Process for manufacturing boron nitride fiber batts using a spinner
Assignee: Stemcor Corp
•
Filing: 1980-03-28
•
Granted: 1982-01-05
•
Expires: 2000-03-28
Abstract
Abstract A process is disclosed for producing non-woven, yet internally cohesive, boron nitride fiber batts, suitable for use as an electric cell separator in a lithium-sulfide battery. Molten boron oxide is centrifugally spun into strands and attenuated by an annular gas stream into fibers at a controlled relative humidity. The fibers are funnelled into a chamber and subjected to a turbulent air flow, which causes random orientation and intertwining of the fibers, resulting in multiple mechanical bonds thereamong. The compacted boron oxide fiber bundle thus produced is heated in an anhydrous ammonia atmosphere to convert boron oxide in the fibers into boron nitride (BN).
Inventors
- 👤 John L. Tworek
- 👤 Gordon R. Rignel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 14:17
CPC Classifications
C; C01; C01B; C01B21/00; C01B21/06; C01B21/064; C04; C04B; C04B35/00; C04B35/622; C04B35/62227; C03; C03B; C03B37/00; C03B37/01; C03B37/04; D; D04; D04H; D04H1/00; D04H1/40; D04H1/54; D04H1/56; H; H01; H01M; H01M50/00; H01M50/40; H01M50/403; H01M50/406; H01M50/409; H01M50/431; H01M50/434; H01M50/44; C01P; C01P2004/00; C01P2004/10; H01M2300/00; H01M2300/0017; H01M2300/0048; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2916
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
148 words
A process for producing non-woven, internally cohesive, boron nitride fiber batts, comprising the steps of: melting solid boron oxide; extruding the molten boron oxide from a rapidly spinning drum having a plurality of circumferentially arranged perforations, whereby said molten boron oxide is extruded through said perforations into a plurality of strands; directing an annular gas stream at a temperature in excess of 700° C. obliquely against each of said strands to attenuate said strands into fibers said temperature being of an intensity and duration to cause the fibers to become sticky and bond together; subjecting said fibers to a turbulent air flow sufficient to cause random orientations and intertwining of the fibers; collecting said fibers into a bundle; and heating said bundle in an anhydrous ammonia atmosphere to a sufficient temperature and for a sufficient time to convert essentially all boron oxide in the fibers into boron nitride.
Claim 2
Dependent Claim
148 words
A process for producing non-woven, internally cohesive, boron nitride fiber batts, comprising the steps of: melting solid boron oxide; extruding the molten boron oxide from a rapidly spinning drum having a plurality of circumferentially arranged perforations, whereby said molten boron oxide is extruded through said perforations into a plurality of strands; directing an annular gas stream at a temperature in excess of 700° C. obliquely against each of said strands to attenuate said strands into fibers said temperature being of an intensity and duration to cause the fibers to become sticky and bond together; subjecting said fibers to a turbulent air flow sufficient to cause random orientations and intertwining of the fibers; collecting said fibers into a bundle; and heating said bundle in an anhydrous ammonia atmosphere to a sufficient temperature and for a sufficient time to convert essentially all boron oxide in the fibers into boron nitride.
Claim 3
Dependent Claim
18 words
The process as set forth in claim 1, wherein said gas stream is a stream of compressed air.
Claim 4
Dependent Claim
18 words
The process as set forth in claim 1, wherein said gas stream is a stream of combustion gases.
Claim 5
Dependent Claim
19 words
The process as set forth in claim 1, wherein said gas stream is a stream of an inert gas.
Claim 6
Dependent Claim
25 words
The process as set forth in claim 1, wherein said gas stream has a speed of from about 800 to about 900 feet per second.
Claim 7
Dependent Claim
22 words
The process as set forth in claim 1, wherein said drum is spinning at a speed of from 1000 to 3000 RPM.
Claim 8
Dependent Claim
24 words
The process as set forth in claim 1, wherein said fibers are discrete having lengths of from about 0.1 inch to about 1.0 foot.
Claim 9
Dependent Claim
52 words
The process as set forth in claim 2, wherein said sufficient temperature to convert boron oxide in the fibers into boron nitride is from about 700° C. to about 1100° C. and said sufficient time to convert the boron oxide fibers to boron nitride is from about 10 to about 100 hours.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-04 | 1985-07-06 | 1986-01-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-04 | 1989-07-06 | 1990-01-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-04 | 1993-07-06 | 1994-01-05 | $7700.00 | Window Closed / Lapsed |