US4308302A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Weatherstrip and composition of matter therefor
Assignee: Goodyear Tire and Rubber Co
•
Filing: 1981-02-27
•
Granted: 1981-12-29
•
Expires: 2001-02-27
Abstract
Abstract A flange mountable weatherstrip includes a coated flange cover and a hollow sealing member. The coating and the sealing member are preferably formed in a single extrusion operation of a single low durometer elastomeric sponge material. The preferred physical properties of the elastomeric material and its formulation are described. The flange cover is adaptable to frictionally engage a supporting edge flange. The sealing member is of an asymmetric cross-sectional configuration resembling an upper case letter D.
Inventors
- 👤 Gordon E. Etter
- 👤 William Hoverman, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 14:05
CPC Classifications
B; B60; B60J; B60J10/00; B60J10/20; B60J10/24; B60J10/15; B60J10/30; B60J10/32; B60J10/80; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24025; Y10T428/2419; Y10T428/24198; Y10T428/24479; Y10T428/24521; Y10T428/24545; Y10T428/24744; Y10T428/24777
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
203 words
A flange mountable weatherstrip comprising: (a) a flange cover adaptable to frictionally engage a supporting edge flange, said cover comprising an elongated carrier capable of being formed into a U-shaped cross-sectional configuration defined by a central web portion and first and second spaced leg portions, said cover having a coating of elastomeric material; (b) a hollow sealing member joined to said flange cover and integral with said coating, said sealing member being cantilevered from said cover, said sealing member being of asymmetric cross-sectional configuration resembling an upper case letter D and including a generally C-shaped portion extending from the outer surface of the first leg portion of the flange cover adjacent the web portion thereof and presenting its convex side to the web portion and a straight portion extending from the outer surface of said first leg portion, said straight portion being joined at its end distal said one leg portion to said C-shaped portion, said straight portion forming an acute angle with the plane of the carrier in said one leg portion when said plane is extended outwardly from the adjacent end of said cover; (c) said sealing member and said coating being formed of a single low durometer elastomeric sponge material.
Claim 2
Dependent Claim
203 words
A flange mountable weatherstrip comprising: (a) a flange cover adaptable to frictionally engage a supporting edge flange, said cover comprising an elongated carrier capable of being formed into a U-shaped cross-sectional configuration defined by a central web portion and first and second spaced leg portions, said cover having a coating of elastomeric material; (b) a hollow sealing member joined to said flange cover and integral with said coating, said sealing member being cantilevered from said cover, said sealing member being of asymmetric cross-sectional configuration resembling an upper case letter D and including a generally C-shaped portion extending from the outer surface of the first leg portion of the flange cover adjacent the web portion thereof and presenting its convex side to the web portion and a straight portion extending from the outer surface of said first leg portion, said straight portion being joined at its end distal said one leg portion to said C-shaped portion, said straight portion forming an acute angle with the plane of the carrier in said one leg portion when said plane is extended outwardly from the adjacent end of said cover; (c) said sealing member and said coating being formed of a single low durometer elastomeric sponge material.
Claim 3
Dependent Claim
21 words
The weatherstrip of claim 1, wherein said straight portion of the sealing member is of less thickness than said C-shaped portion.
Claim 4
Dependent Claim
44 words
The weatherstrip of claim 1, wherein said sealing member in its new undeformed state extends outwardly from said carrier not more than 25.4 mm. (one inch) and the minimum thickness of said straight portion is about one-half the minimum thickness of said C-shaped portion.
Claim 5
Dependent Claim
33 words
The weatherstrip of claim 2, wherein the thickness of the outermost part of the C-shaped portion located most distant from said carrier is greater than that of the remainder of said sealing member.
Claim 6
Dependent Claim
29 words
The weatherstrip of claim 1, 2, 3, or 4, wherein said sealing member has a wall thickness from about 1.8 mm (0.070 inch) to about 5.5 mm. (0.220 inch).
Claim 7
Dependent Claim
36 words
The weatherstrip of claim 5, wherein the cured elastomeric sponge material when free blown has a durometer from about 40 to 60 Shore "00" and a density from about 0.40 to 0.60 megagrams per cubic meter.
Claim 8
Dependent Claim
61 words
The weatherstrip of claim 6, wherein the cured elastomeric sponge material, when measured on the sealing member, has a tensile strength of at least about 17.6 kg. per square centimeter (250 pounds per square inch), an elongation at rupture of at least 250 percent, and does not absorb more than 5 weight percent of water when tested according to ASTM D1056.
Claim 9
Dependent Claim
64 words
The weatherstrip of claim 7, wherein the elastomeric sponge material comprises from about 100 to 80 parts of poly(1,3-cyclopentylenevinylene) elastomer and 0 to 20 parts of high Mooney viscosity chloroprene elastomer, from about 40 to 100 parts per one hundred parts of elastomer of carbon black, a sulfur donor and a blowing agent in amounts sufficient to produce a vulcanized closed cell sponge material.
Claim 10
Dependent Claim
77 words
A closed cell sponge material comprising: from about 100 to 70 parts by weight of poly(1,3-cyclopentylenevinylene) elastomer and 0 to 30 parts by weight of polychloroprene elastomer, and per each hundred weight parts of total elastomer, from about 40 to 100 parts of carbon black, a sulfur bearing reagent in an amount sufficient to cross-link the elastomer and a thermodegradable blowing agent in an amount sufficient to reduce the calculated density of the compounded material during vulcanization.
Claim 11
Dependent Claim
77 words
A closed cell sponge material comprising: from about 100 to 70 parts by weight of poly(1,3-cyclopentylenevinylene) elastomer and 0 to 30 parts by weight of polychloroprene elastomer, and per each hundred weight parts of total elastomer, from about 40 to 100 parts of carbon black, a sulfur bearing reagent in an amount sufficient to cross-link the elastomer and a thermodegradable blowing agent in an amount sufficient to reduce the calculated density of the compounded material during vulcanization.
Claim 12
Dependent Claim
30 words
The sponge material of claim 9, further comprising per each hundred parts by weight of total elastomer from about 170 to 250 parts by weight of naphthenic rubber process oil.
Claim 13
Dependent Claim
67 words
The sponge material of claim 9 or 10, further comprising not more than 20 parts by weight of high Mooney viscosity polychloroprene and per each one hundred parts by weight of total elastomer from about 3 to 5 parts by weight of zinc oxide and from about one-half to two parts by weight of stearic acid, said carbon black being a medium reinforcing oil furnace carbon black.
Claim 14
Dependent Claim
25 words
The sponge material of claim 11, wherein calculated density of the compounded material is reduced by at least 40 percent upon vulcanization at atmospheric pressure.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-28 | 1985-06-29 | 1985-12-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-28 | 1989-06-29 | 1989-12-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-28 | 1993-06-29 | 1993-12-29 | $7700.00 | Window Closed / Lapsed |