a bromine atom such that the polysilane contains from 10-43 weight percent, based on the weight of the polysilane, of hydrolyzable chlorine or 21-62 weight percent based on the weight of the polysilane of hydrolyzable bromine, with at least a stoichiometric quantity, based on the halogen present, of a reducing agent, under anhydrous conditions, at a temperature of from 0° to 120° C. for a period of from 4 to 48 hours., in a suitable solvent, and (B) thereafter recovering the polysilane (I).

Claim 5

A method of preparing silicon carbide ceramic materials which consists of heating a polysilane having the average formula {(CH.sub.3).sub.2 }{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom or a hydrogen atom such that the polysilane contains from 0.3 to 2.1 weight percent of hydrogen attached to silicon, based on the weight of the polysilane, in an inert atmosphere or in a vacuum to an elevated temperature in the range of 700° C. to 1600° C. until the polysilane is converted to silicon carbide.

Claim 6

A method of preparing silicon carbide ceramic materials which consists of heating a polysilane having the average formula {(CH.sub.3).sub.2 }{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom or a hydrogen atom such that the polysilane contains from 0.3 to 2.1 weight percent of hydrogen attached to silicon, based on the weight of the polysilane, in an inert atmosphere or in a vacuum to an elevated temperature in the range of 700° C. to 1600° C. until the polysilane is converted to silicon carbide.

Claim 8

A method of preparing a silicon carbide-containing ceramic article which consists of (A) forming an article of the desired shape from a polysilane having the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom or a hydrogen atom such that the polysilane contains from 0.3 to 2.1 weight percent of hydrogen attached to silicon, based on the weight of the polysilane, and (B) heating the article formed in (A) in an inert atmosphere or in a vacuum to an elevated temperature in the range of 700° C. to 1600° C. until the polysilane is converted to a silicon carbide-containing ceramic article.

Claim 9

A method of preparing a silicon carbide-containing ceramic article which consists of (A) forming an article of the desired shape from a polysilane having the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom or a hydrogen atom such that the polysilane contains from 0.3 to 2.1 weight percent of hydrogen attached to silicon, based on the weight of the polysilane, and (B) heating the article formed in (A) in an inert atmosphere or in a vacuum to an elevated temperature in the range of 700° C. to 1600° C. until the polysilane is converted to a silicon carbide-containing ceramic article.

Claim 11

A method of preparing a filled silicon carbide-containing ceramic article which consists of (A) mixing a polysilane with at least one conventional ceramic filler which polysilane has the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom or a hydrogen atom such that the polysilane contains from 0.3 to 2.1 weight percent of hydrogen attached to silicon, based on the weight of the polysilane; (B) forming an article of the desired shape from the mixture of polysilane and fillers and, (C) heating the article formed in (B) in an inert atmosphere or in a vacuum to an elevated temperature in the range of 700° C. to 1600° C. until the polysilane is converted to a silicon carbide-containing ceramic article.

Claim 12

A method of preparing a filled silicon carbide-containing ceramic article which consists of (A) mixing a polysilane with at least one conventional ceramic filler which polysilane has the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom or a hydrogen atom such that the polysilane contains from 0.3 to 2.1 weight percent of hydrogen attached to silicon, based on the weight of the polysilane; (B) forming an article of the desired shape from the mixture of polysilane and fillers and, (C) heating the article formed in (B) in an inert atmosphere or in a vacuum to an elevated temperature in the range of 700° C. to 1600° C. until the polysilane is converted to a silicon carbide-containing ceramic article.

Claim 14

A method of preparing an article coated with ceramic which consists of (A) mixing a polysilane with at least one conventional ceramic filler which polysilane has the average unit formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom or a hydrogen atom such that the polysilane contains from 0.3 to 2.1 weight percent of hydrogen attached to silicon, based on the weight of the polysilane, (B) coating a substrate with the mixture of polysilane and filler and, (C) heating the coated substrate in an inert atmosphere or in a vacuum to an elevated temperature in the range of 700° C. to 1600° C. until the coating is converted to a silicon carbide ceramic, whereby a silicon carbide-containing ceramic coated article is obtained.

Claim 15

A method of preparing an article coated with ceramic which consists of (A) mixing a polysilane with at least one conventional ceramic filler which polysilane has the average unit formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═ units and 40 to 100 mole percent CH 3 Si.tbd. units, wherein the remaining bonds on silicon are attached to either another silicon atom or a hydrogen atom such that the polysilane contains from 0.3 to 2.1 weight percent of hydrogen attached to silicon, based on the weight of the polysilane, (B) coating a substrate with the mixture of polysilane and filler and, (C) heating the coated substrate in an inert atmosphere or in a vacuum to an elevated temperature in the range of 700° C. to 1600° C. until the coating is converted to a silicon carbide ceramic, whereby a silicon carbide-containing ceramic coated article is obtained.