Process for producing a laminate of metal with thermoplastic material
Assignee: Celotex Corp
•
Filing: 1980-04-14
•
Granted: 1981-12-22
•
Expires: 2000-04-14
Abstract
Abstract A process for producing a laminate comprising a metal sheet having thermoplastic material on both sides thereof is described. The thermoplastic material is calendered to produce an upper thermoplastic sheet and a lower thermoplastic sheet. A metal sheet is fed into the nip between the calender rolls in order to contact the metal sheet simultaneously with the upper and lower thermoplastic sheets, thus producing a laminate. Processes for producing a pipe-wrapping material, a roofing structure and a solvent-welded joint are also provided.
Inventors
- 👤 Smith A. Funk
- 👤 Charles J. Klasen
- 👤 Ilmars Vilmanis
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 20:08
CPC Classifications
B; B32; B32B; B32B15/00; B32B15/04; B32B15/08; B29; B29C; B29C43/00; B29C43/22; B29C43/28; B32B15/18; B32B15/20; B32B27/00; B32B27/30; B32B27/304; B32B37/00; B32B37/14; B32B37/24; E; E04; E04D; E04D5/00; E04D5/10; F; F16; F16L; F16L59/00; F16L59/10
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
197 words
A process for producing a laminate comprising a metal sheet having chlorinated polyethylene composition on both sides thereof, said process consisting essentially of the steps of: I. calendering chlorinated polyethylene composition at 250° F. to 350° F. through the nip of a first roll and a second roll to produce an upper chlorinated polyethylene sheet adhering to the second roll; II. calendering chlorinated polyethylene composition at 250° F. to 350° F. through the nip of a third roll and a fourth roll to produce a lower chlorinated polyethylene sheet adhering to the third roll; III. feeding a metal sheet into the nip between the second roll and the third roll while contacting at 250° F. to 350° F. the upper chlorinated polyethylene sheet with the top of the metal sheet and while simultaneously contacting the lower chlorinated polyethylene sheet with the bottom of the metal sheet wherein the top and the bottom of the metal sheet have thereon a coating of an adhesion promoter, wherein the separation of the second and third roll is substantially equal to the sum of the thicknesses of the upper chlorinated polyethylene sheet, the metal sheet and the lower chlorinated polyethylene sheet.
Claim 2
Dependent Claim
197 words
A process for producing a laminate comprising a metal sheet having chlorinated polyethylene composition on both sides thereof, said process consisting essentially of the steps of: I. calendering chlorinated polyethylene composition at 250° F. to 350° F. through the nip of a first roll and a second roll to produce an upper chlorinated polyethylene sheet adhering to the second roll; II. calendering chlorinated polyethylene composition at 250° F. to 350° F. through the nip of a third roll and a fourth roll to produce a lower chlorinated polyethylene sheet adhering to the third roll; III. feeding a metal sheet into the nip between the second roll and the third roll while contacting at 250° F. to 350° F. the upper chlorinated polyethylene sheet with the top of the metal sheet and while simultaneously contacting the lower chlorinated polyethylene sheet with the bottom of the metal sheet wherein the top and the bottom of the metal sheet have thereon a coating of an adhesion promoter, wherein the separation of the second and third roll is substantially equal to the sum of the thicknesses of the upper chlorinated polyethylene sheet, the metal sheet and the lower chlorinated polyethylene sheet.
Claim 3
Dependent Claim
10 words
The process of claim 1 wherein the metal is aluminum.
Claim 4
Dependent Claim
197 words
A process for producing a laminate comprising a metal sheet having polyvinyl chloride composition on both sides thereof, said process consisting essentially of the steps of: I. calendering polyvinyl chloride composition at 300° F. to 400° F. through the nip of a first roll and a second roll to produce an upper polyvinyl chloride sheet adhering to the second roll; II. calendering polyvinyl chloride composition at 300° F. to 400° F. through the nip of a third roll and a fourth roll to produce a lower polyvinyl chloride sheet adhering to the third roll; III. feeding a metal sheet into the nip between the second roll and the third roll while contacting at 300° F. to 400° F. the upper polyvinyl chloride sheet with the top of the metal sheet and while simultaneously contacting the lower polyvinyl chloride sheet with the bottom of the metal sheet wherein the top and the bottom of the metal sheet have thereon a coating of an adhesion promoter, wherein the separation of the second and third roll is substantially equal to the sum of the thicknesses of the upper polyvinyl chloride sheet, the metal sheet and the lower polyvinyl chloride sheet.
Claim 5
Dependent Claim
197 words
A process for producing a laminate comprising a metal sheet having polyvinyl chloride composition on both sides thereof, said process consisting essentially of the steps of: I. calendering polyvinyl chloride composition at 300° F. to 400° F. through the nip of a first roll and a second roll to produce an upper polyvinyl chloride sheet adhering to the second roll; II. calendering polyvinyl chloride composition at 300° F. to 400° F. through the nip of a third roll and a fourth roll to produce a lower polyvinyl chloride sheet adhering to the third roll; III. feeding a metal sheet into the nip between the second roll and the third roll while contacting at 300° F. to 400° F. the upper polyvinyl chloride sheet with the top of the metal sheet and while simultaneously contacting the lower polyvinyl chloride sheet with the bottom of the metal sheet wherein the top and the bottom of the metal sheet have thereon a coating of an adhesion promoter, wherein the separation of the second and third roll is substantially equal to the sum of the thicknesses of the upper polyvinyl chloride sheet, the metal sheet and the lower polyvinyl chloride sheet.
Claim 6
Dependent Claim
11 words
The process of claim 3 wherein the metal is stainless steel.
Claim 7
Dependent Claim
37 words
The process of claims 1 or 3 wherein the sheet of metal has been coated with a copolymer of 10 to 20 percent by weight of vinyl acetate, the balance of said copolymer being essentially vinyl chloride.
Claim 8
Dependent Claim
19 words
The process of claims 1 or 3 wherein the metal sheet has a thickness of 0.001 to 0.1 inch.
Claim 9
Dependent Claim
18 words
The process of claims 1 or 3 wherein the laminate has a thickness of 0.006 to 0.5 inch.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-21 | 1985-06-22 | 1985-12-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-21 | 1989-06-22 | 1989-12-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-21 | 1993-06-22 | 1993-12-22 | $7700.00 | Window Closed / Lapsed |