Room temperature vulcanizable silicone rubber compositions and process of making

Claim 2

A one-component room temperature vulcanizable silicone rubber composition comprising: (a) 100 parts by weight of a silanol end-stopped liquid organopolysiloxane base polymer having a viscosity of from about 200 to about 500,000 centistokes at 25° C., containing an average of from 1.85 to 2.01 organic radicals per silicon atom, and containing from about 0.02% to about 2.0% silicon-bonded hydroxyl radicals; (b) from about 1.8 to about 6.0 parts by weight, based upon the weight of the organopolysiloxane, of an organotriacyloxysilane cross-linker having the formula: R.sup.3 Si(OY).sub.3 where R 3 is a radical selected from the group consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals, and cyanoalkyl radicals, and Y is a saturated monacyl radical of a carboxylic acid; and (c) from about 0.25 to about 2.85 parts by weight based upon the weight of the organopolysiloxane base polymer, of a polysiloxane polyether copolymer having the formula: ##STR10## where R and R' are monovalent hydrocarbon radicals, R" is a lower alkyl radical, a has a value of at least 2, b has a value of from 2 to 3, inclusive, n has a value of from 2 to 4, inclusive, and x has a value of at least 5.

Claim 3

A composition in accordance with claim 1, wherein the polysiloxane polyether copolymer comprises about 1.40 parts by weight, based upon the weight of the orgaopolysiloxane base polymer.

Claim 4

A composition in accordance with claim 1, wherein R and R' are radicals selected from the group consisting of methyl and phenyl.

Claim 5

A composition in accordance with claim 1, wherein the polysiloxane polyether copolymer corresponds to the formula: ##STR11## having a viscosity of about 730 centipoises at 25° C.

Claim 6

A composition in accordance with claim 1, wherein the silanol end-stopped liquid organopolysiloxane base polymer has the formula: ##STR12## where R 5 is a radical selected from the group consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals and cyanoalkyl radicals, and m has a value of at least 5.

Claim 7

A composition in accordance with claim 5, wherein R 5 is a radical selected from the group consisting of methyl and phenyl.

Claim 8

A composition in accordance with claim 1, wherein R 3 is methyl and Y is acetyl.

Claim 9

A composition in accordance with claim 1, further comprising from about 2 to about 30 parts by weight, based upon the weight of the organopolysiloxane base polymer, of an organosilicon process aid having a viscosity of up to about 200 centipoises at 25° C. comprising diorganosiloxy units of the formula: (R.sup.4).sub.2 SiO chemically combined with organosiloxy units of the formula: R.sup.4 SiO.sub.1.5 and triorganosiloxy units of the formula: (R.sup.4).sub.3 SiO.sub.0.5 wherein said process aid contains from about 0.1% to about 8% by weight of hydroxy radicals attached to silicon, and a ratio of organosiloxy units to diorganosiloxy units of from about 0.11 to about 1.4, inclusive, and a ratio of triorganosiloxy units to diorganosiloxy units of from about 0.02 to about 1, inclusive, and where R 4 is a radical selected from the group consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals and cyanoalkyl radicals.

Claim 10

A composition in accordance with claim 8, wherein R 4 is methyl.

Claim 11

A composition in accordance with claim 1, further comprising from about 0.01 to about 5.0 parts by weight, based upon the weight of the organopolysiloxane base polymer, of a catalyst.

Claim 12

A composition according to claim 10, wherein the catalyst is a carboxylic acid salt of a metal ranging from lead to manganese, inclusive, in the electromotive series of metals.

Claim 13

A composition according to claim 10, wherein the catalyst is a carboxylic acid salt of tin.

Claim 14

A composition according to claim 10, wherein the catalyst is an organometallic ester compound of a metal other than silicon selected from the group consisting of a partially chelated ester of a lower aliphatic alcohol with a β-dicarbonyl compound and a partial hydrolyzate of a partially chelated ester of a lower aliphatic alcohol with a β-dicarbonyl compound which retain at least one hydrocarbonoxy radical or substituted hydrocarbonoxy radical attached to the metal atom through M-O-C linkages, where M is a metal, and wherein the weight ratio of said catalyst to the organotriacyloxysilane cross-linker always is at least 0.5 to 1.

Claim 15

A composition according to claim 13, wherein in said organometallic ester, the metal M is selected from the group consisting of lead, tin, zirconium, antimony, iron, cadmium, barium, calcium, titanium, bismuth, manganese, zinc, chromium, cobalt, nickel, aluminum, gallium or germanium.

Claim 16

A composition according to claim 13, wherein in said organometallic ester, the metal is titanium.

Claim 17

A composition in accordance with claim 1, further comprising from about 5 to about 200 parts by weight, based upon the weight of the organopolysiloxane base polymer, of a filler.

Claim 18

A composition according to claim 16, wherein the filler is fumed silica treated with octamethylcyclotetrasiloxane.

Claim 19

A composition in accordance with claim 1, further comprising from about 0.2 to about 6 parts by weight, based upon the weight of the organopolysiloxane base polymer, of a dialkoxy-diacyloxysilane adhesion promoter.

Claim 20

A process for forming a cured one-component room temperature vulcanizable silicone rubber composition comprising: (a) admixing under substantially anhydrous conditions 100 parts by weight of a silanol end-stopped liquid organopolysiloxane base polymer having a viscosity of from about 200 to about 500,000 centistokes at 25° C., containing an average of from 1.85 to 2.01 organic radicals per silicon atom, and containing from about 0.02% to about 2.0% silicon-bonded hydroxyl radicals, with from about 0.25 to about 2.85 parts by weight, based upon the weight of the organopolysiloxane base polymer, of a polysiloxane polyether copolymer having the formula: ##STR13## where R and R' are monovalent hydrocarbon radicals, R" is a lower alkyl radical, a has a value of at least 2, b has a value of from 2 to 3, inclusive, n has a value of from 2 to 4, inclusive, and x has a value of at least 5; (b) subjecting the mixture to a vacuum to remove moisture; (c) combining the mixture under substantially anhydrous conditions with from about 1.8 to about 6.0 parts by weight, based upon the weight of the organopolysiloxane base polymer, of an organotriacyloxysilane cross-linker having the formula: R.sup.3 Si(OY).sub.3 where R 3 is a radical selected from the group consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals, and cyanoalkyl radicals, and Y is a saturated monoacyl radical of a carboxylic acid; and (d) exposing the combined mixture to moisture until it cures.

Claim 21

A process for forming a cured one-component room temperature vulcanizable silicone rubber composition comprising: (a) admixing under substantially anhydrous conditions 100 parts by weight of a silanol end-stopped liquid organopolysiloxane base polymer having a viscosity of from about 200 to about 500,000 centistokes at 25° C., containing an average of from 1.85 to 2.01 organic radicals per silicon atom, and containing from about 0.02% to about 2.0% silicon-bonded hydroxyl radicals, with from about 0.25 to about 2.85 parts by weight, based upon the weight of the organopolysiloxane base polymer, of a polysiloxane polyether copolymer having the formula: ##STR13## where R and R' are monovalent hydrocarbon radicals, R" is a lower alkyl radical, a has a value of at least 2, b has a value of from 2 to 3, inclusive, n has a value of from 2 to 4, inclusive, and x has a value of at least 5; (b) subjecting the mixture to a vacuum to remove moisture; (c) combining the mixture under substantially anhydrous conditions with from about 1.8 to about 6.0 parts by weight, based upon the weight of the organopolysiloxane base polymer, of an organotriacyloxysilane cross-linker having the formula: R.sup.3 Si(OY).sub.3 where R 3 is a radical selected from the group consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals, and cyanoalkyl radicals, and Y is a saturated monoacyl radical of a carboxylic acid; and (d) exposing the combined mixture to moisture until it cures.

Claim 22

A process according to claim 19, wherein about 1.40 parts by weight of the polysiloxane polyether copolymer, based upon the weight of the organopolysiloxane base polymer, is mixed with 100 parts by weight of said organopolysiloxane base polymer.

Claim 23

A process according to claim 19, wherein R and R' are radicals selected from the group consisting of methyl and phenyl.

Claim 24

A process according to claim 19, wherein the organopolysiloxane is mixed with a polysiloxane polyether copolymer of the formula: ##STR14## having a viscosity of about 730 centipoises at 25° C.

Claim 25

A process according to claim 19, wherein the silanol end-stopped liquid organopolysiloxane base polymer is of the formula: ##STR15## where R 5 is a radical selected from the group consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals and cyanoalkyl radicals, and m has a value of at least 5.

Claim 26

A process according to claim 23, wherein R 5 is a radical selected from the group consisting of methyl and phenyl.

Claim 27

A process according to claim 19, further comprising adding to the silanol end-stopped liquid organopolysiloxane base polymer-polysiloxane polyether copolymer mixture, from about 2 to about 30 parts by weight, based upon the weight of the organopolysiloxane base polymer, of an organosilicon process aid having a viscosity of up to about 200 centipoises at 25° C., said process aid having diorganosiloxy units of the formula: (R.sup.4).sub.2 SiO chemically combined with organosiloxy units of the formula: R.sup.4 SiO.sub.1.5 and triorganosiloxy units of the formula: (R.sup.4).sub.3 SiO.sub.0.5 said process aid containing from about 0.1% to about 8% by weight of hydroxy radicals attached to silicon, and a ratio of organosiloxy units to diorganosiloxy units of from about 0.11 to about 1.4, inclusive, and a ratio of triorganosiloxy units to diorganosiloxy units of from about 0.02 to about 1, inclusive, and where R 4 is a radical selected from the group consisting of monovalent hydrocarbon radicals, halogenated monovalent hydrocarbon radicals and cyanoalkyl radicals.

Claim 28

A process according to claim 25, wherein R 4 is methyl.

Claim 29

A process according to claim 19, further comprising adding from about 0.01 to about 5.0 parts by weight, based upon the weight of the organopolysiloxane base polymer, of a catalyst to the organotriacyloxysilane cross-linker, prior to mixing the organotriacyloxysilane cross-linker with the silanol end-stopped liquid organopolysiloxane base polymer-polysiloxane polyether copolymer mixture.

Claim 30

A process according to claim 27, wherein the catalyst comprises a carboxylic acid salt of a metal ranging from lead to manganese, inclusive, in the electromotive series of metals.

Claim 31

A process according to claim 27, wherein the catalyst is a carboxylic acid salt of tin.

Claim 32

A process according to claim 27, wherein the catalyst comprises an organometallic ester compound of a metal other than silicon selected from the group consisting of a partially chelated ester of a lower aliphatic alcohol with a β-dicarbonyl compound and a partial hydrolyzate of a partially chelated ester of a lower aliphatic alcohol with a β-dicarbonyl compound which retain at least one hydrocarbonoxy radical or substituted hydrocarbonoxy radical attached to the metal atom through M-O-C linkages, where M is a metal and wherein the weight ratio of said catalyst to the organotriacyloxysilane cross-linker always is at least 0.5 to 1.

Claim 33

A process according to claim 30, wherein in said organometallic ester, the metal M is selected from the group consisting of lead, tin, zirconium, antimony, iron, cadmium, barium, calcium, titanium, bismuth, manganese, zinc, chromium, cobalt, nickel, aluminum, gallium or germanium.

Claim 34

A process according to claim 30, wherein in said organometallic ester, the metal M is titanium.

Claim 35

A process according to claim 19, further comprising adding to the silanol end-stopped liquid organopolysiloxane base polymer-polysiloxane polyether copolymer mixture, from about 5 to about 200 parts by weight, based upon the weight of the organopolysiloxane base polymer, of a filler.

Claim 36

A process according to claim 33, wherein the filler comprises a fumed silica treated with octamethylcyclotetrasiloxane.

Claim 37

A process according to claim 19, further comprising adding from about 0.2 to about 6 parts by weight, based upon the weight of the organopolysiloxane base polymer, of a dialkoxy-diacyloxysilane as an adhesion promoter to the organotriacyloxysilane cross-linker, prior to mixing the organotriacyloxysilane cross-linker with the silanol end-stopped liquid organopolysiloxane base polymer-polysiloxane polyether copolymer mixture.