Process for producing plasticized elastomer-styrene coated beads
Assignee: Lyondell Chemical Technology LP
•
Filing: 1980-12-22
•
Granted: 1981-12-22
•
Expires: 2000-12-22
Abstract
Abstract Polymeric beads for use in forming soft molded articles of low density are produced by formation of a plasticized elastomer-styrene polymeric coating about initial styrene beads, by forming an aqueous suspension of the initial beads, adding thereto an aqueous emulsion of a coating composition consisting of styrenic monomer, a conjugated diene elastomer, and a plasticizer, containing a catalyst and a nonionic surfactant comprising an ethylene oxide condensate of an alkylphenol, the surfactant containing at least thirty moles of ethylene oxide per mole of alkylphenol, and polymerizing the coating composition about the initial beads.
Inventors
- 👤 Ralph Milkovich
- 👤 David R. Warfel
- 👤 Elizabeth A. Blommers
- 👤 Alvin R. Ingram
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 03:39
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/0061; C08F; C08F257/00; C08F257/02; C08F279/00; C08F279/02; C08J9/16; C08J9/18; C08J2325/00; C08J2451/00
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
170 words
A process for forming coated styrenic polymer beads for use in producing low density soft foamed articles comprising: (a) forming an aqueous suspension of initial styrenic polymer beads with the aid of a finely divided, difficultly water-soluble, inorganic phosphate suspending agent and a modifier therefor, (b) forming an emulsion containing a plasticized coating composition consisting of a major amount of a styrenic monomer, a minor amount of a conjugated diene elastomer, and a minor amount of a plasticizer therefor, and containing a styrenic-monomer-soluble free-radical-producing catalyst, in an aqueous medium containing a nonionic surfactant comprising an ethylene oxide condensate of an alkylphenol, selected from octylphenols and nonylphenols, said surfactant containing at least thrity moles of ethylene oxide per mole of alkylphenol; (c) adding said emulsion to said styrenic polymer bead suspension to form a mixture thereof, while maintaining the suspension at an elevated temperature; and maintaining the mixture so formed at an elevated temperature to cause said coating composition to polymerize and form a coating about said initial styrenic polymer beads.
Claim 2
Dependent Claim
170 words
A process for forming coated styrenic polymer beads for use in producing low density soft foamed articles comprising: (a) forming an aqueous suspension of initial styrenic polymer beads with the aid of a finely divided, difficultly water-soluble, inorganic phosphate suspending agent and a modifier therefor, (b) forming an emulsion containing a plasticized coating composition consisting of a major amount of a styrenic monomer, a minor amount of a conjugated diene elastomer, and a minor amount of a plasticizer therefor, and containing a styrenic-monomer-soluble free-radical-producing catalyst, in an aqueous medium containing a nonionic surfactant comprising an ethylene oxide condensate of an alkylphenol, selected from octylphenols and nonylphenols, said surfactant containing at least thrity moles of ethylene oxide per mole of alkylphenol; (c) adding said emulsion to said styrenic polymer bead suspension to form a mixture thereof, while maintaining the suspension at an elevated temperature; and maintaining the mixture so formed at an elevated temperature to cause said coating composition to polymerize and form a coating about said initial styrenic polymer beads.
Claim 3
Dependent Claim
24 words
The process as defined in claim 1 wherein said conjugated diene elastomer is selected from homopolymers of conjugated dienes and diene block copolymer rubbers.
Claim 4
Dependent Claim
85 words
The process of claim 2 wherein said conjugated diene block copolymer rubber is selected from the group consisting of graded block, A-B diblock, radial or star block, A-B-A triblock and A-B-A hydrogenated triblock rubbers, wherein A represents essentially polymerized vinyl aromatic monomer with a minor amount of conjugated diene, B represents essentially conjugated diene polymer with a minor amount of vinyl aromatic monomer, and the rubbers contain from 2 to 50% by weight vinyl aromatic monomer and 50 to 98% by weight of conjugated diene.
Claim 5
Dependent Claim
30 words
The process of claims 1, 2 or 3 wherein the diene in the conjugated diene elastomer is selected from the group consisting of butadiene, isoprene, choloroprene, 2, 3-dimethylbutadiene and piperylene.
Claim 6
Dependent Claim
32 words
The process as defined in claim 1 wherein said initial styrenic polymer beads are produced from a styrenic monomer selected from the group consisting of styrene, alpha-methylstyrene, para-methylstyrene, para-t-butylstyrene, monochlorostyrene and dichlorostyrene.
Claim 7
Dependent Claim
25 words
The process as defined in claim 1 wherein said styrenic monomer is selected from the group consisting of styrene, alpha-methylstyrene, para-methylstyrene, para-t-butylstyrene, monochlorostyrene and dichlorostyrene.
Claim 8
Dependent Claim
25 words
The process as defined in claim 1 wherein the coating formed about said initial beads comprises 2-50 percent by weight of the beads so produced.
Claim 9
Dependent Claim
36 words
The process as defined in claim 1 wherein the coating formed about said beads comprises from 75-98 percent by weight of said styrenic monomer and 2-25 percent by weight of said plasticizer and conjugated diene elastomer.
Claim 10
Dependent Claim
54 words
The process as defined in claim 1 wherein said plasticizer is soluble in the styrenic monomer, has a melting point of less than 35° C. and a boiling point greater than 140° C., and is present in an amount of two percent or less by weight, based upon the weight of the coated beads.
Claim 11
Dependent Claim
13 words
The process as defined in claim 1 wherein said plasticizer is mineral oil.
Claim 12
Dependent Claim
13 words
The process as defined in claim 1 wherein said plasticizer is dioctyl adipate.
Claim 13
Dependent Claim
34 words
The process as defined in claim 1 wherein said styrenic monomer is styrene, said plasticizer comprises styrene monomer, and wherein said styrene monomer is only partially polymerized during the polymerization of said coating composition.
References Cited (Backward Citations)
US3185588A
Cited
US3102050A
Cited
GB1025694A
Cited
US3370022A
Cited
FR2413420A1
Cited
FR2413419A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-21 | 1985-06-22 | 1985-12-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-21 | 1989-06-22 | 1989-12-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-21 | 1993-06-22 | 1993-12-22 | $7700.00 | Window Closed / Lapsed |