Process of producing composite powder coated with noble metal
Assignee: Nihon Kogyo KK
•
Filing: 1979-10-11
•
Granted: 1982-01-05
•
Expires: 1999-10-11
Abstract
Abstract Composite powder coated with a noble metal is produced by adding a powder of a metal or alloy baser than the noble metal to a powder of a metallic sulfide, carbon, activated charcoal, metallic carbide, or metallic oxide, and then adding to the resulting mixture a solution containing the noble metal with stirring. The particles of the composite powder are coated with the noble metal that results from a cementation reaction.
Inventors
- 👤 Yoshio Kawasumi
- 👤 Mitsuo Takahashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:47
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; B; B22; B22F; B22F1/00; B22F1/18; B22F9/00; B22F9/16; B22F9/18; B22F9/24; C04B20/00; C04B20/10; C04B20/1055; C04B35/00; C04B35/515; C04B35/52; C04B35/547; C04B41/45; C04B41/50; C04B41/51; C04B41/5105; C04B41/80; C04B41/81; C04B41/85; C04B41/88; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1633; C23C18/1635; C23C18/18; C23C18/1803; C23C18/1824; C23C18/1837; C23C18/1844; C23C18/54; H; H01; H01H; H01H1/00; H01H1/02; H01H1/021; H01H1/027; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
75 words
A process of producing a composite powder coated with a noble metal, which comprises adding a powder of a metal or alloy baser than the noble metal to a starting powder of a metallic sulfide, carbon, activated charcoal, metallic carbide, or metallic oxide, and then adding to the resulting mixture a solution containing said noble metal with stirring, whereby said starting powder particles are coated with said noble metal that results from a cementation reaction.
Claim 2
Dependent Claim
75 words
A process of producing a composite powder coated with a noble metal, which comprises adding a powder of a metal or alloy baser than the noble metal to a starting powder of a metallic sulfide, carbon, activated charcoal, metallic carbide, or metallic oxide, and then adding to the resulting mixture a solution containing said noble metal with stirring, whereby said starting powder particles are coated with said noble metal that results from a cementation reaction.
Claim 3
Dependent Claim
19 words
A process according to claim 1 wherein the starting powder has a particle size between about 20μ and 2000μ.
Claim 4
Dependent Claim
33 words
A process according to claim 1 wherein the solution containing noble metal is a solution of nitrates, hydrochlorides, sulfates, ammonium salt, organic acid salts or cyanates of noble metal and the combination thereof.
Claim 5
Dependent Claim
13 words
A process according to claim 3 wherein the solution is an aqueous solution.
Claim 6
Dependent Claim
24 words
A process according to claim 1 wherein the solution containing noble metal has a noble metal concentration of about 0.5 g/l to saturation value.
Claim 7
Dependent Claim
34 words
A process according to claim 1 wherein the metal or alloy powder baser than noble metal is selected from a group of powders of tin, zinc, iron, copper, aluminum, magnesium, or an alloy thereof.
Claim 8
Dependent Claim
52 words
A process according to claim 1 wherein copper is selected as the metal baser than noble metal, and copper ions in the solution after the cementation reaction for the noble metal coating is recovered as copper powder by the cementation reaction with iron powder and the copper powder thus obtained is reused.
Claim 9
Dependent Claim
44 words
A process according to claim 1 wherein the addition of the solution containing noble metal ion is so effected that the funicular region is reached in about 20 seconds to 10 minutes and then the slurry region is reached in 5 to 10 seconds.
Claim 10
Dependent Claim
18 words
A process according to claim 1 wherein when the starting powder is subjected to preliminary granulation and sizing.
Claim 11
Dependent Claim
85 words
A process according to claim 9 wherein said preliminary granulation and sizing is effected by charging the starting powder into the grinding-granulating mixer together with a binder prepared by diluting a resol and/or novolak type phenol resin with alcohol, to grind and granulate the powder, evaporating the alcohol, sieving the resultant granules, returning into the mixer to coarse and fine particles outside the intended range with only addition of alcohol and repeating said procedure until all the starting powder is sized to the intended range.
Claim 12
Dependent Claim
107 words
A process of producing a composite powder coated with a noble metal comprising the steps of: providing preliminarily granulated and sized starting powder of a metallic sulfide, carbon, activated charcoal, metallic carbide or metallic oxide, mixing the starting powder with powder of a metal or alloy baser than the noble metal, and adding to the mixture produced solution containing said noble metal in such manner that the funicular (II) region is reached in about 20 seconds to 10 minutes and then the slurry region is reached in 5 to 10 seconds, whereby the starting powder particles are coated with noble metal that results from a cementation reaction.
Claim 13
Dependent Claim
107 words
A process of producing a composite powder coated with a noble metal comprising the steps of: providing preliminarily granulated and sized starting powder of a metallic sulfide, carbon, activated charcoal, metallic carbide or metallic oxide, mixing the starting powder with powder of a metal or alloy baser than the noble metal, and adding to the mixture produced solution containing said noble metal in such manner that the funicular (II) region is reached in about 20 seconds to 10 minutes and then the slurry region is reached in 5 to 10 seconds, whereby the starting powder particles are coated with noble metal that results from a cementation reaction.
References Cited (Backward Citations)
US3956528A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-04 | 1985-07-06 | 1986-01-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-04 | 1989-07-06 | 1990-01-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-04 | 1993-07-06 | 1994-01-05 | $7700.00 | Window Closed / Lapsed |