Novel resin compositions based on polyphenylene ether
Assignee: Sumitomo Chemical Co Ltd
•
Filing: 1981-01-13
•
Granted: 1982-01-05
•
Expires: 2001-01-13
Abstract
Abstract A resin composition based on a polyphenylene ether comprising 99 to 1 part by weight of a polyphenylene ether copolymer derived from 99.5 to 85 mole-% of 2,6-dimethylphenol and 0.5 to 15 mole-% of 3-methyl-6-tert-butylphenol and 1 to 99 parts by weight of a styrene polymer (making up 100 parts by weight in total); and said resin composition further containing 0.1 to 100 parts by weight of a rubber-like polymer for 100 parts by weight of the said resin composition. These resin compositions have excellent mechanical strength, heat resistance, and moldability and are suitable as molding resin materials in practical use fields.
Inventors
- 👤 Katsuji Ueno
- 👤 Haruo Inoue
- 👤 Akihiro Furuta
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 19:37
CPC Classifications
C; C08; C08G; C08G65/00; C08G65/34; C08G65/38; C08G65/44; C08L; C08L71/00; C08L71/08; C08L71/10; C08L71/12; C08L71/123
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
61 words
A resin composition based on a polyphenylene ether comprising 99 to 1 part by weight of a polyphenylene ether copolymer derived from 99.5 to 85 mole-% of 2,6-dimethylphenol and 0.5 to 15 mole-% of 3-methyl-6-tert-butylphenol and 1 to 99 parts by weight of a styrene polymer, said ether copolymer and said styrene copolymer (making up 100 parts by weight in total).
Claim 2
Dependent Claim
61 words
A resin composition based on a polyphenylene ether comprising 99 to 1 part by weight of a polyphenylene ether copolymer derived from 99.5 to 85 mole-% of 2,6-dimethylphenol and 0.5 to 15 mole-% of 3-methyl-6-tert-butylphenol and 1 to 99 parts by weight of a styrene polymer, said ether copolymer and said styrene copolymer (making up 100 parts by weight in total).
Claim 3
Dependent Claim
33 words
A resin composition based on a polyphenylene ether according to claim 1, wherein the polyphenylene ether copolymer is derived from 99 to 90 mole-% of 2,6-dimethylphenol and 1 to 10 mole-% of 3-methyl-6-tert-butylphenol.
Claim 4
Dependent Claim
36 words
A resin composition based on a polyphenylene ether according to claim 1, wherein the polyphenylene ether copolymer is 95 to 5 parts by weight and the styrene polymer is 5 to b 95 parts by weight.
Claim 5
Dependent Claim
27 words
A resin composition based on a polyphenylene ether according to claim 1, wherein the styrene polymer is at least one member selected from polystyrenes and styrene-based copolymers.
Claim 6
Dependent Claim
32 words
A resin composition based on a polyphenylene ether according to claim 4, wherein the polystyrenes are homopolymers of styrene, α-methylstyrene vinyltoluene and chlorostyrene and copolymers of two or more of these compounds.
Claim 7
Dependent Claim
44 words
A resin composition based on a polyphenylene ether according to claim 4, wherein the styrene-based copolymers are impact-resistant polystyrenes, styrene-acrylonitrile copolymers, styrene-butadiene block copolymers, styrene-butadiene random copolymers, styrene-methyl methacrylate copolymers, styrene-butadiene-acrylonitrile copolymers, styrene-maleic anhydride copolymers, rubber-modified styrene-maleic anhydride copolymers, ethylene-styrene copolymers, and ethylene-propylene-butadiene-styrene copolymers.
Claim 8
Dependent Claim
79 words
A resin composition based on a polyphenylene ether comprising 99 to 1 part by weight of a polyphenylene ether copolymer derived from 99.5 to 85 mole-% of 2,6-dimethylphenol and 0.5 to 15 mole-% of 3-methyl-6-tert-butylphenol, 1 to 99 parts by weight of a styrene-based polymer, the total of said two polymers being 100 parts by weight, and 0.1 to 100 parts by weight of a rubber-like polymer for 100 parts by weight of the total of said two polymers.
Claim 9
Dependent Claim
79 words
A resin composition based on a polyphenylene ether comprising 99 to 1 part by weight of a polyphenylene ether copolymer derived from 99.5 to 85 mole-% of 2,6-dimethylphenol and 0.5 to 15 mole-% of 3-methyl-6-tert-butylphenol, 1 to 99 parts by weight of a styrene-based polymer, the total of said two polymers being 100 parts by weight, and 0.1 to 100 parts by weight of a rubber-like polymer for 100 parts by weight of the total of said two polymers.
Claim 10
Dependent Claim
33 words
A resin composition based on a polyphenylene ether according to claim 7, wherein the polyphenylene ether copolymer is derived from 99 to 90 mole-% of 2,6-dimethylphenol and 1 to 10 mole-% of 3-methyl-6-tert-butylphenol.
Claim 11
Dependent Claim
35 words
A resin composition based on a polyphenylene ether according to claim 7, wherein the polyphenylene ether copolymer is 95 to 5 parts by weight and the styrene-based polymer is 5 to 95 parts by weight.
Claim 12
Dependent Claim
27 words
A resin composition based on a polyphenylene ether according to claim 7, wherein the styrene-based polymer is at least one member selected from polystyrenes and styrene-based copolymers.
Claim 13
Dependent Claim
32 words
A resin composition based on a polyphenylene ether according to claim 10, wherein the polystyrenes are homopolymers of styrene, α-methylstyrene, vinyltoluene and chlorostyrene and copolymers of two or more of these compounds.
Claim 14
Dependent Claim
44 words
A resin composition based on a polyphenylene ether according to claim 10, wherein the styrene-based copolymers are impact-resistant polystyrenes, styrene-acrylonitrile copolymers, styrene-butadiene block copolymers, styrene-butadiene random copolymers, styrene-methyl methacrylate copolymers, styrene-butadiene-acrylonitrile copolymers, styrene-maleic anhydride copolymers, rubber-modified styrene-maleic anhydride copolymers, ethylene-styrene copolymers, and ethylene-propylene-butadiene-styrene copolymers.
Claim 15
Dependent Claim
35 words
A resin composition based on a polyphenylene ether according to claim 7, wherein the rubber-like polymer is a polybutadiene, butadiene-styrene copolymer, ethylene-propylene copolymer, ethylene-propylene-conjugated diene copolymer, polyisoprene, polyisobutylane, polychloroprene, acrylic ester copolymer, or high-styrene rubber.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-04 | 1985-07-06 | 1986-01-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-04 | 1989-07-06 | 1990-01-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-04 | 1993-07-06 | 1994-01-05 | $7700.00 | Window Closed / Lapsed |