US4307566A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Bulky spun yarn and a method for manufacturing the same from a combination of thermally extensible and thermally shrinkable fibers
Assignee: Teijin Ltd
•
Filing: 1980-01-23
•
Granted: 1981-12-29
•
Expires: 2000-01-23
Abstract
Abstract A double layered yarn having a sheath and core structure is prepared through a roving process, drawing process or fine spinning process. The sheath portion of the yarn is composed of staple fibers which have a high thermal shrinkage in boiling water of at least 5%, and the blended fiber ratio of which is between 50% and 25%. The core portion of the yarn is composed of staple fibers which have a property being spontaneously extensible, and the blended fiber ratio of which is between 25% and 75%. The double layered yarn is subjected to a heat treatment in hot water, and a bulky spun yarn which comprises staple fibers A and B is obtained. The staple fibers A are concentrated toward the inside of the bulky spun yarn after they are shrunk. The ends of staple fibers B are held within the inside of the bulky spun yarn, and the intermediate portions of fibers B are bulged as a loop from the body portion of the bulky spun yarn, after the fibers B are spontaneously extended.
Inventors
- 👤 Goro Murata
- 👤 Osamu Wada
- 👤 Shunichi Takeda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 06:36
CPC Classifications
D; D02; D02G; D02G1/00; D02G1/18; D02G3/00; D02G3/22; D02G3/36; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2922; Y10T428/2924; Y10T428/2933; Y10T428/2964; Y10T428/2967; Y10T428/2969; Y10T428/2973; Y10T428/2976
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
149 words
A method for manufacturing a bulky spun yarn characterized by: preparing a double layered yarn having a sheath and core structure, the sheath portion of said yarn being composed of thermoplastic staple fibers which include fibers having a high thermal shrinkage in boiling water of at least 5%, and the blended fiber ratio of which fibers is between 50% and 25%, and the core portion of said yarn being composed of thermoplastic staple fibers which include fibers having a property of being spontaneously extensible under heating conditions, and the blended fiber ratio of which fibers is between 25% and 75%, and; heat treating said prepared double layered yarn, whereby the intermediate portions of said fibers having a property of being spontaneously extensible are bulged from the body portion of said yarn, and said fibers having a high thermal shrinkage are concentrated toward the inside of said bulky spun yarn.
Claim 2
Independent Claim
149 words
A method for manufacturing a bulky spun yarn characterized by: preparing a double layered yarn having a sheath and core structure, the sheath portion of said yarn being composed of thermoplastic staple fibers which include fibers having a high thermal shrinkage in boiling water of at least 5%, and the blended fiber ratio of which fibers is between 50% and 25%, and the core portion of said yarn being composed of thermoplastic staple fibers which include fibers having a property of being spontaneously extensible under heating conditions, and the blended fiber ratio of which fibers is between 25% and 75%, and; heat treating said prepared double layered yarn, whereby the intermediate portions of said fibers having a property of being spontaneously extensible are bulged from the body portion of said yarn, and said fibers having a high thermal shrinkage are concentrated toward the inside of said bulky spun yarn.
Claim 3
Dependent Claim
47 words
A method according to claim 1, wherein the sum of the thermal shrinkage of said fibers located at said sheath portion in said double layered yarn and the spontaneous extension of said fibers located at said core portion in said double layered yarn is at least 8%.
Claim 4
Dependent Claim
13 words
A method according to claim 1, wherein said thermoplastic polymer is a polyester.
Claim 5
Dependent Claim
40 words
A method according to claim 1, wherein each of said fibers located at said sheath portion in said double layered yarn has a denier between 1.0 de and 15 de and a fiber length between 24 mm and 250 mm.
Claim 6
Dependent Claim
42 words
A method according to claim 1 or 4, wherein each of said fibers located at said core portion in said double layered yarn has a denier between 0.5 de and 10 de and a fiber length between 24 mm and 280 mm.
Claim 7
Dependent Claim
54 words
A method according to claim 1, wherein said double layered yarn is subjected to a preliminarily heat treatment for a period of time between 30 minutes and 60 minutes, at a temperature between 70° C. and 100° C., and thereafter, is subjected to a heat treatment at a temperature of at least 100° C.
Claim 8
Dependent Claim
15 words
A method according to claim 6, wherein said heat treatments takes place in hot water.
Claim 9
Dependent Claim
11 words
A bulky spun yarn prepared by the method of claim 1.
Claim 10
Dependent Claim
40 words
A bulky spun yarn according to claim 8, wherein the blended fiber ratio of said first mentioned staple fibers is between 50% and 25%, and the blended fiber ratio of said last mentioned staple fibers is between 25% and 75%.
Claim 11
Dependent Claim
17 words
A bulky spun yarn according to claim 8 or 9, wherein said thermoplastic polymer is a polyester.
References Cited (Backward Citations)
US3111805A
Cited
US3852948A
Cited
US3439490A
Cited
US3325876A
Cited
US3596459A
Cited
US3568428A
Cited
US3998042A
Cited
GB2039560A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-28 | 1985-06-29 | 1985-12-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-28 | 1989-06-29 | 1989-12-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-28 | 1993-06-29 | 1993-12-29 | $7700.00 | Window Closed / Lapsed |