Laminated conducting film on an integrated circuit substrate and method of forming the laminate
Assignee: Intersil Corp
•
Filing: 1980-10-28
•
Granted: 1981-11-24
•
Expires: 2000-10-28
Abstract
Abstract A method in integrated circuit technology of depositing an adherent aluminum film that does not develop significant protrusions, such as "hillocks" and "whiskers", during or following annealing. The aluminum is deposited by evaporation or sputtering techniques while sufficient dry oxygen is introduced periodically into the deposition chamber to form alernating layers of aluminum and oxygen-doped aluminum consisting of no more than 10 atomic percent oxygen. Photolithographically patterning such a laminated film into the appropriate configuration of conducting lines and bond pads, and subsequently annealing such as a laminated film at temperatures from 450° C. to 560° C. in forming gas, results in aluminum surfaces that are free of protrusions with heights above 0.5 μm and in films that have relatively low resistivity, i.e., resistivity that is less than 1.8 times the resistivity of bulk aluminum. The laminated films range in thickness between 8000 to 25,000 angstroms. The top layer is formed of aluminum with a thickness no less than about 1500 angstroms and no more than about 3000 angstroms.
Inventors
- 👤 Thomas J. Faith, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 08:26
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/40; H10P14/412; C; C23; C23C; C23C14/00; C23C14/06; C23C14/08; C23C14/081; C23C14/14; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/064; H10W20/40; H10W20/41; H10W20/44; H10W20/4403; H10W20/4405; H10W20/4407; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24917; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
107 words
A method of forming by deposition a laminated conducting film on an integrated circuit substance in a vacuum chamber comprising the steps of: depositing aluminum on the substrate; periodically introducing dry oxygen into the chamber while depositing the aluminum to provide a laminated film of alternate layers of aluminum and oxygen-doped aluminum, the oxygen-doped layers of aluminum having less than 10 atomic percent oxygen; and interrupting the flow of oxygen to form the top layer of aluminum to a thickness of no less than about 1,500 angstroms and no more than about 3,000 angstroms; the laminated film having a composite thickness in the range of 8000-25,000 angstroms.
Claim 2
Independent Claim
107 words
A method of forming by deposition a laminated conducting film on an integrated circuit substance in a vacuum chamber comprising the steps of: depositing aluminum on the substrate; periodically introducing dry oxygen into the chamber while depositing the aluminum to provide a laminated film of alternate layers of aluminum and oxygen-doped aluminum, the oxygen-doped layers of aluminum having less than 10 atomic percent oxygen; and interrupting the flow of oxygen to form the top layer of aluminum to a thickness of no less than about 1,500 angstroms and no more than about 3,000 angstroms; the laminated film having a composite thickness in the range of 8000-25,000 angstroms.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein the oxygen-doped layers comprise aggregate thicknesses of 10-50 percent of the composite thickness of the laminated film.
Claim 4
Dependent Claim
40 words
The method of claim 2 comprising introducing the dry oxygen to an oxygen fill pressure of 5×10 -6 to 1×10 -4 Torr to develop respectively a flow rate of approximately 2×10 17 to 3×10 18 molecules of oxygen per second.
Claim 5
Dependent Claim
54 words
The method of claim 3 comprising depositing odd-numbered aluminum layers each layer having thicknesses of about 1,000 angstroms, and alternately depositing even-numbered layers of oxygen-doped aluminum each layer having a thickness of about 1,000 angstroms, whereby a minimum of three odd-numbered layers of aluminum and three even-numbered alternating layers of oxygen-doped aluminum are deposited.
Claim 6
Dependent Claim
41 words
The method of claim 1 wherein the vacuum deposition of aluminum is done by an electron beam evaporator and further comprising the step of depositing the aluminum in the range of approximately 25 angstroms per second to 50 angstroms per second.
Claim 7
Dependent Claim
35 words
The method of claim 1 wherein the deposition of aluminum is done by a magnetron sputterer and wherein the step of depositing the aluminum is done at a rate of about 4 angstroms per second.
Claim 8
Dependent Claim
45 words
The method of claim 1 wherein the deposition of aluminum is done by a filamentary evaporator providing high energy aluminum-atom flux incident to the substrates and wherein the step of depositing aluminum is done at rates ranging from about 20 to 50 angstroms per second.
Claim 9
Dependent Claim
47 words
The method of claim 1 wherein the deposition of aluminum is done by evaporating the aluminum from a crucible of aluminum heated by an RF coil and wherein the step of depositing the aluminum is done at rates ranging from about 20 to 50 angstroms pr second.
Claim 10
Independent Claim
38 words
The method of claims 1 or 2 further comprising the step of depositing the top layer of the film solely with aluminum to a thickness of at least about 1500 angstroms but not greater than about 3000 angstroms.
Claim 11
Independent Claim
34 words
The method of claims 1 or 2 further comprising the step of depositing the initial layer of the film on said substrate solely with aluminum to a thickness no more than about 2000 angstroms.
Claim 12
Independent Claim
26 words
The method of claims 1 or 2 further comprising the step of heating said substrate to a temperature of about 250° C. while depositing the aluminum.
Claim 13
Independent Claim
45 words
The method according to claims 1 or 2 further comprising the step of providing a desired integrated circuit photoresist pattern on the surface of the laminated film, and etching the film away in areas free of photoresist to leave a desired conducting circuit interconnection pattern.
Claim 14
Independent Claim
29 words
The method according to claims 1, or 2 further comprising the step of annealing the laminated film at a temperature within the range of 450° C. to 560° C.
Claim 15
Dependent Claim
15 words
A metallized integrated circuit device made in accordance with the method recited in claim 12.
Claim 16
Dependent Claim
15 words
A metallized integrated circuit device made in accordance with the method recited in claim 13.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-23 | 1985-05-25 | 1985-11-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-23 | 1989-05-25 | 1989-11-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-23 | 1993-05-25 | 1993-11-24 | $7700.00 | Window Closed / Lapsed |