US4308223A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing electret fibers for enhancement of submicron aerosol filtration
Assignee: Albany International Corp
•
Filing: 1980-03-24
•
Granted: 1981-12-29
•
Expires: 2000-03-24
Abstract
Abstract A method is provided for imparting a permanent electrostatic charge to polymeric fibers. Ions are implanted into the fibers in the presence of a strong electric field while the temperature is maintained above the glass transition temperature but below the melting temperature of the fibers. The method is particularly adapted for ion implantation into a fibrous filter mat. Carbonium ions formed by a corona discharge may be implanted into deep sites within the fibers.
Inventors
- 👤 Sidney C. Stern
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 21:44
CPC Classifications
B; B29; B29C; B29C71/00; B29C71/0081; B01; B01D; B01D39/00; B01D39/14; B01D39/16; B01D39/1607; B01D39/1623; B29C59/00; B29C59/10; H; H01; H01G; H01G7/00; H01G7/02; H01G7/021; H01G7/023; H01T; H01T19/00; H01T19/04; B01D2239/00; B01D2239/10; B29K; B29K2023/00; B29K2023/10; B29K2023/12; B29K2313/00; B29K2995/00; B29K2995/0003; B29K2995/001
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
164 words
A method for imparting a permanent electrostatic charge to a polymeric fibrous filter mat, comprising the steps of: providing a first metallic base plate having a dielectric film thereon, said first plate being connected to ground; placing said polymeric fibrous filter mat in physical contact with said dielectric film; providing a second metallic base plate having a high density of corona discharge points extending therefrom, said second metallic base plate being connected to a high voltage source, and said corona discharge points being in close proximity to said filter mat; elevating the temperature of said plates and said filter mat to between the glass transition and melt temperatures of said polymeric filter mat; and applying a high voltage to said corona points to expose said filter mat to corona charging and an electric field, whereby the molecules within said polymeric fibrous filter mat become aligned so as to form dipoles and electrostatic charges are implanted within said filter mat due to said corona charging.
Claim 2
Independent Claim
164 words
A method for imparting a permanent electrostatic charge to a polymeric fibrous filter mat, comprising the steps of: providing a first metallic base plate having a dielectric film thereon, said first plate being connected to ground; placing said polymeric fibrous filter mat in physical contact with said dielectric film; providing a second metallic base plate having a high density of corona discharge points extending therefrom, said second metallic base plate being connected to a high voltage source, and said corona discharge points being in close proximity to said filter mat; elevating the temperature of said plates and said filter mat to between the glass transition and melt temperatures of said polymeric filter mat; and applying a high voltage to said corona points to expose said filter mat to corona charging and an electric field, whereby the molecules within said polymeric fibrous filter mat become aligned so as to form dipoles and electrostatic charges are implanted within said filter mat due to said corona charging.
Claim 3
Dependent Claim
15 words
A method as described in claim 1 wherein said filter mat is made from polypropylene.
Claim 4
Dependent Claim
51 words
A method as described in claim 1 further including the step of providing an increased concentration of carbon dioxide near said polymeric fibrous filter mat in the presence of corona discharge such that stable CO 3 ═ ions are formed and are implanted into deep sites in said polymeric filter mat.
Claim 5
Dependent Claim
47 words
A method as described in claim 1 further including the step of securing said filter mat and said dielectric film to said first base plate by means of plastic rings upon said mat and nylon screws extending through said rings, mat, film and said first base plate.
Claim 6
Dependent Claim
22 words
A method as described in claim 1 including inserting said corona discharge points into said filter mat without contacting said dielectric film.
Claim 7
Dependent Claim
17 words
A method as described in claim 1 wherein said dielectric film is a polyester or flurocarbon film.
Claim 8
Dependent Claim
43 words
A method as described in claim 1 including scouring said polymeric fibrous filter mat in a distilled water solution of tetra sodium pyrophosphate, rinsing with distilled water, and oven drying said mat prior to placing it in physical contact with said dielectric film.
Claim 9
Dependent Claim
23 words
A method as described in claim 1 wherein said mat is exposed to the electric field and corona discharge for about three minutes.
Claim 10
Dependent Claim
36 words
A method as described in claim 1 wherein said first base plate is connected to ground through a microammeter, and applying high voltage to said corona discharge points until low current flow occurs in said microammeter.
Claim 11
Dependent Claim
16 words
A method as described in claim 1 wherein said filter mat is a non-woven needled felt.
Claim 12
Independent Claim
80 words
A method for imparting a permanent electrostatic charge to polymeric fibers, comprising the steps of implanting stable ions into said fibers in the presence of a strong electric field while said fibers are at a temperature above the glass transition temperature but below their melting temperature, whereby dipoles are formed in said fibers which are oriented in an array resembling the alignment of magnetic North and South poles in an electromagnetic field, and electrostatic charges are implanted in said fibers.
Claim 13
Independent Claim
80 words
A method for imparting a permanent electrostatic charge to polymeric fibers, comprising the steps of implanting stable ions into said fibers in the presence of a strong electric field while said fibers are at a temperature above the glass transition temperature but below their melting temperature, whereby dipoles are formed in said fibers which are oriented in an array resembling the alignment of magnetic North and South poles in an electromagnetic field, and electrostatic charges are implanted in said fibers.
Claim 14
Dependent Claim
19 words
A method as described in claim 11 wherein said fibers are in the form of a fibrous filter mat.
Claim 15
Independent Claim
33 words
A method as described in claims 11 or 12 wherein said ions are implanted within said fibers by means of a corona discharge from multiple sharp points that are at a high potential.
Claim 16
Independent Claim
14 words
A method as described in claims 11 or 12 wherein said fibers are polypropylene.
Claim 17
Dependent Claim
47 words
A method as described in claim 13 further including the step of providing an increased concentration of carbon dioxide near said polymeric fibers in the presence of corona discharge such that stable CO 3 ═ ions are formed and are implanted into deep sites within the fibers.
Claim 18
Dependent Claim
23 words
A method as described in claim 15 wherein said fibers are exposed to the electric field and corona discharge for about three minutes.
Claim 19
Dependent Claim
20 words
A method as described in claim 9 wherein said low current flow is between 10 -7 and 10 -8 amps.
Claim 20
Dependent Claim
27 words
A method as described in claim 13 wherein high voltage is applied to the multiple sharp points until corona current flow to ground reaches a predetermined level.
Claim 21
Dependent Claim
19 words
A method as described in claim 18 wherein said predetermined level is between 10 -7 and 10 -8 amps.
References Cited (Backward Citations)
US2385873A
Cited
US2476283A
Cited
US2476282A
Cited
US2740184A
Cited
US2820716A
Cited
US3003304A
Cited
US2920679A
Cited
US2920172A
Cited
US2998051A
Cited
US3414444A
Cited
US3483374A
Cited
US3571679A
Cited
US3708561A
Cited
US3900538A
Cited
US3924324A
Cited
US3998916A
Cited
JPS5120718A
Cited
US4147745A
Cited
US4086499A
Cited
US4178157A
Cited
US4215682A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-28 | 1985-06-29 | 1985-12-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-28 | 1989-06-29 | 1989-12-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-28 | 1993-06-29 | 1993-12-29 | $7700.00 | Window Closed / Lapsed |