Method of coloring and molding a shaped thermoplastic resin article
Assignee: Plastic Molders Supply Co Inc
•
Filing: 1979-09-10
•
Granted: 1982-01-05
•
Expires: 1999-09-10
Abstract
Abstract Fatty acid amide coated pigments are obtained and used to formulate with uncolored thermoplastic materials. The colors of the pigments are fully developed, and extremely high pigment loadings are obtained. The coated pigments are formed by admixing the pigment with melted fatty acid amide; solidifying the material by cooling it; grinding the material; and separating out the fines. The coated pigment's particles are compounded with thermoplastic materials by low shear means, such as, injection molding. An improved form of the coated pigments can be obtained by admixing the melted fatty acid amide, and the pigment; extruding the admixture to form a creamy mass; solidifying and forming the creamy mass by passing it through cold and forming rollers; grinding the resultant wafer-like material; and separating out the fines.
Inventors
- 👤 Edward T. Pollard
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 11:14
CPC Classifications
C; C09; C09B; C09B67/00; C09B67/0071; C09B67/0092; C09B67/0095; B; B29; B29C; B29C45/00; B29C45/0001; C08; C08J; C08J3/00; C08J3/20; C08J3/22; C09B67/006; C09C; C09C3/00; C09C3/006; C09C3/04; C09C3/045; C09C3/08; C01; C01P; C01P2004/00; C01P2004/10; C01P2004/12; C01P2004/20; C01P2004/30; C01P2004/32; C01P2004/38; C01P2004/50; C01P2004/60; C01P2004/61; C01P2004/62; C01P2004/80; C01P2006/00; C01P2006/60
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
206 words
The process for dry coloring and molding a shaped article of a thermoplastic resin having highly developed color and hue and intense and lustrous color comprising: (a) preparing a fluid admixture of a melted fatty acid amide and pigment particles, while avoiding agglomeration, said fatty acid amide being solid at room temperature, the amine radical in the fatty acid amide containing 0 to 36 carbon atoms, each fatty acid radical in the fatty acid amide containing 1 to 36 carbon atoms, and said fatty acid amide can be substituted by hydroxyl; (b) cooling the admixture until it is in a solidified state, the pigment particles being substantially encapsulated by the fatty acid amide, and said admixture being in dry form; (c) particulating the solidified admixture, particles of said solidified admixture being obtained; (d) removing the fines portion of said particles of said particulated solidified admixture from said particles of said particulated solidified admixture; (e) admixing said particles of said particulated solidified admixture in dry form with a particulated thermoplastic resin; and (f) molding said admixture of said particles of said particulated solidified admixture and said particulate thermoplastic resin, whereby said colored, molded, shaped article results, said admixing step and molding step do not utilize any solvent.
Claim 2
Dependent Claim
206 words
The process for dry coloring and molding a shaped article of a thermoplastic resin having highly developed color and hue and intense and lustrous color comprising: (a) preparing a fluid admixture of a melted fatty acid amide and pigment particles, while avoiding agglomeration, said fatty acid amide being solid at room temperature, the amine radical in the fatty acid amide containing 0 to 36 carbon atoms, each fatty acid radical in the fatty acid amide containing 1 to 36 carbon atoms, and said fatty acid amide can be substituted by hydroxyl; (b) cooling the admixture until it is in a solidified state, the pigment particles being substantially encapsulated by the fatty acid amide, and said admixture being in dry form; (c) particulating the solidified admixture, particles of said solidified admixture being obtained; (d) removing the fines portion of said particles of said particulated solidified admixture from said particles of said particulated solidified admixture; (e) admixing said particles of said particulated solidified admixture in dry form with a particulated thermoplastic resin; and (f) molding said admixture of said particles of said particulated solidified admixture and said particulate thermoplastic resin, whereby said colored, molded, shaped article results, said admixing step and molding step do not utilize any solvent.
Claim 3
Dependent Claim
11 words
The process of claim 1 wherein the thermoplastic resin is polypropylene.
Claim 4
Dependent Claim
21 words
The process of claim 1 wherein the admixing and molding steps are achieved by means of a screw injection molding machine.
Claim 5
Dependent Claim
19 words
The process of claim 1 wherein the admixing and molding steps are achieved by means of a compression press.
Claim 6
Dependent Claim
13 words
The process of claim 1 wherein the shaped item is in sheet form.
Claim 7
Dependent Claim
33 words
The process of claim 1 wherein, in step (e), about 0.1 to about 10 parts by weight of said particulated solidified admixture is used per 100 parts by weight of said thermoplastic resin.
Claim 8
Dependent Claim
142 words
Process for dry coloring and molding a shaped article of a thermoplastic resin having highly developed color and hue and intense and lustrous color comprising: (a) admixing a particulated solid composition with a particulate thermoplastic resin, while avoiding agglomeration, said solid composition consisting of pigment particles which are encapsulated by a fatty acid amide, each amide radical in the fatty acid amide containing 0 to 36 carbon atoms, each fatty acid radical in the fatty acid amide containing 1 to 36 carbon atoms, said fatty acid amide can be substituted by hydroxyl groups, said solid composition being solid at room temperature, and said admixture being in dry form; and (b) molding said admixture of said particulated solid composition and particulate thermoplastic resin into a shaped article, whereby said colored, molded, shaped article results; said admixing and molding steps not utilizing any solvent.
Claim 9
Dependent Claim
142 words
Process for dry coloring and molding a shaped article of a thermoplastic resin having highly developed color and hue and intense and lustrous color comprising: (a) admixing a particulated solid composition with a particulate thermoplastic resin, while avoiding agglomeration, said solid composition consisting of pigment particles which are encapsulated by a fatty acid amide, each amide radical in the fatty acid amide containing 0 to 36 carbon atoms, each fatty acid radical in the fatty acid amide containing 1 to 36 carbon atoms, said fatty acid amide can be substituted by hydroxyl groups, said solid composition being solid at room temperature, and said admixture being in dry form; and (b) molding said admixture of said particulated solid composition and particulate thermoplastic resin into a shaped article, whereby said colored, molded, shaped article results; said admixing and molding steps not utilizing any solvent.
Claim 10
Dependent Claim
10 words
The process of claim 7 wherein said thermoplastic is polypropylene.
Claim 11
Dependent Claim
20 words
The process of claim 7 wherein the admixing and molding is achieved by means of a screw injection molding machine.
Claim 12
Dependent Claim
18 words
The process of claim 7 wherein the admixing and molding is achieved by means of a compression press.
Claim 13
Dependent Claim
13 words
The process of claim 7 wherein the shaped article is in sheet form.
Claim 14
Dependent Claim
36 words
The process of claim 7 wherein, in said admixing and molding step, about 0.1 to about 10 parts by weight of said particulated solidified admixture is used per 100 parts by weight of said thermoplastic resin.
Claim 15
Dependent Claim
193 words
The process for dry coloring and molding a shaped article of a thermoplastic resin having a highly developed color and hue and intense and lustrous color comprising: (a) preparing a fluid admixture of a melted fatty acid amide and pigment particles, said fatty acid being solid at room temperature, each radical in the fatty acid amide containing 0 to 36 carbon atoms, each fatty acid radical in the fatty acid amide containing 1 to 36 carbon atoms, and said fatty acid amide can be substituted by hydroxyl groups; (b) passing the fluid admixture through a heated low-shear mixer; (c) cooling the fluid admixture until it is in a solidified state by passing the mixed fluid admixture through cooled rollers, whereby solid wafer-like flakes in dry form are formed and the pigment particles being substantially encapsulated by the fatty acid amide; (d) particulating the solid wafer-like flakes; (e) admixing said particulated flakes in dry form with a particulate thermoplastic resin; and (f) molding said admixture of said particles of said particulated solidified admixture and said particulate thermoplastic resin, whereby said colored, molded, shaped article results, said admixing and molding steps not utilizing any solvent.
Claim 16
Dependent Claim
193 words
The process for dry coloring and molding a shaped article of a thermoplastic resin having a highly developed color and hue and intense and lustrous color comprising: (a) preparing a fluid admixture of a melted fatty acid amide and pigment particles, said fatty acid being solid at room temperature, each radical in the fatty acid amide containing 0 to 36 carbon atoms, each fatty acid radical in the fatty acid amide containing 1 to 36 carbon atoms, and said fatty acid amide can be substituted by hydroxyl groups; (b) passing the fluid admixture through a heated low-shear mixer; (c) cooling the fluid admixture until it is in a solidified state by passing the mixed fluid admixture through cooled rollers, whereby solid wafer-like flakes in dry form are formed and the pigment particles being substantially encapsulated by the fatty acid amide; (d) particulating the solid wafer-like flakes; (e) admixing said particulated flakes in dry form with a particulate thermoplastic resin; and (f) molding said admixture of said particles of said particulated solidified admixture and said particulate thermoplastic resin, whereby said colored, molded, shaped article results, said admixing and molding steps not utilizing any solvent.
References Cited (Backward Citations)
US2234164A
Cited
US2192956A
Cited
US2385379A
Cited
US2442972A
Cited
US2450940A
Cited
US2683702A
Cited
US2841504A
Cited
US2927091A
Cited
US2971922A
Cited
US3197425A
Cited
US3278479A
Cited
US3266924A
Cited
US3328185A
Cited
US3313730A
Cited
US3354111A
Cited
US3252820A
Cited
US3394210A
Cited
US3441507A
Cited
US3706825A
Cited
US3978036A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-04 | 1985-07-06 | 1986-01-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-04 | 1989-07-06 | 1990-01-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-04 | 1993-07-06 | 1994-01-05 | $7700.00 | Window Closed / Lapsed |