Hot melt adhesive compositions
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1980-10-14
•
Granted: 1982-01-12
•
Expires: 2000-10-14
Abstract
Abstract This invention relates to hot melt adhesive compositions which includes a neutralized sulfonated polystyrene resin wherein the neutralized sulfonated polystyrene resin has about 5 to about 250 meq. of neutralized sulfonate groups per 100 grams of the neutralized sulfonated polystyrene resin and about 25 to about 250 parts by weight of a hydrocarbon resin of a petroleum or coal tar distillate, aliphatic dienes and mono and diolefins, cyclic olefins of 5 or 6 carbon atoms and hydrogenated poly cyclics per 100 parts by weight of the neutralized sulfonated polystyrene resin. Additionally, an unsaturated hydrocarbon polymer such as polyisoprene and polybutadiene can be incorporated into the adhesive compositions.
Inventors
- 👤 Pawan K. Agarwal
- 👤 Henry S. Makowski, deceased
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 10:29
CPC Classifications
C; C09; C09J; C09J109/00; C09J125/00; C09J125/18; C08; C08L; C08L2666/00; C08L2666/02; C08L2666/04
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
79 words
A hot melt adhesive composition which comprises: (a) a highly unsaturated polybutadiene or polyisoprene hydrocarbon rubber; (b) a neutralized sulfonated polystyrene resin said neutralized sulfonated polystyrene having about 80 to 250 meq. of neutralized sulfonated groups per 100 grams of said neutralized sulfonated polystyrene resin; and (c) about 25 to about 200 parts by weight of a hydrocarbon tackifying resin based on a petroleum or coal tar distillate per 100 parts by weight of said neutralized sulfonated polysytrene resin.
Claim 2
Dependent Claim
79 words
A hot melt adhesive composition which comprises: (a) a highly unsaturated polybutadiene or polyisoprene hydrocarbon rubber; (b) a neutralized sulfonated polystyrene resin said neutralized sulfonated polystyrene having about 80 to 250 meq. of neutralized sulfonated groups per 100 grams of said neutralized sulfonated polystyrene resin; and (c) about 25 to about 200 parts by weight of a hydrocarbon tackifying resin based on a petroleum or coal tar distillate per 100 parts by weight of said neutralized sulfonated polysytrene resin.
Claim 3
Dependent Claim
44 words
A hot melt adhesive composition according to claim 1, wherein said neutralized sulfonate groups are neutralized with a counterion selected from the group consisting of amines ammonium, aluminum, antimony, iron, lead and Groups IA, IIA, IB and IIB of the Periodic Table of Elements.
Claim 4
Dependent Claim
19 words
A hot melt adhesive composition according to claim 1, wherein said neutralized sulfonate groups are neutralized with zinc ions.
Claim 5
Dependent Claim
81 words
A hot melt adhesive according to claim 1 further including about 3 to about 75 parts by weight of an ionic preferential plasticizer per 100 parts by weight of said neutralized sulfonated polystyrene resin, wherein said preferential plasticizer is selected from the group consisting of carboxylic acids having about 8 to about 22 carbon atoms, metallic salts of said carboxylic acids, amides having an aliphatic group of about 8 to about 22 carbon atoms, amines, ureas and thioureas and mixtures thereof.
Claim 6
Dependent Claim
20 words
A hot melt adhesive according to claim 4, wherein said preferential plasticizer is said metallic salt of said carboxylic acid.
Claim 7
Dependent Claim
20 words
A hot melt adhesive composition according to claim 5, wherein said metallic salt of said carboxylic acid is zinc stearate.
Claim 8
Dependent Claim
82 words
A hot melt adhesive composition according to claim 1, further including about 5 to about 800 parts by weight of a filler per 100 parts by weight of said neutralized sulfonated polystyrene resin, said filler being selected from the group consisting of calcium carbonates, silicas, carbon blacks, clays and talcs and mixtures thereof and/or less than about 100 parts by weight of an oil having less than 2 wt. % polars per 100 parts by weight of said neutralized sulfonated polystyrene resin.
Claim 9
Dependent Claim
34 words
A hot melt adhesive composition according to claims 1,2 or 7 wherein said hydrocarbon resin has about 5 to about 6 carbon atoms and consists of aliphatic dienes, mono- and di-olefins and cyclic olefins.
Claim 10
Dependent Claim
43 words
A hot melt adhesive composition according to claim 1 further including from about 1 to about 100 parts by weight of an oil per 100 parts by weight of said highly unsaturated hydrocarbon resin, said oil being an aromatic, naphthenic or paraffinic basestock.
Claim 11
Dependent Claim
13 words
An adhesive composition according to claim 1, further including an unsaturated hydrocarbon resin.
References Cited (Backward Citations)
US3932328A
Cited
US3932341A
Cited
US4169822A
Cited
US3917551A
Cited
US4158653A
Cited
US4137203A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-11 | 1985-07-13 | 1986-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-11 | 1989-07-13 | 1990-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-11 | 1993-07-13 | 1994-01-12 | $7700.00 | Window Closed / Lapsed |