Chemical modification of metal oxides and lecithin materials
Assignee: American Lecithin Co Inc
•
Filing: 1980-03-11
•
Granted: 1981-12-15
•
Expires: 2000-03-11
Abstract
Abstract A process of chemically modifying metal oxides, that is oxides of metals such as iron, lead, molybdenum, titanium, zinc and other metals, by treating them under heating at a temperature between 100° and 160° C. for a time period between 10 minutes and one hour or more with a lecithin material, in fluid form (including molten form). The lecithin material is a vegetable lecithin, an animal lecithin or the acetone-soluble fraction of either type of lecithin. Such metal oxide groupings enter the lecithin-fluid fraction. Whereafter a modified metal oxide, partially in a suspended form, is developed partially dissolved in the fluid lecithin (where such product can be utilized as a modified form of the fluid lecithin fraction). Such solid modified metal oxide thereafter can be sedimented from the modified oily fraction. Such modified metal oxides, instead of their initial form, can be used in such form. Or, the modified metal oxides can be placed into a water dispersion, whereafter the dissolved matter can in solution further interreact with reactive components dissolved in the same water, or can interreact with an additional reactive organic component (such as an unsaturated polymeric matter, in particular a latex), whereby such metal oxide matter with the lecithin-groupings enters into the water dispersion. The lecithin modified metal oxides can be used as paint pigments which are readily redispersible within the paint after storage (with or without addition of additional lecithin matter).
Inventors
- 👤 Max Kronstein
- 👤 Joseph Eichberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 21:16
CPC Classifications
C; C09; C09C; C09C3/00; C09C3/08; C08; C08K; C08K9/00; C08K9/04; C09C1/00; C09C1/14; C09C1/18; C01; C01P; C01P2002/00; C01P2002/80; C01P2002/82; C01P2002/84; C01P2004/00; C01P2004/50; C01P2006/00; C01P2006/60
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
77 words
Process of chemically modifying a metal oxide, which comprises treating said metal oxide under heating at a temperature between 100° and 160° C. for a time period of at least 10 minutes with a lecithin material, in fluid form, whereby said metal oxide in the form of a grouping enters the lecithin fluid or the lecithin-fluid fraction, and whereby thereafter a modified metal oxide, partially in a suspended form, is developed partially dissolved in the fluid lecithin.
Claim 2
Dependent Claim
77 words
Process of chemically modifying a metal oxide, which comprises treating said metal oxide under heating at a temperature between 100° and 160° C. for a time period of at least 10 minutes with a lecithin material, in fluid form, whereby said metal oxide in the form of a grouping enters the lecithin fluid or the lecithin-fluid fraction, and whereby thereafter a modified metal oxide, partially in a suspended form, is developed partially dissolved in the fluid lecithin.
Claim 3
Dependent Claim
18 words
Process as claimed in claim 1 wherein said vegetable lecithin is soybean lecithin, corn lecithin or safflower lecithin.
Claim 4
Dependent Claim
67 words
Process as claimed in claim 1 wherein said lecithin is used in the form of its oily fraction or acetone-soluble fraction, which is obtained by mixing lecithin in its crude oil carrier form with acetone, whereby an oily fraction of said crude lecithin is dissolved in the acetone and an insoluble fraction is precipitated, and separating said oily fraction or acetone-soluble fraction from said precipitated insoluble fraction.
Claim 5
Dependent Claim
25 words
Process as claimed in claim 3 wherein said fluid lecithin is used in the presence of another fluid such as triglyceride oil or a diluent.
Claim 6
Dependent Claim
13 words
Process as claimed in claim 1 wherein said lecithin is an egg lecithin.
Claim 7
Dependent Claim
22 words
Process as claimed in claim 1 wherein the metal oxide is an oxide of iron, lead, molybdenum, titanium, zinc, cadmium or copper.
Claim 8
Dependent Claim
20 words
Process as claimed in claim 1 wherein said heating is conducted for a time between 6 minutes and one hour.
Claim 9
Dependent Claim
32 words
Process as claimed in claim 1 wherein said lecithin material is a vegetable lecithin, an animal lecithin, an acetone-soluble fraction of a vegetable lecithin or an acetone-soluble fraction of an animal lecithin.
Claim 10
Dependent Claim
86 words
Process wherein the metal oxide of claim 1, which has an increased rate of water solubility, such as allowing the lecithin-modified metal oxide to enter a solution in water, are subjected, after addition of some acidity, to electrodeposition, with the present straight metal ions being deposited at the cathode of the analyzer and the reaction product between the metal groupings and the lecithin and a reactive additional polymeric component being deposited at the anode, whereby the presence of the water dissolved product can so be identified.
Claim 11
Dependent Claim
22 words
Process as in claim 1 wherein said solid modified metal oxide is separated from the modified lecithin or modified lecithin fluid fraction.
Claim 12
Dependent Claim
82 words
Metal oxide particles, which have been chemically modified by heating said metal oxide particles with a lecithin, selected from the group consisting of a plant lecithin, an animal lecithin and an acetone-soluble fraction of either, said heating having been done at a temperature effective to achieve said chemical modification, at least an extensive portion of said metal oxide particles being chemically modified by said lecithin, and which has increased redispersibility and solubility, that is useful in a solvent-based or water-based coating material.
Claim 13
Dependent Claim
82 words
Metal oxide particles, which have been chemically modified by heating said metal oxide particles with a lecithin, selected from the group consisting of a plant lecithin, an animal lecithin and an acetone-soluble fraction of either, said heating having been done at a temperature effective to achieve said chemical modification, at least an extensive portion of said metal oxide particles being chemically modified by said lecithin, and which has increased redispersibility and solubility, that is useful in a solvent-based or water-based coating material.
Claim 14
Dependent Claim
84 words
Metal oxide particles, which have been chemically modified by heating said metal oxide particles with a lecithin, selected from the group consisting of a plant lecithin, an animal lecithin and an acetone-soluble fraction of either, said heating having been done at a temperature effective to achieve said chemical modification, at least an extensive portion of said metal oxide particles being chemically modified by said lecithin, and which has either increased redispersibility or solubility, that is useful in a solvent-based or a water-based coating material.
Claim 15
Dependent Claim
84 words
Metal oxide particles, which have been chemically modified by heating said metal oxide particles with a lecithin, selected from the group consisting of a plant lecithin, an animal lecithin and an acetone-soluble fraction of either, said heating having been done at a temperature effective to achieve said chemical modification, at least an extensive portion of said metal oxide particles being chemically modified by said lecithin, and which has either increased redispersibility or solubility, that is useful in a solvent-based or a water-based coating material.
Claim 16
Dependent Claim
56 words
Metal oxide particles, which have been reacted with lecithin matter, thereby being chemically modified, in the form of a component in the oily fraction of lecithin, said reaction having been done at a temperature effective to achieve said chemical modification, at least an extensive portion of said metal oxide particles being chemically modified by said lecithin.
Claim 17
Dependent Claim
56 words
Metal oxide particles, which have been reacted with lecithin matter, thereby being chemically modified, in the form of a component in the oily fraction of lecithin, said reaction having been done at a temperature effective to achieve said chemical modification, at least an extensive portion of said metal oxide particles being chemically modified by said lecithin.
Claim 18
Dependent Claim
70 words
Lecithin or a lecithin fraction, which has been chemically modified by the reaction with and the entry of metal oxide particles in the form of an interreaction product between said lecithin or said lecithin fraction and said metal oxide particles, said reaction having been done at a temperature effective to achieve said chemical modification, at least an extensive portion of said metal oxide particles being chemically modified by said lecithin.
Claim 19
Dependent Claim
70 words
Lecithin or a lecithin fraction, which has been chemically modified by the reaction with and the entry of metal oxide particles in the form of an interreaction product between said lecithin or said lecithin fraction and said metal oxide particles, said reaction having been done at a temperature effective to achieve said chemical modification, at least an extensive portion of said metal oxide particles being chemically modified by said lecithin.
Claim 20
Dependent Claim
12 words
The chemically modified metal oxide prepared by the process of claim 1.
Claim 21
Dependent Claim
58 words
Process as claimed in claim 3 wherein said lecithin is used in the form of its acetone-insoluble fraction, which has been separated from the oily lecithin fraction, after reintroducing a selected oily matter from the group of triglyceride oils, so as to become a component of said lecithin material which is then used to treat said metal oxide.
Claim 22
Dependent Claim
20 words
Process as claimed in claim 3 wherein the solid and modified metal oxide are separated from the modified oily fraction.
Claim 23
Dependent Claim
57 words
Process of placing said modified form of metal oxide of claim 17 in a water dispersion, whereafter the dissolved matter can in solution further interract with reactive components dissolved in the same water or an additional reactive organic component in the water so further modifying in the water dispersion the metal oxide matter with the lecithin groupings.
Claim 24
Dependent Claim
17 words
Process as claimed in claim 18 wherein said additional reactive organic component is an unsaturated polymeric matter.
Claim 25
Dependent Claim
14 words
Process as claimed in claim 19 wherein said unsaturated polymeric matter is a latex.
Claim 26
Dependent Claim
39 words
Process of using the lecithin-modified metal oxide of claim 17 as a paint pigment which is, with or without the addition of additional lecithin matter, more readily after storage redispersible in the paint than the not-lecithin-modified metal oxide pigment.
Claim 27
Dependent Claim
49 words
Process as claimed in claim 21 wherein the dispersions of the lecithin-modified metal oxides are incorporated as dispersions in fluids or in solutions jointly with unsaturated polymeric materials, and wherein said modified metal oxides are after storage readily redispersible with or without requiring a separate addition of lecithin materials.
Claim 28
Dependent Claim
41 words
Process as claimed in claim 22 wherein said modified metal oxide is used in a paint composition, said metal oxide being more readily redispersible in said paint after extended storage that can be obtained when not-modified metal oxide has been used.
Claim 29
Dependent Claim
40 words
Process as claimed in claim 22 wherein the paint contains said modified metal oxide having a higher specific gravity jointly with a non-lecithin-heat-modified pigment of lower specific gravity, whereby both the pigment and the modified metal oxide are readily redispersible.
Claim 30
Dependent Claim
17 words
Process as claimed in claim 22 wherein said unsaturated polymeric materials are those used in coating materials.
Claim 31
Dependent Claim
20 words
The metal oxide as claimed in claim 11 wherein said heating is at a temperature between 100° and 160° C.
Claim 32
Dependent Claim
21 words
The metal oxide as claimed in claim 13 wherein said reaction is conducted at a temperature between 100° and 160° C.
Claim 33
Dependent Claim
23 words
The lecithin or lecithin fraction as claimed in claim 14 wherein said reaction is conducted at a temperature between 100° and 160° C.
Claim 34
Dependent Claim
22 words
The process as claimed in claim 1 wherein only said metal oxide and said lecithin material are present during said heating step.
Claim 35
Dependent Claim
12 words
The chemically modified metal oxide prepared by the process of claim 29.
Claim 36
Dependent Claim
22 words
The metal oxide as claimed in claim 26 wherein only said metal oxide and said lecithin are present during said heating step.
Claim 37
Dependent Claim
23 words
The metal oxide as claimed in claim 27 wherein only said metal oxide and said lecithin matter are present during said reaction step.
Claim 38
Dependent Claim
27 words
The lecithin or lecithin fraction as claimed in claim 28 wherein only said metal oxide and said lecithin or lecithin fraction are present during said reaction step.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-14 | 1985-06-15 | 1985-12-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-14 | 1989-06-15 | 1989-12-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-14 | 1993-06-15 | 1993-12-15 | $7700.00 | Window Closed / Lapsed |